• Journal of Korea Foundry Society
• /
• v.34 no.2
• /
• pp.54-59
• /
• 2014

In this study, the extruded Al-6.3Zn-2.4Mg alloys were selected among the 7000 series aluminum alloys sensitive to hydrogen environment in order to examine the effects of both the aging conditions and the length of hydrogen charging period on the mechanical properties of the alloy. The specimens were aged for 24hours at $100^{\circ}C$ (under aging (UA)), $120^{\circ}C$ (peak aging (PA)), and $160^{\circ}C$ (over aging (OA)), respectively. Charging tests were performed at RT for 12, 24, 36 hours under potentiostatic conditions (-2000 mV vs (Ag/AgCl)) for 12, 24 and 36 hours in 1M $H_2SO_4$ and 0.1%$NH_4SCN$ solution. The fracture surface was examined by scanning electron microscopy (SEM). X-ray diffraction (XRD) pattern in peak aged sample was obtained before and after hydrogen charging from extruded Al-6.3Zn-2.4Mg alloys. The decreasing rate of tensile strength and elongation is represented in order of over aging < under aging < peak aging, and it is believed that the hydrogen recharge is more sensitive to elongation than tensile strength. The formation of $AlH_3$ in hydrogen charged Al-6.3Zn-2.4Mg alloys has been confirmed by X-ray diffraction studies.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.448-449
• /
• 2008

Light Mg alloy stands on the center of investigation due to the high potential of industrial application not only to the structural, but also to the functional fields. However, the intrinsic low strength and corrosion resistance have limited to extend its industrial use. In order to overcome the disadvantage, various attempts have been come to the modification of composition, resulting in finding Mg-Zn-Y alloys. The cast Mg-Zn-Y alloy leads to the high strength and hardness, low friction coefficient and low interfacial energy in both the ambient and elevated temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.114-114
• /
• 2009

ZnO has received considerable attention due to its potential applicability to optoelectronic devices such as ultraviolet-light emitting diodes (UVLEDs) and laser diodes (LDs). As well known, however, polar ZnO with the growth direction along the c-axis has spontaneous and piezoelectric polarizations that will result in decreased quantum efficiency. Recently, nonpolar ZnO has been studied to avoid such a polarization effect. In order to realize applications of nonpoar ZnO-based films to LEDs, growth of high quality alloys for quantum well structures is one of the important tasks that should be solved. $Mg_xZn_{1-x}O$ and $Cd_xZn_{1-x}O$ is ones of most promising alloys for this application because the alloys of ZnO with MgO and CdO provide a wide range of band-gap engineering spanning from 2.4 to 7.8 eV. In this study, we investigated on $Mg_xZn_{1-x}O$ films grown with various Mg/Zn flux ratios The films were grown on R-plane sapphire substrates by plasma-assisted molecular beam epitaxy (PAMBE). we investigated on $Mg_xZn_{1-x}O$ films grown with various Mg/Zn flux ratios. The films were grown on R-plane sapphire substrates by plasma-assisted molecular beam epitaxy (PAMBE). With the relatively low Mg/Zn flux ratios, a typical striated anisotropic surface morphology which was generally observed from the nonpolar (11-20) ZnO film on r-plane sapphire substrates. By increasing the Mg/Zn flux ratio, however, additional islands were appeared on the surface and finally the surface morphology was entirely changed, which was generally observed for the (0001) polar ZnO films by losing the striated morphology. Investigations by X-ray $\Theta-2{\Theta}$ diffraction revealed that (0002) and (10-11) ZnO planes are appeared in $Mg_xZn_{1-x}O$ films by increasing the Mg/Zn flux ratio. Further detailed investigation by transmission electron microscopy (TEM) and photoluminescence (PL) will be discussed.

• Korean Journal of Materials Research
• /
• v.7 no.2
• /
• pp.129-135
• /
• 1997

This study has investigated the effects of aging treatment on thc nlechanical propcrries of blg-iiAl-x%nix - 0.1.2) alloys fabricated by the squeeze castmg process. The microstructurcs of as-squeeze cast were composed of pro eurectic $\alpha$ magnesium solid solution, super saturated $\alpha$ solid solution and $\beta(Mg_{17}AI_{12}$) compund. Agcd at both $200^{\circ}C$ and $240^{\circ}C$, Mg--6AixZn alloys showed the peak hardness due to the formation of $\beta(Mg_{17}AI_{12}$) precipitates. The tiiscontinuous precipitates of the lamella r\.pe are predominant at $200^{\circ}C$ aging tredrment. tvhilc. the finely dispersed continu ous precipitates were major type at $240^{\circ}C$ treatment. Mg-- GAI-xZn a1loi.s fabricated hy the squeeze casting process had the hetter combination of tensile strength and elongation compared to the conventionally cast alloys. As increascci zinc: contents. the tensile strength was increased 11y the soiid solutirin strengthening effect of zinc,.

• Journal of Powder Materials
• /
• v.30 no.6
• /
• pp.470-477
• /
• 2023

The effects of annealing on the microstructure and mechanical properties of Al-Zn-Mg-Cu-Si alloys fabricated by high-energy ball milling (HEBM) and spark plasma sintering (SPS) were investigated. The HEBM-free sintered alloy primarily contained Mg₂Si, Q-AlCuMgSi, and Si phases. Meanwhile, the HEBM-sintered alloy contains Mg-free Si and θ-Al₂Cu phases due to the formation of MgO, which causes Mg depletion in the Al matrix. Annealing without and with HEBM at 500℃ causes partial dissolution and coarsening of the Q-AlCuMgSi and Mg₂Si phases in the alloy and dissolution of the θ-Al₂Cu phase in the alloy, respectively. In both alloys, a thermally stable α-AlFeSi phase was formed after long-term heat treatment. The grain size of the sintered alloys with and without HEBM increased from 0.5 to 1.0 ㎛ and from 2.9 to 6.3 ㎛, respectively. The hardness of the sintered alloy increases after annealing for 1 h but decreases significantly after 24 h of annealing. Extending the annealing time to 168 h improved the hardness of the alloy without HEBM but had little effect on the alloy with HEBM. The relationship between the microstructural factors and the hardness of the sintered and annealed alloys is discussed.

• Korean Journal of Materials Research
• /
• v.25 no.6
• /
• pp.269-273
• /
• 2015

The effect of adding Ca on the microstructural and mechanical properties of as-cast Mg-11Li-3Zn-1Sn(wt%) alloys were investigated. Mg-11Li-3Zn-1Sn-0.4Mn with different Ca additions (0.4, 0.8, 1.2 wt%) were cast under an $SF_6$ and $Co_2$ atmosphere at $720^{\circ}C$. The cast billets were homogenized at $400^{\circ}C$ for 12h and extruded at $200^{\circ}C$. The microstructural and mechanical properties were analyzed by OM, XRD, SEM, and tensile tests. The addition of Ca to the Mg-11Li-3Zn-1Sn-0.4Mn alloy resulted in the formation of $Ca_2Mg_6Zn_3$, MgSnCa intermetallic compound. By increasing Ca addition, the volume fraction and size of $Ca_2Mg_6Zn_3$ with needle shape were increased. This $Ca_2Mg_6Zn_3$ intermetallic compound was elongated to the extrusion direction and refined to fine particles due to severe deformation during hot extrusion. The elongation of the 0.8 wt% Ca containing alloy improved remarkably without reduction strength due to the formation of fine grain and $Ca_2Mg_6Zn_3$ intermetallic compounds by Ca addition. It is probable that fine and homogeneous $Ca_2Mg_6Zn_3$ intermetallic compounds played a significant role in the increase of mechanical properties.

• Korean Journal of Materials Research
• /
• v.7 no.11
• /
• pp.1012-1017
• /
• 1997

Mg-Zn-Ca합금의 잉곳트는 BN을 내벽에 바른 4x$10^{-5}$Torr의 진공의 석영관내에서 제조하였다. Mg-Zn합금계의 입자미세화를 위하여 0.5-5wt.%조성범위의 Ca를 첨가하였다. 제조된 합금을 용체화처리한 후 결정립크기와 경도를 측정하였다. Mg-6wt.%Zn합금의 입자미세화효과는 Ca가 1.5wt%첨가 될 때 최적의 조건이었다. Mg-6wt.% Zn과 Mg-6wt.% Zn-2wt.% Ca및 Mg-6wt.% Zn-1.5wt.% Si합금을 시효처리하여 시효거동을 조사하였다. 입자미세화에 의한 경도증가효과는 Mg-Zn-Ca합금계에서 크게 나타났으며 시효에 의한 경도증가효과는 Mg-Zn-Si합금계에서 크게 나타났다. Mg-6wt.%Zn합금의 부식전류밀도는 0.5wt.% Ca의 조성에서 감소되었다.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.1
• /
• pp.25-34
• /
• 2006

Al-Mg alloy, an open rack vaporizer(ORV) material was reported to be corroded in seawater environments though the ORV material was coupled to thermally sprayed Al-Zn alloy functioning a sacrificial anode. In addition, the corrosion behavior based on the calculated corrosion potential did not match the observed corrosion behavior. Hence, the goal of this study is to get better understanding on Al or Al-Mg alloy coupled to Al-Zn alloy and to provide the calculated corrosion potential representing the corrosion behavior of the ORV material by immersion test, electrochemical tests, and calculation of corrosion and galvanic potential. The corrosion potentials of Al and Al alloys also depended on alloying element as well as surface defects. The corrosion potentials of Al and Al-Mg alloy were changed with time. In the meantime, the corrosion potentials of Al-Zn alloys were not. The corrosion rates of Al-Zn alloys were exponentially increased with zinc contents. The phenomena were explained with the stability of passive film proved by passive current density depending on pH and confirmed by the model proposed by McCafferty. Dissimilar material crevice corrosion (DMCC) test shows that higher content of zinc caused Al-Mg alloy corroded more rapidly, which was due to the fact that higher corrosion rate of Al-Zn makes [$H^+$] and [$Cl^-$] more concentrated within pit solution to corrode Al-Mg alloy. Considering electrochemical reactions within pit as well as bulk in the calculation gives better prediction on the corrosion behavior of Al and Al-Mg alloy as well as the capability of Al-Zn alloy for corrosion protection.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.11
• /
• pp.148-157
• /
• 1999

The objective of this study is to investigate the effect of three main chemical compositions(Mg, Zn, Si) on extrudability of 7xxx Al alloy with high tensile strength. A few Al alloys based on 7xxx alloys were metal mold cast with various weight*%) of Mg 0.3-1.2%, Zn 5.0-8.0% and Si 0.4-0.7%, to envestigate the effects of extrudability, as well as mechanical properties. To measure the extrudability of cast billets, maximum extrusion pressure and surface temperature at die exit before tearing occurs were obtained by experiment and simulation of thermo-viscoplastic F.E.M. Also the yield and tensile strength of extruded products were tested.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.2
• /
• pp.96-102
• /
• 2006

Development of Rotation-Cylinder Method(RCM) is given for Mg-Al-Zn-X(X=Sr) alloys, identifying some of the key factors that need to be controlled and indicating subsequent casting processes. Effects of Sr addition on the microstructure and mechanical properties of as-cast and T6 heat-treated Mg-Al-Zn-X alloys fabricated by the RCM were investigated. The microstructural and mechanical characterizations were performed by utilizing optical microscope, scanning electron microscope, transmission electron microscope, hardness test and ultimate tensile test. The solution and aging treatment time was varied to optimize the T6 heat treatment conditions, and experimental results were discussed. The grain size of Sr containing alloys was refined by increasing Sr content, but the tensile and yield strengths were increased by addition up to 1wt% Sr.