• Journal of Korea Foundry Society
• /
• v.38 no.4
• /
• pp.75-81
• /
• 2018

This study examined the effect of the CaMgSn ternary phase on the aging response of the Mg-Sn-Zn alloy. The results revealed that the CaMgSn ternary phase formed in rod-like or needle-like shapes in Mg-3Zn-0.3Ca-xSn (x=1.5, 3, and 5 wt%) alloys and its size decreased as the Sn content increased from 1.5 wt% to 5 wt%. The Mg-3Zn-0.3Ca-5Sn alloy with a relatively fine CaMgSn phase was subjected to solution heat treatment and an aging process. Both the Mg-5Sn-3Zn-0.3Ca and Mg-5Sn-3Zn (base alloy) alloys had similar peak hardness values throughout all aging temperatures but the time-to-peak hardness in the Mg-5Sn-3Zn-0.3Ca alloy was 24-36 hours-earlier than that in the base alloy. Precipitates in the Mg-5Sn-3Zn-0.3Ca alloy were more refined than those in the Mg-5Sn-3Zn alloy and were mostly formed on basal planes. The $Mg_2Sn$ phase formed in either plate-like or rod-like shapes in the Mg-5Sn-3Zn alloy, whereas block-shaped $Mg_2Sn$ particles also formed in the Mg-5Sn-3Zn-0.3Ca alloy.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.15-15
• /
• 2012

Mg(1-4)Zn 이원계 압출재 및 Mg5Sn(1-4)Zn 삼원계 압출재의 부식거동을 3.5 % NaCl 용액에서 다양한 전기화학기법을 이용하여 평가하였다. 이원계 합금에 대한 연구결과, Zn 함량 증가에 따라 Mg 모재의 부동태화가 촉진되었고 동시에 수소발생속도가 증가하였으며 그 결과 부식전위의 상승이 관찰되었다. 그러나 Zn 함량 증가에 따른 부동태화 효과보다 수소발생 증가 효과가 우세하므로 결과적으로 Zn 함량 증가에 따라 부식속도는 증가하였다. Mg5Sn(1-4)Zn 삼원계 합금에 대한 부식시험 결과, Mg5Sn2Zn 합금이 가장 낮은 부식속도 및 우수한 부동태화를 나타내었으며 이는 합금원소 Sn의 수소발생속도 감소효과와 합금원소 Zn의 부동태화 효과의 상호작용에 의한 것으로 사료된다.