• Journal of the Korean Ceramic Society
• /
• v.56 no.2
• /
• pp.178-183
• /
• 2019

A process of fabricating the foamed glass that has closed pores with 8 ~ 580 ㎛ sizes without a blowing agent by sintering 10 ㎛ boron-free glass powder composed of CaO, MgO, SO₃, Al₂O₃-83 wt% SiO₂ at a molding pressure of 0 ~ 120 MPa and a sintering temperature of 750 ~ 1000℃ was investigated. To analyze the glass transition temperature of glass powder, thermogravimetric analysis-differential thermal analysis (TGA-DTA) method were used. The microstructure and pore size of foamed glass were examined using the optical microscopy and field emission scanning electron microscopy (FE-SEM). For the thermal diffusivity and color of the fabricated samples, a heat flow meter and ultraviolet-visible-near-infrared (UV-VIS-NIR)-colormetry were used, respectively. In the TGA-DTA result, the glass transition temperature of glass powder was confirmed to be 626℃. In the microstructure result, closed pores of 7 ~ 20 ㎛ were formed at 750 ~ 900℃, and they were not affected by the molding pressure and sintering temperature. However, at 1,000℃, when there was 0 MPa molding pressure, closed pores of 580 ㎛ were confirmed, and the pore size decreased as the molding pressure increased. Moreover, at a molding pressure of 30 MPa or higher, closed pores of approximately 400 ㎛ were formed. The porosity showed an increasing trend of smaller molding pressure and larger sintering temperature, and it was controllable in the range of 5.69 ~ 68.45%. In the thermal diffusivity result, there was no change according to the molding pressure, and, by increasing the sintering temperature, up to 0.115 W/m·K could be obtained. The Lab color index (CIE-Lab) results all showed a similar translucent white color regardless of molding pressure and sintering temperature. Therefore, based on the foamed glass without boron and blowing agent, it was confirmed that white foamed glass, which has closed pores of 8 ~ 580 ㎛ and a thermal diffusivity characteristic of 0.115 W/m·K, can be fabricated by changing the molding pressure and sintering temperature.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.12
• /
• pp.6187-6195
• /
• 2012

Recycling process of iron should be developed for efficient recovery of neodymium(Nd), rare metal, from acid-leaching solution of neodymium magnet. In this study, $FeCl_3$ solution as iron source was used for synthesis of iron nanoparticle with the condition of various factors, etc, reductant, surfactant. $Na_4O_7P_2$ and polyvinylpyrrolidone(PVP) as surfactants, $NaBH_4$ as reductant, and palladium chloride($PdCl_2$) as a nucleation seed were used. Iron powder was analyzed with instruments of XRD, SEM and PSA for measuring shape and size. Iron nanoparticles were made at the ratio of 1 : 5(Fe (III) : $NaBH_4$) after 30 min of reduction time. Size and shape of iron particles synthesized were round-form and 50 nm ~ 100 nm size. Zeta-potential of iron at the 100 mg/L of $Na_4O_7P_2$ was negative value, which is good for dispersion of metal particle. When $Na_4O_7P_2$(100 mg/L), PVP($FeCl_3$ : PVP = 1 : 4, w/w) and Pd($FeCl_3$ : $PdCl_2$ = 1 : 0.001, w/w) were used, iron nanoparticles which are round-shape, well-dispersed, near 100 nm-sized can be made.

• Bulletin of the Korean Chemical Society
• /
• v.26 no.2
• /
• pp.248-252
• /
• 2005

Synthetic layered double hydroxides (LDHs), [$Mg_4Al_2(OH)_{12}]CO_3{\cdot}nH_2O$, were prepared in the submicron size of plate-like polycrystals. Anion-exchange reactions with various linear dicarboxylic acids were performed to produce LDH/organic hybrid materials by solvothermal treatment in toluene. X-ray powder diffraction spectra for the products indicated that the interlayer spacings of LDHs remarkably changed, up to 20 $\AA$ when 1,10-decanedicarboxylic acid anions were intercalated as an organic guest. Dicarboxylates-LDHs samples could be also re-exchanged consecutively with other dicarboxylic acids or carbonate without serious destruction of layer structure under the scanning electron microscopic observation.

• Journal of the Korean Ceramic Society
• /
• v.22 no.5
• /
• pp.35-42
• /
• 1985

$eta$-Sialon powders were prepared by reduction-nitridation from mixture of Wando pyrophyllite and graphite as a reducing agent at 135$0^{\circ}C$ in 80% $N_2$-20% $H_2$ atmosphere. As the reaction products $Si_2ON_2$, $\beta$-$Si_3N_4$ a--$Si_3N_4$ and $\beta$-SiC were observed. Additive agents of MgO, CaO, $Y_2O_3$ were used for promoting the reduction and nitridiation aeaction. The present study was conducted to investigate the effects of silica-carbon ratio ($SiO_2$/C=weight ratio), raction time gas flow rate pellet size and powder packing on synthesis of $\beta$-Sialon from Wando pyropyllite.

• Journal of the Korean Ceramic Society
• /
• v.29 no.10
• /
• pp.779-784
• /
• 1992

In producing cordierite glass-ceramics by sintering, following experiments were conducted in order to determine the optimum heat-treatment schedule for high-crystallinity and dense sintered body. The glass composition of 11.67MgO-29.46Al2O3-52.88SiO2-5P2O5-1B2O3 (wt%) was selected on the basis of the early experiment. The 3-step heat treatment schedule was determined by the results of DTA, Dilatometric measurement and high-temperature XRD, where the particle-size-controlled glass powder was used. The degree of densification and the crystallinity were evaluated by the measurement of the bulk density and X-ray scattering intensity. The specimen fired with the optimum conditions showed ${\alpha}$-cordierite phase, relative density ∼98%, crystallinity ∼92%, thermal expansion coefficient ∼30${\times}$10-7/$^{\circ}C$, dielectric constant ∼5.5 and resistivity ∼1.0${\times}$1012 {{{{ OMEGA }}cm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.613-618
• /
• 1990

The pure and 6mol% MgO-doped ZrO2 powders were prepared by hot petroleum drying method. The power characterization of homogeneous fine powder was indentified by the method of thermal analysis, BET and electron microscope. The transformation, content of t-ZrO2, crystallite size and apparent strain were measured by X-ray diffraction technique. The prepared powders were transformed in order of amorphouslongrightarrowmetastable cubic ZrO2longrightarrowmetastable tetragonal ZrO2longrightarrowstable monoclinic ZrO2 by a adequate heat treatment. The stabilization of metastable phase can be discussed in terms of energetial concept ; the difference of surface energy and internal strain in particle.

• Journal of Surface Science and Engineering
• /
• v.36 no.1
• /
• pp.99-107
• /
• 2003

The diffusion coefficient of Xe-133 was obtained from an annealing test. The specimens were made from a UO$_2$ single crystal powder with natural enrichment. Weight and grain size were 300mg and ($23\mu\textrm{m}$, respectively. Oxygen potentials were obtained from an oxygen sensor. Released fractions were obtained from both results of gamma scans and quantitative analysis with MCNP code, The annealing test was performed at three temperatures at once. Diffusion coefficients of Xe-133 were calculated using slope of Booth theory in each O/M ratios. Activation energy and the pre-exponential factor of the diffusion coefficient were obtained. The activation energy of near stoichiomeric $UO_2$ is 310 kJ/mol. The measured values of near stoichiometric $UO_2$ are very close to other data available. Diffusion coefficients increase with hyper-stoichiometry, due to higher concentration of cation vacancies.

• Archives of Metallurgy and Materials
• /
• v.66 no.3
• /
• pp.783-787
• /
• 2021

This study suggests a new way to modify the size and morphology of Al-Fe phases in modified AA 7075 by using an Fe-Mn solid solution powder as the precursor. When Fe and Mn are added in the form of a solid solution, the diffusion of Fe and Mn toward the Al is delayed, thus altering the chemical composition and morphology of the precipitates. The fine, spherical precipitates are found to provide a good balance between strength and ductility compared to the case where Fe and Mn are separately added.

• Journal of Pharmaceutical Investigation
• /
• v.29 no.1
• /
• pp.37-45
• /
• 1999

ABSTRACT-A self-microemulsifying drug delivery system (SMEDDS) was developed to enhance the solubility and dissolution rate of poorly water soluble drug, biphenyl dimethyl dicarboxylate, DDB. The system was optimized by evaluating the solubility of DDB and the microemulsion existence range after the preparation of microemulsions with varying compositions of triacetin and surfactant-cosurfactant mixtures (Labrasol as surfactant (S) and the combination of Transcutol, Cremophor RH 40 and Plurol oleique as cosurfactant (CoS)). SMEDDS in this study markedly improved the solubility of DDB in water up to 10 mg/ml and the size of the o/w microemulsion droplets measured by dynamic light scattering showed a narrow monodisperse size distribution with an average diameter less than 50 nm. The microemulsion existing range is increased proportional to the ratio of S/CoS, however, it decreased remarkably as the oil content was more than 20%. In vitro dissolution study of SMEDDS showed a significantly increased dissolution rate of DDB in water (> 12 fold over DDB powder), and SMEDDS also had significantly greater permeability of DDB in Caco-2 cell compared to powders.

• Journal of Korean Society on Water Environment
• /
• v.25 no.5
• /
• pp.750-757
• /
• 2009

The ammonium ion exchange characteristics of natural zeolite were investigated to remove ${NH_4}^+-N$. The effect of water temperature, particle size and competitive cation on the exchange capacity was examined. Ammonium ion exchange capacity tended to decrease when the temperature increased from $25^{\circ}C$ to $40^{\circ}C$. Exchange capacity was increased according to the particle size of natural zeolite comes to be small. Batch isotherm experiments were conducted for measuring ammonium ion exchange capacity. The ion exchange capacity was well described either by the Langmuir isotherm model or by the Freundlich isotherm model. The ammonium ion exchange capacity ($q_m$) of zeolite carrier can be calculated $11.744mg-{NH_4}^+/g$-carrier. The ion exchange capacity of manufactured zeolite carrier was showed a similar tendency as ion exchange capacity of powder-sized natural zeolite. Therefore, zeolite carrier can be used for increasing of nitrogen removal efficiency in the wastewater treatment plants.