In this study, metallurgical grade (MG) silicon with 99% purity produced by arc furnace process was systematically investigated for slag refining. The most problematic impurities to remove from MG silicon are boron (B) and phosphorus (P). To remove B and P from MG-silicon, we used synthetic slag in the molten state. MG-silicon with synthetic slag of CaO, $SiO_2$, and $CaF_2$ was melted using by high-frequency induction furnace with electrical output of 50kW. Specimens prepared by various refining process conditions(holding time, mixture ratio) were inspected by combined analysis of ICP-MS and XRF. With this approach, B has been reduced to <5ppm, P to <1ppm and other impurities to 0.1~0.2% except for Calcium. Calcium has been increased from 17ppm to 1500ppm. Problem of calcium contamination will be resolved by additional refining processes.

• Journal of Korea Foundry Society
• /
• v.15 no.3
• /
• pp.235-241
• /
• 1995

In order to improve the production process of low cost and high purity Vanadium, this study was done to reduce $V_2O_5$ into V-Al master alloy by Aluminothermic Reduction, followed by refining of V-Al master alloy electron beam melting. As melting time was increased in electron beam melting of V, the contents of interstitial impurities and Al, Fe were decreased but the contents of Si, Mo and W were increased due to lower vapor pressure of these elements than that of matrix V. Consequently, it was profitable that melting of V was done for 180 seconds. In addition, with number of melting, the purity of V did not significantly vary, because volatile impurities in V were removed mostly during the first step of melting. As a result of V refining by electron beam melting, high purity Vanadium of 3N(99.91wt%) was acquired including interstitial impurities total contents of which were maximum 400ppm.

• Journal of Korea Foundry Society
• /
• v.23 no.2
• /
• pp.63-68
• /
• 2003

Al-Ti-C grain refiner form a relatively new alternative to the existing class of Al-Ti-B type grain refiners for achieving fine equiaxed structures in aluminum alloys during casting and solidification. The present study was carried out to investigate the influence of Al-Ti-C master alloys on the grain structure of Al-7Si alloys. The present study also investigates the relationship between grain refining efficiency and concentrations of Fe and Si in hypo-eutectic Al-Si alloys using Al-3Ti-0.13C master alloys. It is found that several parameters affect significantly the grain refining performance in silumin alloys. The present study reports the influence of various parameters such as alloy content, master alloy addition level, melt holding time and superheat on the grain refining efficiency in Al-7Si alloys.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.16.2-16
• /
• 2003

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.474-480
• /
• 1998

Microstructural characteristics of semi-solid state processed hypereutectic Al-Si alloys have been investigated. Main concern of the present study is to investigate the effects of P and Sr addition on the size and morphology change of the primary Si particles. Refinement of the primary Si particles was observed with the addition of P and Sr at the early stage of semi-solid state processing, but such a refining effects became negligible resulting in Si particles with a near-spherical morphology with continuous stirring. This implies that the microstructural transformation mechanism became more dependent to stirring effects than to the alloying effects during semi-solid state processing. Brittle fracture and agglomeration were proposed as the mechanisms for microstructural alterations during semi-solid state processing.

• Journal of Korea Foundry Society
• /
• v.17 no.3
• /
• pp.267-275
• /
• 1997

Fabrication of high strength Mg-Li-Al alloys by squeeze casting was established by the stabilization of melt and mold temperatures, applied pressure and the refining method. The entrapment of inclusions during pouring was prevented using 30 ppi alumina foam filter. The as-cast microstructure consists of a mixture of ${\alpha}$ and ${\beta}$ phases including AILi and $MgLi_2$, Al particles, which are distributed in the ${\beta}$ matrix. The grain sizes of gravity and squeeze casting alloys were 288 ${\mu}m$ and 207 ${\mu}m$ respectively. The addition of Al in Mg-Li alloys promoted the formation of second phase particles, which were adjusted to optimize the properties of Mg-Li-Al alloys. The Mg-10wt%Li-5wt%Al alloy after heat treatment at $350^{\circ}C$ for 1 hour showed the maximum hardness value. This is due to the facts that the amounts of ${\alpha}$ and ${\beta}$ phases and their distributions are dependent upon the solution treatment temperature, and that the amounts of AILi and $MgLi_2Al$ particles are dependent upon the Al content.

• Journal of Conservation Science
• /
• v.37 no.6
• /
• pp.738-747
• /
• 2021

This study attempted to investigate the metallurgical characteristic through material scientific analysis of hammer scale produced as a direct smelting method restoration experiment for each raw material of iron. To this end, four hammer scale groups were set up, respectively, by experimenting with Gyeongju-Gampo Iron sand and Yangyang Iron ore. For the analysis, principal component analysis, compound analysis, microstructure observation, and chemical composition were confirmed. As a result of principal component analysis, as forging and refining progressed, the content of Fe increased and the content of non-metallic objects decreased. As a result of compound analysis, iron oxide-based compounds were identified. As a result of confirming microstructure and chemical composition, Wüstite and Fayalite were observed overall, and agglomerated Wüstite were observed in some. Magnetite on shape of polygon and pillar was observed. In addition, it was confirmed that internal defects, impurities, and non-metallic interventions gradually decreased. In the future, it is necessary to investigate the metallurgical characteristic through material scientific analysis of hammer scale produced through restoration experiments using various raw material of iron, and compare them with those excavated from Iron manufacture ruins.

• Transactions of the Korean hydrogen and new energy society
• /
• v.7 no.1
• /
• pp.81-92
• /
• 1996

The Ar/Ar-$H_2$ plasma method was applied to reduce oxides and refine metals of V, Ta and B. In addition, the high temperature chemical reaction in Ar plasma and of the refining reaction in the Ar-(20%)$H_2$ plasma were analyzed. The crude V of 96wt% purity was obtained at the ratio of $C/V_{2}O_{5}=4.50$ by the Ar plasma reduction grade and the maximum reduction was obtained at $C/V_{2}O_{5}=4.50$ due to the $O_{2}$ loss from the thermal decomposition of vanadium oxide. In the Ar-(20%)$H_2$ plasma refining, the metallic V of 99.2wt% was produced at the ratio of $C/V_{2}O_{5}=4.40$. It was considered that a main refining reaction resulted from the chemical reaction between the residual carbon and residual oxygen. The metallic Ta of 99.8wt% was obtained at the ratio of $C/Ta_{2}O_{5}=5.10$ in a Ar plasma reduction and the Oz loss from the thermal decomposition of tantalum pentoxide did not take place. The deoxidation reaction was more significant than the decarburization reaction in the Ar-(20%)$H_2$ plasma refining and the metallic Ta of 99.9wt% was produced within the range of $C/Ta_{2}O_{5}$ ratio of 4.50 to 5.10. The Vickers hardness of Ta in the above mentioned range was about 220Hv due to the decrease in a residual oxygen by the deoxidation reaction. On the other hand, C is no suitable agent for the reduction of $B_{2}O_{3}$ by the Ar and Ar-$H_2$ plasma. But Fe-B-Si alloy was produced with the reduction of $B_{2}O_{3}$ in the melt when Fe, C, $B_{2}O_{3}$, and ferroboron mixtures were melted by the high frequency induction melting.

• Journal of the Korean institute of surface engineering
• /
• v.19 no.1
• /
• pp.13-19
• /
• 1986

Manganese in the Anode slime and the paste-positive material of waste-dry cell was recovered by leaching with the hydrochloric acid solution. The impurities (Zn, Fe, Pb), co-leached with manganese were removed from the leached solution prior to electrolysis by hydrometallurgical techniques such as the neutralization with ammonium hydroxide and cementation on manganese powder. The electrodeposition of manganese from the purified chloride solution with sodium selenate was performed. Cathode current efficiency was found to be affected significantly by the concentration of sodium selenate and ammonium chloride salt, bath temperate, current density and PH. The current efficiency of about 88.7% was obtained by electrolysis manganese chloride solution with sodium selenate (0.1/g) at 10$^{\circ}C$.

• Resources Recycling
• /
• v.21 no.4
• /
• pp.53-59
• /
• 2012

In this study, behaviors of removing Sb and Pb by oxidation of molten Bi-Pb-Sb alloy which is a by-product of non-ferrous smelting process was investigated. The molten alloy was oxidized at 1173 K by bubbling $N_2+O_2$ gas through a submerged nozzle. The Sb was removed and recovered as mixed phase of $Sb_2O_3$ and metal Sb. In the case of bubbling $N_2+O_2$ gas into molten Bi-Pb alloy at 923 K, Pb was oxidized and removed to slag. But Bi could not be refined due to simultaneous oxidization of Bi with Pb.