• Journal of Powder Materials
• /
• v.6 no.2
• /
• pp.145-151
• /
• 1999

Nickel silicides ($Ni_5$Si$_2$, Ni$_2$Si and NiSi) have been synthesized by mechanical alloying (MA) of Ni-27.9at.9at%Si, Ni-33.3at% and Ni-50.0at% powder mixtures, respectively. From in situ thermal analysis, eash citical milling period for the formation of the three phases was observed to be 40.2, 34.9 and 57.5 min, at which there was a rapid increase in temperature. This indicates that rapid, self-propagating high-temperature synthesis (SHS) reactions were observed to produce the three phases during room-temperature high-energy ball milling of elemental powders. Each Ni silicide, Ni and Si, however, coexisted for an extended milling time even after the critical milling period. The powders mechanically alloyed after the critical period showed the rapid increase in microhardness. The Hv values were found to be higher than 1000kgf/mm$^2$. The formation of nickel silicides by mechanical alloying and the relevant reaction rates appeared to be influenced by the critical milling period and the heat of formation of the products involved ($Ni_5$Si$_2$$\rightarrow$-43.1kJ/mol.at., Ni$_2$Si$\rightarrow$-47.6kJ/mol.at., NiSi$\rightarrow$-42.4kJ/mol.at).

• Journal of Powder Materials
• /
• v.6 no.1
• /
• pp.27-35
• /
• 1999

A study was made on the fabrication of nanostructured Fe-Co powders by mechanical alloying and their magnetic properties. Microstrural development during the process of MA was inverstigated by means of X-ray diffraction, differential thermal analyzer, scanning electron microscopy and transmission electron microscopy. The magnetic properties of NS Fe-Co powders were evaluated through the measurements of the saturation magnetization $(M_s)$ as well as the coercivity $(H_c)$. The average grain size calculated from line braodening in XRD peak was about 10nm or less and confirmed by TEM. In this experiment, two different milling methods (cycle opertion and conventional milling) were used. Cycle operation had an advantage over the conventional milling method in that more refined powders can be obtained. Solid state alloying of the components was confirmed from both the change of the saturation magnetization and the change of lattice parameter with Co contentration. Maxium $M_s$ was obtained at the composition of 30at.%Co. Relatively high coercivities of 10~150e were obtained for the compositions investigated, and this seems to be due to the high amount of internal strain introduced during milling.

• Journal of Powder Materials
• /
• v.8 no.4
• /
• pp.223-230
• /
• 2001

Ti-37.5at%Si elemental powder mixtures were mechanically alloyed by a high-energy ball mill, followed by CIP (cold isostatic pressing) and HIP (hot isostatic pressing) for different processing conditions. Only elemental phases (Ti and Si) were observed for the 5 min mechanically alloyed (MA 5 min) powder, but only $Ti_5Si_3$phase was observed for the 30 min mechanically alloyed (MA 30 min) powder. $Ti_5Si_3$phase was observed for the HIPed compact of MA 5 min and 30 min powders at 150 and 190 MPa for 3 hr at $1000^{\circ}C$. For the HIPed compacts, the highest sintered density was obtained to be 99.5% of theoretical density by a HIP step at $1350^{\circ}C$ at 190MPa for 3hr. The hardness values of the HIPed $Ti_5Si_3$compacts at $1350^{\circ}C$ at 150/190 MPa for 3hr were higher than HRC 76. The densification and mechanical property of HIPed $Ti_5Si_3$compacts was found to depend on more HIP temperature than HIP pressure.

• Journal of Powder Materials
• /
• v.4 no.3
• /
• pp.179-187
• /
• 1997

Milling media of steel and zirconia were used to produce $MoSi_2$ by mechanical alloying (MA) of Mo and Si powders. The effect of milling media on MA of Mo-65.8at%Si powder mixture has been investigated by SEM, XRD, DTh and in-situ thermal analysis. The powders mechanically alloyed by milling medium of steel for 8 hours showed the structure of fine mixture of Mo and Si, and those mechanically alloyed by milling medium of zirconia for longer milling time showed the structure of fine mixture of Mo and Si. The tetragonal $\alpha$-$MoSi_2$ Phase and the tetragonal $Mo_5Si_3$ phase appeared with small Mo peaks in the powders milled by milling medium of steel for 4 and 8 hours. The $\alpha$-$MoSi_2$ phase and the hexagonal $\beta$-$MoSi_2$ phase were formed after longer milling time. The $\alpha$-$MoSi_2$ phase appeared with large Mo peaks in the powders milled by milling medium of zirconia for 4 hours. The phases, $\alpha$-$MoSi_2$ and $\beta$-$MoSi_2$. were formed in the powders milled for longer milling time. DTA and annealing results showed that Mo and Si were transformed into $\alpha$-$MoSi_2$ and $Mo_5Si_3$, while $\beta$-$MoSi_2$ into $\alpha$-$MoSi_2$. In-situ thermal analysis results demonstrated that there were a sudden temperature rise at 212 min and a gradual increase in temperature in case of milling media of steel and zirconia, respectively. The results indicate that MA can be influenced by materials of milling medium which can give either impact energy on powders or thermal energy accumulated in vial.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.516-520
• /
• 1999

Mechanical alloying (MA) by planetary type ball mill of pure iron powders was carried out under the ammonia gas atmosphere. The powders of metastable iron nitrides was synthesized up to the nitrogen content of 23 at% N. The observed phases are identified as the super-saturated bcc solid solution for the nitrogen concentration below 14.5 at% N and the non-equilibrium hcp phase stable at high temperature for 20.8 at.% N. Magnetization of Fe-N powders gradually decreases with increasing the N concentration on contrast to the enhancement reported for the bct iron nitrides. Neutron diffraction experiments also provide detailed information concerning the local atomic structure surrounding the nitrogen atoms. The coordination number of Fe atom around a nitrogen atom for the iron nitride containing 9.5 at% N turns out to be 3.9 atoms. This suggests that a nitrogen atom is situated at a center of the tetrahedron formed by iron atoms.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1292-1293
• /
• 2006

A non-equilibrium powder metallurgy processing such as an MA/SPS (Mechanical Alloying / Spark Plasma Sintering) process is examined in a Ti-48moll%Al. TiAl intermetallic compound is a potential light-weight/high-temperature structural material. One of the major problems, however, limiting the practical use of the material is its poor workability. From this point, the powder metallurgy (PM) processing route has been attractive alternative of the conventional processing for such material The MA/SPS process is able to apply to a LIGA process. Optimization of the pseudo-superplasticity enables to fabricate micro-parts made of fine grained ceramics composites of TiAl by the LIGA process.

• Korean Journal of Materials Research
• /
• v.10 no.7
• /
• pp.499-504
• /
• 2000

Recently there have been many investigations on the synthesis and properties of transition metal trialuminides based on Ti, Zr, V, Nb and Ta for use aircraft structure materials in an elevated environment. The effect of Zr additions on the formation behaviour of Al-Nb alloy was investigated. Al-1.3at.%(Nb+Zr) alloys with different Nb to Zr atomic 1:3, 1:1 and 3:1 were prepared by mechanical alloying(MA). The morphological changes and microstructural evolution of Al-Nb-Zr powders during MA were investigated by SEM, XRD and TEM. The intermetallic compound phase of $Nb_2Al\; and\; Al_3Zr_4$ was identified by X-ray diffraction. The intemetallic compound of $Al_3Zr,\; Al_3Nb$ and $Al_3Zr_4$ were formed by heat treatment for 1 hour at $500^{\circ}C$. The size of intermetallic compounds observed by TEM were approximately below 100nm, when they were heat treated after mechanically alloying for 30 hours.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1035-1041
• /
• 2001

The refining process and solubility of Ti in Al matrix during mechanical alloying (MA) were investigated by using X-ray diffraction (XRD), transmission electron microscopy (TEM) as functions of alloy composition, milling time and ball to powder ratio (BPR). Mechanical alloyed samples were annealed for investigating their stability and the formation behavior of$Al_3Ti$in the temperature range from$200{\circ}C$to$600{\circ}C$. It is observed from present experimental that disappearance of Ti peaks in mechanically alloyed Al-10wt%Ti is not simply attributable to the dissolution of Ti into Al, but associated mainly with extreme refining and/or heavy straining of Ti particles The annealing of the mechanically alloyed Al-Ti powders show differences in aluminide formation behavior when Ti content in Al is equal to or less than l0wt% and higher than l5wt%Ti. When Ti-content in Al is equal to or less than l0wt%, the MA powders transform directly to a global equilibrium state forming $DO_{22}- type\;Al_3$Ti above$400{\circ}C$. In the Al-Ti samples with equal to or higher than l5wt%Ti, transitional phases of cubic$Al_3Ti$and tetragonal $Al_{24}Ti_8$ are formed above$400{\circ}C$. They are stable only below$500{\circ}C$, and, $DO_{22}-type\;Al_3Ti$ becomes dominant aluminide at temperature higher than$ 600{\circ}C$.

• Journal of Powder Materials
• /
• v.12 no.2 s.49
• /
• pp.136-145
• /
• 2005

Graphite-Ni composite powders were synthesized by mechanical alloying(MA) and spray drying(SD). Fabricated powders as well as commercial graphite-Ni powders were thermally sprayed on mild steel substrates using high velocity oxygen fuel (HVOF) thermal spray process and flame thermal spray process. The effects of several process parameters on related properties in thermally sprayed coatings have been investigated and correlated with microstructures in this study. The results indicated that the desired properties can be obtained when commercial powders were applied using HVOF process, while coating properties in case of MA powder application were inferior to those in HVOF process in so far. However, it is suggested that property enhancement can be obtained if the fraction of hexagonal graphite phase can be increased in mechanically alloyed powders.

• Journal of Powder Materials
• /
• v.5 no.2
• /
• pp.145-153
• /
• 1998

W-Cu alloy is attractive to thermal managing materials in microelectronic devices because of its good thermal properties. The metal injection molding (MIM) of W-Cu systems can satisfy the need for mass production of the complex shaped W-Cu parts in semiconductor devices. In this study, the application of MIM process of the mechanically alloyed (MA) W-Cu composite powders, which had higher sinterability were investigated. The MA W-Cu powders and reduction treated (RT) powders were injected by using of the multicomponent binder system. The multi-stage debinding cycles were adopted in $N_2$ and $H_2$ atmosphere. The isostatic repressing treatment was carried out in order to improve the relative density of brown parts. The brown part of RT W-Cu composite powder sintered at 110$0^{\circ}C$ had shown the higher sinterability compared to that of MA powder. The relative sintered density of all specimens increased to 96% by sintering at 120$0^{\circ}C$ for 1 hour. The relationship between green density and the sintering behavior of MA W-Cu composite powder was analyzed and discussed on the basis of the nanostructured characteristics of the MA W-Cu composite powder.