• 동력기계공학회지
• /
• 제9권4호
• /
• pp.137-142
• /
• 2005

The effects of temperature and initial crack length on impact fracture behavior of side plate material of 35 ton class FRP ship, which are composed by glass fiber and unsaturated polyester resin, were investigated. Impact fracture toughness of GF/PE composites displayed maximum value when the temperature of specimen is room temperature and $50^{\circ}C$, and with decrease in temperature of specimen, impact fracture toughness decreased. Impact fracture energy of GF/EP composites decreased with increase in initial crack length of specimen, and this value decreased rapidly when the temperature of specimen is lowest, $-25^{\circ}C$,. It is believed that sensitivity of notch on impact fracture energy were increased with decrease in temperature of specimen. As the GF/EP composites exposed in low temperature, impact fracture toughness of composites decreased gradually owing to the decrease of interface bonding strength caused by difference of thermal expansion coefficient between the glass fiber/polyester resin. Further, decrease of interface bonding strength of composites with decrease in specimen temperature was ascertained by SEM photograph of impact fracture surface.

• 한국강구조학회 논문집
• /
• 제11권1호통권38호
• /
• pp.33-42
• /
• 1999

궤도용 차량의 안전성 확보를 위한 연구의 일환으로서 레일강의 균열 발생 조건과 모재와 용접부에 대한 정적파괴거동 및 단일모드 하중하의 피로균열진전거동을 검토하였다. 레일에서 횡방향 균열의 원점은 표면하층균열이며 이는 최대전단응력에 의해 발생하였다. 또한 표면하층균열의 크기가 증가함에 따라 균열의 진전은 전단모드에서 혼합모드로 천이될 가능성이 증가하였다. 용접부의 평면변형률 파괴인성은 조직의 조대화와 경도의 상승으로 인하여 모재에 비하여 약 10% 저하하였다. 용접부의 제 2단계 영역의 피로 균열진전속도는 낮은 ${\Delta}K$ 영역에서 모재에 비하여 저하하였으나 높은 ${\Delta}K$영역에서는 이의 차이가 소멸되었으며 이러한 경향은 R=0.1의 낮은 응력비에서 현저하였다. 이는 용접부의 미시조직이 모재에 비하여 성장하였기 때문이라고 판단된다.

• Structural Engineering and Mechanics
• /
• 제74권6호
• /
• pp.747-756
• /
• 2020

High-strength concrete (HSC) generally is made with high amount of cement which may release large amount of hydration heat at early age. The hydration heat will increase the internal temperature of slab and may cause potential cracking. In this study, slab specimens with a dimension of 600 × 600 × 100 mm were cast with concrete incorporating silica fume for test. The thermistors were embedded in the slabs therein to investigate the interior temperature development. The test variables include water-to-binder ratio (0.25, 0.35, 0.40), the cement replacement ratio of silica fume (RSF; 5 %, 10 %, 15 %) and fly ash (RFA; 10 %, 20 %, 30 %). Test results show that reducing the W/B ratio of HSC will enhance the temperature of first heat peak by hydration. The increase of W/B decrease the appearance time of second heat peak, but increase the corresponding maximum temperature. Increase the RSF or decrease the RFA may decrease the appearance time of second heat peak and increase the maximum central temperature of slab. HSC slab with the range of W/B ratio of 0.25 to 0.40 may occur cracking within 4 hours after casting. Reducing W/B may lead to intensive cracking damage, such as more crack number, and larger crack width and length.

• Biomaterials and Biomechanics in Bioengineering
• /
• 제5권1호
• /
• pp.11-23
• /
• 2020

Total hip prosthesis is used for the patients who have hip fracture and are unable to recover naturally. To de-sign highly durable prostheses one has to take into account the natural processes occurring in the bone. Finite element analysis is a computer based numerical analysis method which can be used to calculate the response of a model to a set of well-defined boundary conditions. In this paper, the static load analysis is based, by se-lecting the peak load during the stumbling activity. Two different implant materials have been selected to study appropriate material. The results showed the difference of maximum von Misses stress and detected the frac-ture of the femur shaft for different model (Charnley and Osteal) implant with the extended finite element method (XFEM), and after the results of the numerical simulation of XFEM for different was used in deter-mining the stress intensity factors (SIF) to identify the crack behavior implant materials for different crack length. It has been shown that the maximum stress intensity factors were observed in the model of Charnley.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 봄 학술발표회 논문집
• /
• pp.751-756
• /
• 2000

The structural behavior of reinforced concrete slabs strengthened by glass fiber reinforced plastic-panels experimentally investigated. The experimental variables are strengthening length, strengthening width, and pre-crack existence. The pre-cracked slabs are initially loaded to 70 percent of ultimate flexural capacity and subsequently repaired with GFRP-Panels bonded to the tension face of the slabs. Five one-way slabs were tested to failure. The main failure mode of strengthened slabs is separation failure by crack propagation from load point section to end of plate. The behavior of strengthened slabs is represented by a maximum load, load-deflection curves an load-strain curves.

• Journal of Biosystems Engineering
• /
• 제26권2호
• /
• pp.177-188
• /
• 2001

This research was carried out to examine the optimum design conditions of a vertical small-scale milling machine where the rough rice is processed directly into the white rice in one pass. Effects of the main spindle speed, feed screw pitch and ceramic coating length of the roller on various milling characteristics such as white rice processing capacity, electric energy consumption, rice temperature increase, broken rice ratio, moisture reduction, outlet force and crack ratio increase were studied. The results are as follows. 1. The maximum white rice processing capacity and the lowest crack ratio increase, were obtained from a machine with specification: main spindle speed of 970rpm having a feed screw pitch of 19㎜. 2. The minimum electric energy consumption was obtained with the main spindle speeds of 900 and 970rpm respectively having a feed screw pitch of 19㎜. 3. The rice temperature was increased as the feed screw pitch decreased and the main spindle speed increased. 4. Broken rice ratio was relatively low with the range of 0.8∼1.3%. 5. Moisture content loss was with the range of 0.05∼0.4%. 6. The highest outlet force was 0.72kg$\_$f/ with 900rpm of the main spindle speed and 19㎜ of the feed screw pitch and the lowest outlet force was 0.18∼0.34kg$\_$f/ with 970rpm of the main spindle speed and 16㎜ of the feed screw pitch. 7. The optimum design conditions for the vertical small-scale milling machine were obtained at 970rpm of the main spindle speed, 19㎜ of the feed screw pitch and 20㎜ of the ceramics coating length.

• 대한기계학회논문집
• /
• 제8권3호
• /
• pp.195-200
• /
• 1984

본 연구에서는 SUS 304강의 상온하의 평골재 표면에 발생. 성장하는 미소표면 피로균열의 거동을 파괴역학적 관점과 수법으로 정량적으로 조사하려는 연구의 일환 이다.

• 한국정밀공학회지
• /
• 제27권10호
• /
• pp.69-76
• /
• 2010

This study examined how the fracture toughness is affected according to the variation of the initial crack length and the fiber arranged angle using FEA method and experimental method. Therefore, the energy release rates were calculated and compared by J-integral method and VCCT(Virtual Crack Closure Technique). The results of fracture toughness test verified these results. At this time, the locus method was used in order to determine the energy release rate. When the results of FEA were compared with those of experiment, all of those decreased with the increase of angle between load and the fiber arranged direction. The decrease was due to reducing maximum load and stiffness, and the reason of reduction has been judged that the inplane shear stress.

• 한국재료학회지
• /
• 제14권6호
• /
• pp.425-431
• /
• 2004

A laser welding was applied between sintered tip of Fe-Co-W and low carbon steel shank for the diamond saw blade. The welding characteristics and formation of defects were investigated carefully for the weld fusion zone in different welding condition. Dendrite arm spacing in weld bead decreased with decrease of heat input. Co and W increased and Fe decreased in the weld fusion zone with increase of the heat input. The corresponding change of composition was observed with the change of beam position. The maximum and total length of crack decreased with increase of the heat input. The crack in weld bead was propagated along the dendrite boundary and was caused mainly by the segregation of constituent during the solidification.

• Advances in Computational Design
• /
• 제4권3호
• /
• pp.295-305
• /
• 2019

The sealing cement of total hip arthroplasty is the most widely used binder in orthopedic surgery for anchoring implants to their recipient bones. Nevertheless, this latter remains a fragile material with weak mechanical properties. Inside this material cracks initiate from cavities. These cracks propagate under the effect of fatigue and lead to the failure of this binder and consequently the loosening of the prosthesis. In this context, this work consists to predict the position of cracks initiation and their propagations path using the Extended Finite Element Method (XFEM). The results show that cracks can only be initiated from a sharp edges of an ellipsoidal cavity which the ratio of the minor axis over the major axis is equal to 0.1. A maximum crack length of 19 ?m found for a cavity situated in the proximal zone position under a static loading. All cracks propagate in same(almost) way regardless of the cavity(site of initiation) position and its inclination in the proximal zone.