• 한국전기전자재료학회논문지
• /
• 제27권7호
• /
• pp.462-467
• /
• 2014

In this paper, we studied the magnetic composite sheets for electromagnetic wave noise absorber of quasi-microwave band by using soft magnetic FeSiCr and Fe50Ni flakes with the thickness of about $1{\mu}m$ and polymer. The magnetic hysteresis curve including saturation magnetization and residual magnetization and the complex permeability characteristics of the composite sheets were investigated to clarify the mixing effect on electromagnetic wave absorption properties. The saturation magnetization was decreased about 10% while the residual magnetization was increased about 15% and the real parts of complex permeability at below 500 MHz were increased 0.6~4 while those values at above 500 MHz were decreased 0.4~2.5 according to the change of contents of FeSiCr and Fe50Ni powders. As a result, the reflection loss can be moved to the lower frequency from 2~3 GHz to 1~1.5 GHz as the contents of Fe50Ni flaky powder into FeSiCr flaky powder was increased up to 50%.

• Journal of Magnetics
• /
• 제1권1호
• /
• pp.24-30
• /
• 1996

The relationship between effective permeability and the remanence ratio of an Fe-based amorphous alloy (Metglas 2605S3A) is investigated over a wide frequency range, in an effort to understand magnetization behavior of the alloy. In the frequency range from 1 to 200 kHz, the permeability is maximum at the remanence ratio of 0.4-0.5 and, at frequencies over 500 kHz, the correlation with negative coefficients emerges indicating that the permeability decreases with the remanent ratio, except for the ribbon coated with an insulating layer of MgO which exhibits both high values of the effective permeability and remanence ratio. It is considered from the correlation results that the boundary at which the dominant magnetization mechanism changes from domain wall motion to spin rotation is near 500 kHz. The core loss is also investigated as a function of annealing time when the samples are annealed at a fixed temperature of $435^{\circ}C$. The core loss in most cases decreases with the annealing time, the degree of the loss may consist of the hysteresis loss and anomalous eddy current loss. The two loss components are considered to be of similar magnitudes at low frequencies while, at high frequencies, the dominant contribution to the total loss is the anomalous loss.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 추계학술대회 논문집 학회본부 C
• /
• pp.1050-1053
• /
• 1998

To be applied to electrical equipment HTSC tapes have to endure external stress and so on. The critical current density has been shown depending on the mechanical properties. strain and bending stress. AC loss reduction is primary concern in the development of such high-efficiency equipment. AC losses in Bi-2223 silver-sheathed tapes, both single and multi-filamentary, were investigated by means of AC magnetization techniques. The results were compared with the hysteresis loss equation based on Bean model and the eddy current loss equation. The AC loss of the mono-filamentary tape was the hysteresis. On the contrary, the AC loss of the multi-filamentary tape was substantially dominated by the eddy current loss in the Ag matrix.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 추계학술대회 논문집 학회본부 B
• /
• pp.702-705
• /
• 1998

To be applied to electrical equipment HTSC tapes have to endure external stress and so on. The critical current density has been shown depending on the mechanical properties, strain and bending stress. AC loss reduction is primary concern in the development of such high-efficiency equipment. AC losses in Bi-2223 silver-sheathed tapes, both single and multi-filamentary, were investigated by means of AC magnetization techniques. The results were compared with the hysteresis loss equation based on Bean model and the eddy current loss equation. The AC loss of the mono-filamentary tape was the hysteresis. On the contrary, the AC loss of the multi-filamentary tape was substantially dominated by the eddy current loss in the Ag matrix.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 추계학술대회 논문집 학회본부A
• /
• pp.382-385
• /
• 1998

To be applied to electrical equipment HTSC tapes have to endure external stress and so on. The critical current density has been shown depending on the mechanical properties, strain and bending stress. AC loss reduction is primary concern in the development of such high-efficiency equipment. AC losses in Bi-2223 silver-sheathed tapes, both single and multi-filamentary, were investigated by means of AC magnetization techniques. The results were compared with the hysteresis loss equation based on Bean model and the eddy current loss equation. The AC loss of the mono-filamentary tape was the hysteresis. On the contrary, the AC loss of the multi-filamentary tape was substantially dominated by the eddy current loss in the Ag matrix.

• 한국초전도ㆍ저온공학회논문지
• /
• 제1권2호
• /
• pp.30-36
• /
• 1999

Superconductors are dissipative when exposed to time-varying magnetic fields. To analyze the AC characteristics of a superconductor, one usually needs to know magnetization curves of it. Good magnetization curves can be obtained only in homogeneous magnetic filed. In This paper, we report the setup and test results of a magnetization measurement system, which consists mainly of frequency-variable power supply and homeogenous magnet with 7-cm long air gap. Special emphasis are foused on the design and fabrication of the magnet, which aims to give background magnetic fields, and on the overall characteristics of the system.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2004년도 동계학술연구발표회 논문개요집
• /
• pp.179-180
• /
• 2004

• 대한전기학회논문지:전기기기및에너지변환시스템부문B
• /
• 제49권11호
• /
• pp.729-736
• /
• 2000

This paper deals with the characteristic analysis of magnetizer for convergence purity magnet by the finite element method. The analysis utilizes combined method of the time-stepped finite element analysis and the Preisach model with hysteresis phenomena. In the finite element analysis, the non-linearity and the eddy current of the magnetizing fixure and permanent-magnet are taken account. The magnetization distribution in the permanent magnet is determined by using Preisach model which are composed of Everett function table and the first order transition curves is obtained by the Vibrating Sample Magnetometer. The calculated flux density values on the surface of the permanent magnet are led to the approximated gauss density values measured by the gauss meter. As a result, winding current, copper loss, eddy current loss of the magnetizing yoke, flux plot, surface gauss plot, temperature rise of the coil and resistor variation, vector diagram of magnetization distribution are shown.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 1999년도 제1회 학술대회논문집(KIASC 1st conference 99)
• /
• pp.77-80
• /
• 1999

In this paper. We experimentally investigated the magnetic properties of YBCO bulk superconductor using AC magnetization method. The sample is 2.8cm wide in a diameter and 1.4cm long. We applied Ac magnetic field parallel to the direction of length of YBCO bulk. It is observed that YBCO bulk has the diamagnetic properties. AC loss calculation of YBCO bulk superconductor was performed by evaluating the total area of magnetization traces. As depends on the frequency and amplitude of the applied magnetic field.

• 한국분말재료학회지
• /
• 제24권2호
• /
• pp.122-127
• /
• 2017

Fe-6.5 wt.% Si alloys are widely known to have excellent soft magnetic properties such as high magnetic flux density, low coercivity, and low core loss at high frequency. In this work, disc-shaped preforms are prepared by spark plasma sintering at 1223 K after inert gas atomization of Fe-6.5 wt.% Si powders. Fe-6.5 wt.% Si sheets are rolled by a powder hot-rolling process without cracking, and their microstructure and soft magnetic properties are investigated. The microstructure and magnetic properties (saturation magnetization and core loss) of the hot-rolled Fe-6.5 wt.% Si sheets are examined by scanning electron microscopy, electron backscatter diffraction, vibration sample magnetometry, and AC B-H analysis. The Fe-6.5 wt.% Si sheet rolled at a total reduction ratio of 80% exhibits good soft magnetic properties such as a saturation magnetization of 1.74 T and core loss ($W_{5/1000}$) of 30.7 W/kg. This result is caused by an increase in the electrical resistivity resulting from an increased particle boundary density and the oxide layers between the primary particle boundaries.