• Journal of Surface Science and Engineering
• /
• v.49 no.3
• /
• pp.231-237
• /
• 2016

This article reports a new chemical bath for preparing a mirror-like surface of AZ31 Mg alloy. In order to find an appropriate chemical polishing solution, four different acidic solutions of sulphuric acid, nitric acid, acetic acid and a specially designed mixture of nitric acid and acetic acid were investigated in view of the changes in surface appearance, roughness and dissolution rate of AZ31 Mg alloy. The surface scales on AZ31 Mg alloy were readily removed by all the acidic solutions, but a reflective surface was produced only by etching in the specially designed solution, and only after a specific etching time. The surface roughness increased with etching time in sulphuric acid, nitric acid, and acetic acid, but it lowered after a specific etching time in the specially designed mixture of nitric acid and acetic acid. Dissolution rate of the alloy in the specially designed mixture of nitric acid and acetic acid appeared to be more than twice than that in separate nitric acid or acetic acid. In this work, we recommend the mirror-like surface of AZ31 Mg alloy obtained by polishing for an optimum time in a mixture of nitric acid and acetic acid for following surface finishings, chemical conversion coating, electroplating, electrophoretic painting and anodizing treatment.

• Journal of Mechanical Science and Technology
• /
• v.20 no.8
• /
• pp.1209-1216
• /
• 2006

An AZ31 magnesium alloy was tested at constant temperatures ranging from 423 to 473 K (0.46 to 0.51 Tm) under constant stresses. All of the creep curves exhibited two types depending on stress levels. At low stress (${\sigma}/ G < 4 {\times}10^{-3}$), the creep curve was typical of class A (Alloy type) behavior. However, at high stresses (${\sigma}/ G > 4 {\times}10^{-3}$), the creep curve was typical of class M (Metal type) behavior. At low stress level, the stress exponent for the steady-state creep rate was of 3.5 and the true activation energy for creep was 101 kJ/mole which is close to that for solute diffusion. It indicates that the dominant deformation mechanism was glide-controlled dislocation creep. At low stress level where n=3.5, the present results are in good agreement with the prediction of Fridel model.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.62-65
• /
• 2008

Extrusion characteristics of Mg alloys were studied experimentally. The Al-Zn-Mg alloys, AZ31, AZ6l, AZ80, and AZ91 were extruded with hot hydrostatic extrusion process. The hydrostatic process was efficient to reduce surface friction and extend steady state region in extrusion which made it more convenient to examine deformation behavior of the alloys avoiding the disturbance caused by temporary contact state between billet and die, and billet and container. High pressure was cooperative to expand forming limit of the alloys which were applied on the billet during the extrusion process. Extrusion limits were traced in temperature and extrusion speed domain with changing composition of the alloying elements. Effects of process parameters on extrusion load and microstructure evolution were investigated also.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.231-234
• /
• 2005

The high temperature deformation behavior of AZ 31 Mg alloy was investigated by designing a back propagation neural network that uses a gradient descent-learning algorithm. A neural network modeling is an intelligent technique that can solve non-linear and complex problems by learning from the samples. Therefore, some experimental data have been firstly obtained from continuous compression tests performed on a thermo-mechanical simulator over a range of temperatures $(250-500^{\circ}C)$ with strain rates of $0.0001-100s^{-1}$ and true strains of 0.1 to 0.6. The inputs for neural network model are strain, strain rate, and temperature and the output is flow stress. It was found that the trained model could well predict the flow stress for some experimental data that have not been used in the training. Workability of a material can be evaluated by means of power dissipation map with respect to strain, strain rate and temperature. Power dissipation map was constructed using the flow stress predicted from the neural network model at finer Intervals of strain, strain rates and subsequently processing maps were developed for hot working processes for AZ 31 Mg alloy. The safe domains of hot working of AZ 31 Mg alloy were identified and validated through microstructural investigations.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.18-18
• /
• 2012

마그네슘 합금의 화성처리는 주로 탈지-산세-디스머트-화성처리의 4단계를 거쳐 진행되는 것으로 알려져 있다. 즉, 마그네슘 합금은 공기 중에서 자연 산화막이 쉽게 생성되며 이때 생성된 산화막을 제거하기 위한 산세 공정이 필수적이다. 본 연구에서는 AZ91D 마그네슘 주조재에 주로 사용되어 왔던 다양한 산 종류에 따른 AZ31B 마그네슘 판재의 산 에칭 후의 표면 상태 및 부식 거동을 관찰하였다. 따라서 AZ31B에 적합한 산 종류를 선별하고 그에 따른 표면 거동에 대한 논의를 통하여 마그네슘 합금의 표면에 대한 이해를 높이고자 한다.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.6
• /
• pp.9-16
• /
• 2020

This study aims to assess the effects of specimen thickness (ST) on fatigue crack growth in the early stages of crack propagation and near failure in magnesium alloys. The analysis of variance (ANOVA) method was adopted because fatigue crack propagation in magnesium alloys exhibits statistical behavior. The equality of variance test and residual diagnostics were performed on the grown cracks to confirm the validity of ANOVA by verifying the normal distribution and mutual independence of the residuals and their homoscedasticity. ANOVA confirmed that ST heavily impacts crack growth; i.e., when ST is smaller, cracks grow faster in the early crack propagation stage and break more quickly before the formation of larger cracks. We found that ST significantly affects fatigue crack growth in the early crack propagation stage and near the failure stage in magnesium alloys. The regression model was also used to predict crack formation near the failure stage.

• Korean Journal of Metals and Materials
• /
• v.47 no.1
• /
• pp.1-6
• /
• 2009

Magnesium alloys are drawing a lot of attention and have been extensively studied. The major obstacle to the practical application of the alloys is the poor formability at room temperature, originating basically from the insufficient number of slip system. Development of a proper texture is one promising solution to improve the formability. In the present work, after extrusion and full annealing, microstructures, texture developments and tensile properties of AZ31 Mg alloys are studied. After full annealing strong <1010>||ED fiber texture and weak <1120>+<1230>||ED fiber texture (c-axes in the radial direction) were developed. The textures are distinctly influencing the tensile properties, which can be understood in terms of the activation of basal slip modes. With the random orientation, which is developed in the $45^{\circ}$ sample to the extrusion direction, the better workability can be achieved at room temperature.

• Transactions of Materials Processing
• /
• v.17 no.7
• /
• pp.466-472
• /
• 2008

In this paper, tension tests and formability tests are performed to construct a database related to mechanical properties and the formability of the AZ31B Mg alloy sheet. A forming test with a hemi-spherical punch is conducted at varying temperatures to establish a forming limit diagram. In order to verify the applicability of the analysis using the conventional flow hardening model, a finite element analysis is performed on the hemi-spherical punch forming process and the results are compared with experimental ones. The study investigates problems involving a computational analysis that does not consider flow softening of the magnesium alloy at elevated temperatures.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.67-69
• /
• 2006

Since magnesium alloy has a limited formability at room temperature, forming should be carried out at the elevated temperature. If the initial grain size is small, superplasticity could be expected over $400^{\circ}C$. Using superplastic behavior, blow forming can be used to overcome the low formability of Mg alloys. In the present study, the optimization of blow forming of AZ31 alloy at the elevated temperature was investigated. Finite element simulation was carried out and verified with the blow forming experiments.

• Transactions of Materials Processing
• /
• v.19 no.7
• /
• pp.429-434
• /
• 2010

The material used is a commercial magnesium based alloy AZ31(Mg-3Al-1Zn) sheet with a thickness of 0.8 mm. Friction tests at various temperatures(R.T. to $200^{\circ}C$) and at various holding forces in the 4 type molds were carried out to investigate the coefficient of friction. A warm drawing process with a local heating and cooling technique was developed in the Mg alloy sheet forming to improve formability because it is very difficult for Mg alloy to deform at room temperature by the conventional method. So, the coefficient of friction at various mold surface treatment conditions in this study was needed to develop the Mg alloy sheet forming technology.