• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.134-138
• /
• 2000

The physical, electrical and piezoresitive characteristics of CrN(chromiun nitride) thin-films on silicon substrates have been investigated for use as strain gauges. The thin-film depositions have been carried out by DC reactive magnetron sputtering in an argon-nitrogen atmosphere(Ar-(5~25 %)$N_2$). The deposited CrN thin-films with thickness of $3500{\AA}$nd annealing conditions($300^{\circ}C$, 48 hr) in Ar-10 % $N_2$ deposition atmosphere have been selected as the ideal piezoresistive material for the strain gauges. Under optimum conditions, the CrN thin-films for the strain gauges is obtained a high electrical resistivity, $\rho=1147.65\;{\mu}{\Omega}cm$, a low temperature coefficient of resistance, TCR=-186 ppm/$^{\circ}C$ and a high temporal stability with a good longitudinal gauge factor, GF=11.17.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.04a
• /
• pp.65-66
• /
• 2008

The realization and origin of p-type ZnO are main issue for photoelectronic devices based on ZnO material. N-doped and nominally undoped p-type ZnO films were achieved on silicon (100) and homo-buffer layers by RF magnetron sputtering and post in-situ annealing. The undoped film shows high hole mobility of 1201 $cm^2V^{-1}s^{-1}$ and low resistivity of $0.0454\Omega{\cdot}cm$ with hole concentration of $1.145\times10^{17}cm^{-3}$. The photoluminescence(PL) spectra show the emissions related to FE, DAP and defects of $V_{Zn}$, $V_O$, $Zn_O$, $O_i$ and $O_{Zn}$.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.349-352
• /
• 1989

Poling piezoelectric ceramic-polymer composites with 0-3connectivity is difficult because of the high dielectric constant of most of the ferroelectric filler materials, and the high resistivity of the polymer matrix. To aid in poling this type of composite, conductivity of the polymer phase can be controlled by adding small amount of a semiconductor phase such as germanium, carbon or silicon. In this study, flexible piezoelectric composites of $PbTiO_3$ powder and Eccogel polymer were developed using small amounts of a semiconducting phase. These composites were poled rapidly at low voltages, resulting in properties superior to composites prepared without a conductive phase. The effect of addition of various conductive phase with different volume percentage on the dielectric and piezoelectric properties of the composite are discussed here.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.135-141
• /
• 2000

The physical, electrical and piezoresitive characteristics of CrN(chromiun nitride) thin-films on silicon substrates have been investigated for use as strain gauges. The thin-film depositions have been carried out by OC reactive magnetron sputtering in an argon-nitrogen atmosphere(Ar-(5~25 %)$N_2$). The deposited CrN thin-films with thickness of $3500{\AA}$ and annealing conditions($300^{\circ}C$, 48 hr) in Ar-10 % $N_2$ deposition atmosphere have been selected as the ideal piezoresistive material for the strain gauges. Under optimum conditions, the CrN thin-films for the strain gauges is obtained a high electrical resistivity, $\rho=1147.65\;{\mu}{\Omega}cm$, a low temperature coefficient of resistance, TCR=-186 ppm/$^{\circ}C$ and a high temporal stability with a good longitudinal gauge factor, GF=11.17.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.597-600
• /
• 1999

A solar cell conversion efficiency was degraded by grain boundary effect in polycrystalline silicon To reduce grain boundary effect, we performed a preferential grain boundary etching, POC$_3$ n-type emitter doping, and then ITO film growth on poly- Si. Among the various preferential etchants, Schimmel etch solution exhibited the best result having grain boundary etch depth higher than 10 ${\mu}{\textrm}{m}$. RF magnetron sputter grown ITO films showed a low resistivity of 10$^{-4}$ $\Omega$ -cm and high transmittance of 85 %. With well fabricated poly-Si solar cells, we were able to achieve as high as 15 % conversion efficiency at the input power of 20 mW/$\textrm{cm}^2$.

• Electrical & Electronic Materials
• /
• v.7 no.3
• /
• pp.206-212
• /
• 1994

In this paper, We discuss the $POCI_3$ doping process according to the variation of deposition temperature, gas flow rate and doping time. The factors acted with $POCI_3$ doping are gas flow rate deposition temperature and time etc. Among them the temperature is the most important factor. For the $POCI_3$ flow rate, it should not exceed the resistivity saturation point developed on poly surface by annealing treatment. Therefore, this study suggests the optimum conditions of Poly-silicon treatments with the $POCI_3$ flow rate.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.215-216
• /
• 2013

The silicide is a compound of Si with an electropositive component. Silicides are commonly used in silicon-based microelectronics to reduce resistivity of gate and local interconnect metallization. The popular silicide candidates, CoSi2 and TiSi2, have some limitations. TiSi2 showed line width dependent sheet resistance and has difficulty in transformation of the C49 phase to the low resistive C54. CoSi2 consumes more Si than TiSi2. Nickel silicide is a promising material to substitute for those silicide materials providing several advantages; low resistivity, lower Si consumption and lower formation temperature. Nickel silicide (NiSi) nanowire (NW) has features of a geometrically tiny size in terms of diameter and significantly long directional length, with an excellent electrical conductivity. According to these advantages, NiSi NWs have been applied to various nanoscale applications, such as interconnects [1,2], field emitters [3], and functional microscopy tips [4]. Beside its tiny geometric feature, NW can provide a large surface area at a fixed volume. This makes the material viable for photovoltaic architecture, allowing it to be used to enhance the light-active region [5]. Additionally, a recent report has suggested that an effective antireflection coating-layer can be made with by NiSi NW arrays [6]. A unique growth mechanism of nickel silicide (NiSi) nanowires (NWs) was thermodynamically investigated. The reaction between Ni and Si primarily determines NiSi phases according to the deposition condition. Optimum growth conditions were found at $375^{\circ}C$ leading long and high-density NiSi NWs. The ignition of NiSi NWs is determined by the grain size due to the nucleation limited silicide reaction. A successive Ni diffusion through a silicide layer was traced from a NW grown sample. Otherwise Ni-rich or Si-rich phase induces a film type growth. This work demonstrates specific existence of NiSi NW growth [7].

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.58-58
• /
• 1999

The diamond films which can be applied to SOD (silicon-on-diamond) structure were deposited on Si(100) substrate using CO/H2 CH4/H2 source gases by microwave plasma chemical vapor deposition(MPCVD), and SOD structure have been fabricated by poly-silicon film deposited on the diamond/Si(100) structure y low pressure chemical vapor deposition(LPCVD). The phase of the diamond film, surface morpholog, and diamond/Si(100) interface were confirmed by X-ray diffraction(XRD), scanning electron microscopy(SEM), atomic force microscopy(AFM), and Raman spectroscopy. The dielectric constant, leakage current and resistivity as a function of temperature in films are investigated by C-V and I-V characteristics and four-point probe method. The high quality diamond films without amorphous carbon and non-diamond elements were formed on a Si(100), which could be obtained by CO/H2 and CH4/H2 concentration ratio of 15.3% and 1.5%, respectively. The (111) plane of diamond films was preferentially grown on the Si(100) substrate. The grain size of the films deposited by CO/H2 are gradually increased from 26nm to 36 nm as deposition times increased. The well developed cubo-octahedron 100 structure nd triangle shape 111 are mixed together and make smooth and even film surface. The surface roughness of the diamond films deposited by under the condition of CO/H2 and CH4/H2 concentration ratio of 15.3% and 1.5% were 1.86nm and 3.7 nm, respectively, and the diamond/Si(100) interface was uniform resistivity of the films deposited by CO/H2 concentration ratio of 15.3% are obtained 5.3, 1$\times$10-9 A/cm, 1 MV/cm2, and 7.2$\times$106 $\Omega$cm, respectively. In the case of the films deposited by CH4/H2 resistivity are 5.8, 1$\times$10-9 A/cm, 1 MV/cm, and 8.5$\times$106 $\Omega$cm, respectively. In this study, it is known that the diamond films deposited by using CO/H2 gas mixture as a carbon source are better thane these of CH4/H2 one.

• The Journal of Information Technology
• /
• v.7 no.2
• /
• pp.69-76
• /
• 2004

This paper presents the results of spectral analysis about waveforms and leakage current waveforms on contaminated silicon insulators under various environment conditions.(salt fog, clean fog, rain). The larger the leakage current during 200ms, the higher the power spectrum at 60Hz. If contaminated insulators suffers from high salt density fog, the leakage current occurs with high crest value intermittently, results in the low spectrum. Analysis of leakage current data showed that this electrical activity was characterized by transient arcing behavior contaminants are deposited on the insulator surface during salt fog tests. This provides a path for the leakage current to flow along the surface of the insulator. It is important to have an indication of the pollution accumulation in order to evaluate the test performance of a particular insulator. If the drop in surface resistivity is severe enough, then the leakage current may escalate into service interrupting flashover that degrade power quality.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.10
• /
• pp.113-123
• /
• 1990

Tungsten film was deposited on the single crystal silicon wafer in a low pressure chemical vapor deposition reactor from silane and tungsten hexafluoride in the temperature range of $250-400^{\circ}C$ Deposition rate was found to be determined by the mass transfer rate of reactants from the gas phase to the safter surface. It was found out that tungsten films deposited contained about 3 atomic $\%$ of silicon and that the crystallinity and the grain size increased as the deposition temperature was increased. The resistivity of the film was measured to be in the range of $7~25{\mu}{\Omega}-cm$ and decreased with increasing deposition temperature. The adhesion of the tungsten film on a silicon surface was measured by the tape peel off test and it was improved with increasing deposition temperature. From the analysis of the gas composition, the reaction pathway to form $SiF_{4}$ and $H_{2}$ was found to be more favorable than HF formation.