• 대한기계학회논문집A
• /
• 제39권1호
• /
• pp.11-17
• /
• 2015

최근에 원자력 발전소 안전 3 등급 배관에 적용되고 있는 고밀도 폴리에틸렌 배관은 융착표면을가열한 후 축방향으로 가압하는 열 융착 공정을 이용하여 맞대기 융착되어진다. 이러한 열 융착공정은 맞대기 융착부에 비드 형상을 발생시킨다. 이러한 비드 형상의 응력집중에 기인하여 피로수명이 줄어들 수 있다. 따라서 피로거동에 미치는 맞대기 열 융착부 비드의 효과를 고찰하는 것이 필요하다. 본 연구에서는 응력 제어 조건 하의 인장 피로 시험과 유한요소 탄성응력 해석을 수행하여 맞대기 열 융착부의 인장 피로 거동을 고찰하였다. 고찰 결과, 중주기 및 고주기 피로 영역에선 피로수명에 미치는 비드의 영향이 미미한 반면 저주기 피로 영역에선 비드의 존재가 피로 수명을 감소시킴을 확인하였다.

• 한국소음진동공학회:학술대회논문집
• /
• 한국소음진동공학회 2000년도 추계학술대회논문집
• /
• pp.612-617
• /
• 2000

This paper describes the experience gained from the treatments for prevention of blade failure occurred in the low-pressure turbine. Some cracks due to high cycle fatigue were found at the blades in low-pressure turbines after long time operation. Such failure was mainly caused by the resonance of the blade with the vane passing frequency excitation. If a natural frequency of the blade exists near the excitation frequency, a resonant vibration can occur and leads to a large amount of stress which may cause fatigue failures in turbine blades. To avoid the resonance of the blade, some modifications have been performed and full-scaled mockup testing has been done to confirm the verification for modification. Test result shows that enlarging the span cover is very useful to change the natural frequency of the grouped blades effectively.

• 수산해양기술연구
• /
• 제26권4호
• /
• pp.380-386
• /
• 1990

The high stress, low cycle fatigue test were carried out on HT80 plates with artificial part-through notch. The LBB conditions by the net section stress approach was examined in detail. Finite element methods for the state of deformation were also applied and the results were compared with the results from experiments. From the test results, it was noted that the LBB condition in fatigue test was dependent upon the maximun load change before and after the crack penetration. The LBB criterion By the net section stress approach were slightly dependent on initial crack size. It was shown that the state of deformation can be used to predict whether the component is likely to show LBB condition or they will be broken rapidly.

• KEPCO Journal on Electric Power and Energy
• /
• 제4권1호
• /
• pp.19-24
• /
• 2018

가스터빈 동익에 대한 지속적인 국산화 개발이 추진되어, 국내 정밀 주조 기술을 향상시키고, 동익의 유지 보수 비용을 낮추는 등의 직간접적인 긍정적 효과를 가져왔지만, 여전히 국산화 개발품이 발전소에서 안정적인 실사용이 가능한지에 대한 우려가 존재한다. 향상된 소재와 주조기술을 바탕으로 조직학적, 기계적 성질에서 충분한 품질을 확보하였더라도, 개발품을 대상으로 다양한 신뢰성 검증이 요구되는 이유이다. 고속회전시험기는 로터, 디스크 등의 회전체에 원심력을 가하여, 이에 따른 제품의 특성을 분석하기 위한 시험장비로 일반적으로 과속도시험을 통한 최종적인 품질검사에 주로 사용된다. 본 논문에서는 전력연구원에 구축된 고속회전시험기를 활용한 가스터빈 동익에 대한 과속도시험을 포함한 저주기피로시험 사례를 중심으로 신뢰성 시험 및 평가 결과를 기술하였다.

• Nuclear Engineering and Technology
• /
• 제55권5호
• /
• pp.1616-1629
• /
• 2023

To quantify the conservatism of existing ASME strain-based evaluation methods for seismic loading, this paper presents very low cycle fatigue test data of elbows under various cyclic loading conditions and comparison of evaluation results with experimental failure cycles. For strain-based evaluation methods, the method presented in ASME BPVC CC N-900 and Sec. VIII are used. Predicted failure cycles are compared with experimental failure cycle to quantify the conservatism of evaluation methods. All methods give very conservative failure cycles. The CC N-900 method is the most conservative and prediction results are only ~0.5% of experimental data. For Sec. VIII method, the use of the option using code tensile properties gives ~3% of experimental data, and the use of the material-specific reduction of area can reduce conservatism but still gives ~15% of experimental data.

• 한국지진공학회논문집
• /
• 제27권6호
• /
• pp.275-281
• /
• 2023

The demand for high-strength steel is rising due to its economic efficiency. Low-cycle fatigue (LCF) tests have been conducted to investigate the nonlinear behaviors of high-strength steel. Accurate material models must be used to obtain reliable results on seismic performance evaluation using numerical analyses. This study uses the combined hardening model to simulate the LCF behavior of high-strength steel. However, it is challenging and complex to determine material model parameters for specific high-strength steel because a highly nonlinear equation is used in the model, and several parameters need to be resolved. This study used the particle swarm algorithm (PSO) to determine the model parameters based on the LCF test data of HSA 650 steel. It is shown that the model with parameter values selected from the PSO accurately simulates the measured LCF curves.

• 한국주조공학회지
• /
• 제14권6호
• /
• pp.541-547
• /
• 1994

The effects of weld repair on the durability in Al-10%Si-0.3%Mg castings were evaluated. The strength and fracture toughness in fusion zone were higher than those in the base metal by rapid cooling of fusion zone after welding. There were no significant differences between fatigue properties in castings and weld repaired specimen as the results of low cycle fatigue and rotating bending fatigue test. Therefore it was concluded that weld repairing did not have any significant effect on the mechanical properties of castings.

• 열처리공학회지
• /
• 제24권2호
• /
• pp.92-98
• /
• 2011

The influence of the cooling condition after solution treatment on the high temperature fatigue resistance of 23Cr-26Ni heat resistant steel was investigated. Two different cooling conditions were applied to the steel after solution treatment at $1200^{\circ}C$ for 3 hours. One specimen was water quenched immediately after the solution treatment. The other one was furnace cooled at a rate of $0.5^{\circ}C/min$ down to $750^{\circ}C$ after the solution treatment. Then, both specimens were aged at $750^{\circ}C$ for 5 hours. Under two different heat treatment conditions, the low cycle fatigue (LCF) test was performed at $600^{\circ}C$ and room temperature (RT). Only cyclic hardening continued from the beginning until fracture at all strain amplitudes during LCF at $600^{\circ}C$. This phenomenon was attributed to the increase in the dislocation density due to cyclic deformation, which resulted in the interaction between the newly created dislocations and precipitates. Cyclic hardening followed by saturation and cyclic softening was observed at RT. Cyclic softening was attributed to the dislocation annihilation rate exceeding the dislocation generation rate. Other probable factor for cyclic softening was some cavities formed around grain boundaries after 20 cycles. WQ and FC have a similar LCF behavior at RT and $600^{\circ}C$ as shown in the cyclic stress response curves.

• 대한기계학회논문집A
• /
• 제27권8호
• /
• pp.1398-1408
• /
• 2003

Tensile and LCF(low cycle fatigue) tests were carried out in air at wide temperature range 20$^{\circ}C$-750$^{\circ}C$ and strain rates of 1${\times}$10$\^$-4//s-1${\times}$10$\^$-2/ to ascertain the influence of strain rate on tensile and LCF properties of prior cold worked 316L stainless steel, especially focused on the DSA(dynamic strain aging) regime. Dynamic strain aging induced the change of tensile properties such as strength and ductility in the temperature region 250$^{\circ}C$-600$^{\circ}C$ and this temperature region well coincided with the negative strain rate sensitivity regime. Cyclic stress response at all test conditions was characterized by the initial hardening during a few cycles, followed by gradual softening until final failure. Temperature and strain rate dependence on cyclic softening behavior appears to result from the change of the cyclic plastic deformation mechanism and DSA effect. The DSA regimes between tensile and LCF loading conditions in terms of the negative strain rate sensitivity were well consistent with each other. The drastic reduction in fatigue resistance at elevated temperature was observed, and it was attributed to the effects of oxidation, creep and dynamic strain aging or interactions among them. Especially, in the DSA regime, dynamic strain aging accelerated the reduction of fatigue resistance by enhancing crack initiation and propagation.

• 열처리공학회지
• /
• 제9권1호
• /
• pp.69-77
• /
• 1996

The fatigue crack initiation behavior of plasma ion nitrided SACM645 steel was investigated through the rotary bending fatigue test and residual stress measurement by XRD. It was shown by XRD and EPMA that the plasma ion nitrided surface was composed of ${\gamma}^{\prime}(Fe_4N)$phase and ${\varepsilon}(Fe_{2-3}N)$phase, and that the nitrogen atoms existed in Fe matrix in diffusion layer. The OM, SEM and Auger spectroscopy showed that the depth of compound layer, mixed compound and diffusion layer, and diffusion layer was $8{\mu}m$, $30{\mu}m$ and $300{\mu}m$, respectively. However, the microhardness test showed that the depth of hardened layer was $500{\mu}m$. The tensile strength of the ion nitrided SACM645 was lower than that of the unnitrided SACM645, and the ion nitrided specimen was fractured without plastic deformation. The nitrided SACM645 showed much poorer low cycle fatigue properties than the unnitrided one. In rotary bending fatigue, the fatigue strength of the ion nitrided SACM645 was higher than that of the unnitrided specimen, and the fatigue crack initiation sites changed by applied fatigue stress levels. The XRD result showed that the ion nitrided SACM645 has the compressive residual stress from surface to $600{\mu}m$ deep and the tensile residual stress from $600{\mu}m$ to deeper site. It is thought that crack initiation takes place at the point where the total stress of residual stress and applied stress is maximum.