• Journal of the Korean institute of surface engineering
• /
• v.31 no.5
• /
• pp.286-296
• /
• 1998

Galvannealing is becomming the main stream of the coating technology applied to automobile outer and inner panels due to its low cost and easy application applied to automobile outer and inner panels due to its low cost and easy application in thick Zn coating, compared to electro galvanizing. Despite of filed up data with an experience in this field, galvannealing in thick Zn coating is getting more difficult because of the absence of Fe deposition in Zn coating. As a result, it exhibits, with different steel sheet and grain size there is a proper temperature range which is good for the tarket coating thickness of galvannealing. In case of 1,200mm wide and 0.77 mm thick extra low carbon steel with 20$mu extrm{m}$ grain size, its proper temperature range for galvannealing of one side 60g/$\textrm{m}^2$ is 470-$480^{\circ}C$.

• Journal of the Korean Society of Industry Convergence
• /
• v.11 no.4
• /
• pp.195-199
• /
• 2008

The carbon fiber has low x-ray absorption property and high stiffness. This is the reason why many CT(Computed Tomography) manufacturer use carbon fiber in couch tabletop for CT scanner. In this paper, we design and make the couch tabletop made of carbon fiber composite, and verify the validity in CT scanner. In designing the couch tabletop, to determine the aluminum equivalent thickness of couch tabletop, we evaluate X-ray the transmissivity of aluminum and carbon plate in 80-120kVp X-ray energy range. And we perform structural analysis and mechanical design using determined thickness of carbon sheet. In conclusion, it was evaluated that manufactured couch tabletop satisfies X-ray transmissivity and mechanical requirements in CT scanner.

• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.863-869
• /
• 2004

The purpose of this research is to investigate the mechanical property and ductile-brittle transition temperature of Ti-Nb-P added extra low carbon interstitial free steel having a tensile strength of 440 MPa. The mechanical property and transition temperature of hot rolled steel sheets were more influenced by the coiling temperature rather than by the small amount of alloying element. Further, at the same composition, the property of the specimen coiled at low temperature was superior to that obtained at higher coiling temperature. The fracture surface of 0.005C-0.2Si-1.43Mn steel coiled at $630^{\circ}C$ showed a ductile fracture mode at $-100^{\circ}C$, but coiling at $670^{\circ}C$ showed a transgranular brittle fracture mode at $-90^{\circ}C$. The galvannealed 0.006C-0.07Si-1.33Mn steel sheet annealed at $810^{\circ}C$ has tensile strength and elongation of 442.8 MPa and $36.6\%$, respectively. The transition temperature of galvannealed 0.006C-0.07Si-1.33Mn steel sheet was increased with a drawing ratio, and the transition temperature of the galvannealed 0.006C-0.07Si-1.33Mn steel was $-60^{\circ}C$ at a drawing ratio of 1.8

• Proceedings of the Korean Society of Laser Processing Conference
• /
• 2000.06a
• /
• pp.11-14
• /
• 2000

• Laser Solutions
• /
• v.4 no.3
• /
• pp.30-39
• /
• 2001

This work was tamed out to apply a laser welding technique in joining between a Zn coated low carbon steel plate(SECC) and a free cutting carbon steel shaft(SUM24L) with or without W coating. Experiments were carried out and analysed by applying the FD(factorial design)method to obtain the optimum Laser welding condition. Optical microscopy, SEM, TEM and XRD analyses were performed in order to observe the microstructures in the fusion zone and the HAZ. Mechanical properties of the welded specimens were examined by microhardness test, tensile test and twist test. There was no flawed Zn in the fusion zone by EDS analysis. This means that during the welding process, Zn gas could be eliminated by appropriate shielding gas flow rate and butt welding gap. Ni coating itself did not influence on the tensile strength and hardness. However, twist bending strength and the weld depth of the Ni-coated free cutting carbon steel were lower as compared with those of the uncoated free cutting carbon steel. It was attributed to a lower absorbance of laser beam to the shin Ni surface. According to the results of the factorial design tests, the twist bending strength of welded specimens was primarily affected by pulse width, laser power, frequency and speed.

• Korean Journal of Metals and Materials
• /
• v.47 no.6
• /
• pp.331-337
• /
• 2009

To lower the annealing temperature and the deviation of the mechanical properties of bake hardening steels, high purity steels were investigated. The steels were characterized by treating at low recrystallization temperature. It was confirmed that the strengthening originated from the solid solution of carbon and the ferrite grain refinement by fine MnS precipitates as carbon and sulfur contents increased in high purity steels. However, it was observed that there was no more increase of strength in steels containing over 40 ppm of carbon. It was considered that the excess carbon formed either the carbon cluster or the low temperature unstable carbides which had the negligible effect on the strengthening because they were reported to be highly coherent with the matrix. The carbon cluster and unstable carbides could be transformed to the stable cementite during bake hardening treatment. MnS was not observed in the high purity steel containing 5 ppm S, resulting in very coarse recrystallized grains and good ductility. As sulfur content increased, the recrystallized grain size decreased due to the formation of the fine MnS precipitates.

• Corrosion Science and Technology
• /
• v.23 no.4
• /
• pp.289-295
• /
• 2024

Zn-Mg-Al alloy hot-dip galvanized steel sheet has high corrosion resistance. Compared to conventional Zn coating with the same coating thickness, the high corrosion resistance Zn-Mg-Al coating is more corrosion-resistant. Various coating compositions are commercially produced and applied in diverse fields. However, these steel sheets typically contain up to 3 wt% magnesium. In recent years, there has been a growing demand for higher corrosion resistance in harsh corrosive environments. Therefore, variations in Mg and Al contents were investigated while evaluating primary properties and performance. As a result, we developed new alloy-coated steel with ultra-high corrosion resistance. A Zn-5 wt%Mg-Al coated steel sheet was evaluated for its corrosion resistance and various properties. As the amount of Mg added increased, the corrosion loss tended to decrease. The corrosion resistance of the coated steel sheet in a particular composition, the Zn-5 wt%Mg-Al coating sheet, was about 1.5 to 2 times higher than that of the conventional Zn-3 wt%Mg-Al coating sheet. Ultimately, this ultra-high corrosion-resistance coated steel sheet will provide a robust solution to conserve Zn resources and contribute to a low-carbon society.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.4
• /
• pp.208-218
• /
• 2006

The effects of the grain size on the magnetic properties in extra-low carbon steel after strain annealing were investigated. Two kinds of sample were prepared. One is the annealed sheet, which was annealed at $670^{\circ}C$ and $850^{\circ}C$ for various time periods after cold rolling. The other is the strain annealed sheet, which was temper rolled by 0.4% and subsequently strain annealed at the temperature ranging between $670^{\circ}C$ and $850^{\circ}C$ for various time periods. The grains after strain annealing became more coarse than those after primary annealing. The grains were coarsened due to the strain induced grain boundary migration (SIGM). It was found that the permeability tended to be increased and coercivity tended to be decreased with the increase of grain size. The optimum magnetic properties was achieved after strain annealing at $850^{\circ}C$ for 30 minites. Under this condition, the coercivity was measured to be 0.6 and the permeability was measured up to be 13000.

• Composites Research
• /
• v.33 no.5
• /
• pp.282-287
• /
• 2020

In the present study, a high-strength polyethylene terephthalate (PET) sheet was fabricated through a densification process of low melting PET fiber (LMF) combined PET sheet. During the thermal heat treatment process of the combined LMF, individual PET fiber was connected, which in turn leads to the improvement of the interfacial bonding force between the fibers. Also, the densification of the PET sheet leads to reduce macrospore density and in return could enhance the binding force between the overlapped PET networks. Consequently, the asprepared LMF-PET sheet showed about 410% improved tensile strength and the same elongation compared to before compression. Besides, the enhanced bonding force can prevent the shrinkage of the PET fiber network and exhibited excellent dimensional stability.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.4
• /
• pp.333-339
• /
• 2011

In this work, electrochemical characteristics and optical transmittance of carbon nanotubes (CNTs) counter electrodes which had different amount of CNTs in CNTs slurries were analyzed. Two-step heat treatment processes were applied to achieve well-fabricated CNTs electrode. Three sets of CNTs electrodes and dye-sensitized solar cells (DSSCs) with CNTs counter electrodes were prepared. As the amount of CNTs increased, sheet resistance of CNTs electrode decreased. CNTs electrode with low sheet resistance had low electrochemical impedance and fast redox reaction. On the other hand, in case of CNTs counter electrode with low density of CNTs, performance of the dye-sensitized solar cell was improved due to its high optical transmittance. We found that the transmittance of CNTs counter electrode influence the performance of dye-sensitized solar cells.