Using a high-rise building water piping after hydrostatic test of the reliability of the leak to be completed if the pressure is maintained until the leak is not commercially available considered. Due to the nature of high-rise buildings and the construction period will take several years from the lower levels of use of the water supply and fire fighting water pipe construction is in progress, the order of which I do most of the first pipe to the construction and more than three years. So kind of riser pipe is complete, install the valve in the basement by installing an automatic pump to maintain a constant pressure after hydrostatic test and after each floor plumbing piping is complete, the progress of the hydrostatic test without undergoing a separate branch pipe the valve is opened automatically when the number of the pressing pressure of the structure. I kind of do and keep working pressure of pipe until the completion of the construction work to keep the damage to human error when it is intended to prepare. In winter, the frost protection and an alternative to drainage water pipe is damaged or deformed, even if unaware of the finishing work to the building, the use of the damage caused by a leak in a after construction of finish work to be expected. Alternative to reduce this damage if the pressure test without fear of freezing to help maintain long-term commercial pressures may be considered.

• 폴리머
• /
• 제32권5호
• /
• pp.440-445
• /
• 2008

정수압 상태의 선형저밀도 폴리에틸렌 튜빙의 파손 메커니즘과 파손 모폴로지를 연구하였다. 비디오현미경과 주사전자현미경을 이용한 관찰 결과, 선형저밀도 폴리에틸렌 튜빙의 파손모드는 내면에서 외면으로 진전되는 크랙을 수반하는 취성파괴임을 확인하였다. 또한 산화유발시간과 적외선분광분석을 통하여, 파손된 선형저밀도 플리에틸렌 튜빙의 단면상에 열화에 의한 발열 피크와 카르보닐 피크의 증가를 관찰하였다. 열 가속에 의한 음력과 수명특성 사이의 관계를 고려한 선형저밀도 폴리에틸렌 튜빙의 가속수명시험법 및 시험장치를 개발하였다. 선형저밀도 폴리에틸렌 튜빙의 장기 정수압 상태의 수명을 예측하기 위해 아레니우스 모델과 와이블 분포를 적용한 통계학적 기법을 도입하였다. 그 결과, 사용온도 $25^{\circ}C$에서의 선형저밀도 폴리에틸렌 튜빙의 장기수명을 평가/분석하였다.

• 설비공학논문집
• /
• 제30권1호
• /
• pp.44-49
• /
• 2018

High-strength plastic water supply pipe evaluation method was evaluated in this study. Up to date, high strength water supply pipes that we install are mostly ductile cast iron pipes. Sometimes, a few PVC pipes are installed. Metal pipes have rust problem on the surface, causing serious damage to metal pipes and reducing the expected life span of water piping system. Nowadays, depending on technology development, some companies have improved properties of general PVC pipe performance with remarkable properties that exceed KS and ASTM standard. Here, we suggest a new method of performance evaluation for high-strength water plastic pipes.

• 폴리머
• /
• 제33권5호
• /
• pp.446-451
• /
• 2009

신뢰성 평가 시험법인 RS M 0042에 따라, 열화시간 경과에 따른 선형저밀도 폴리에틸렌 파이프의 신뢰성 평가를 수행하였다. 열화시간이 증가함에 따라, 인장강도는 250일 열화시점까지 비례적으로 증가하였고, 경도는 비교적 미소한 증가를 보였으며, 연신율은 점진적으로 감소하는 경향을 보였다. 이러한 결과는 열화시간이 증가함에 따른, 결정화도의 증가와 열산화에 의한 가교밀도의 증가, 사슬 전단 및 사슬 운동성의 감소 등에 기인한 것으로 판단된다. 장기정수압시험 결과는 초기의 연성파괴에서 차후 취성파괴로 전환되는 시점이 존재함을 확인하였다. 산화유도시간 측정은 선형저밀도폴리에틸렌 파이프의 열산화 정도를 관찰하기 위해 도입되었다. 측정 결과는 250일 이후 선형저밀도폴리에틸렌 파이프에 첨가된 산화방지제가 거의 고갈되었음을 보여준다. $100^{\circ}C$ 열화 조건에서 산화방지제의 잔존량을 계산할 수 있는 실험식을 열화시간의 함수로 표현하여 제안하였다. 적외선분광분석 결과는 열화된 선형저밀도폴리에틸렌 파이프 표면상에 카르보닐 및 하드록실 관능기가 증가하였음을 보여준다. 이는 선형저밀도폴리에틸렌 표면의 탄화수소 그룹의 산화가 국부적으로 발생하였음을 나타낸다.