• Journal of the Korea Safety Management & Science
• /
• v.16 no.2
• /
• pp.211-216
• /
• 2014

Using a high-rise building water piping after hydrostatic test of the reliability of the leak to be completed if the pressure is maintained until the leak is not commercially available considered. Due to the nature of high-rise buildings and the construction period will take several years from the lower levels of use of the water supply and fire fighting water pipe construction is in progress, the order of which I do most of the first pipe to the construction and more than three years. So kind of riser pipe is complete, install the valve in the basement by installing an automatic pump to maintain a constant pressure after hydrostatic test and after each floor plumbing piping is complete, the progress of the hydrostatic test without undergoing a separate branch pipe the valve is opened automatically when the number of the pressing pressure of the structure. I kind of do and keep working pressure of pipe until the completion of the construction work to keep the damage to human error when it is intended to prepare. In winter, the frost protection and an alternative to drainage water pipe is damaged or deformed, even if unaware of the finishing work to the building, the use of the damage caused by a leak in a after construction of finish work to be expected. Alternative to reduce this damage if the pressure test without fear of freezing to help maintain long-term commercial pressures may be considered.

• Polymer(Korea)
• /
• v.32 no.5
• /
• pp.440-445
• /
• 2008

The failure mechanism and failure morphology of linear low density polyethylene (LLDPE) tubing under hydrostatic pressure were investigated. Microscopic observations using video microscope and scanning electron microscope indicate that the failure mode is a brittle fracture including cracks propagated from inner wall to outer wall. In addition, oxidation induction time and Fourier transform infrared spectroscopy results show the presence of exothermic peak and the increase in carbonyl index on the surface of fractured LLDPE tubing, due to thermal-degradation. An accelerated life test methodology and testing system for LLDPE tubing are developed using the relationship between stresses and life characteristics by means of thermal acceleration. Statistical approaches using the Arrhenius model and Weibull distribution are implemented to estimate the long-term life time of LLDPE tubing under hydrostatic pressure. Consequently, the long-term life time of LLDPE tubing at the operating temperature of $25^{\circ}C$ could be predicted and also be analyzed.

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.30 no.1
• /
• pp.44-49
• /
• 2018

High-strength plastic water supply pipe evaluation method was evaluated in this study. Up to date, high strength water supply pipes that we install are mostly ductile cast iron pipes. Sometimes, a few PVC pipes are installed. Metal pipes have rust problem on the surface, causing serious damage to metal pipes and reducing the expected life span of water piping system. Nowadays, depending on technology development, some companies have improved properties of general PVC pipe performance with remarkable properties that exceed KS and ASTM standard. Here, we suggest a new method of performance evaluation for high-strength water plastic pipes.

• Polymer(Korea)
• /
• v.33 no.5
• /
• pp.446-451
• /
• 2009

Reliability evaluations of linear low density polyethylene (LLDPE) pipe with respect of thermal exposure time have been investigated in accordance with RS M 0042, which is a reliability standard for polymer pipe. As the thermal exposure time is prolonged, a progressive increase, until 250 days, in tensile strength and a slight increase in hardness are observed, while a proportional decrease in elongation at break is showed. These results can be explained by the increase of crystallinity, followed by the increase of crosslinking density, chain scission and the decrease in chain mobility, due to thermal oxidation as the exposure time increases. Long term hydrostatic pressure test result implies the existence of transition point from ductile to brittle fracture. Oxidation induction time (OIT) test is employed to monitor the thermo-oxidative degradation of LLDPE pipe. This result shows that after the exposure time is 250 days, the depletion of antioxidants added in LLDPE pipe occurs. An empirical equation as function of exposure time, under $100^{\circ}C$ thermal-degradation condition, is proposed to assess the remaining amount of antioxidants owing to thermo-oxidative degradation. Fourier transform infrared spectroscopy results show the increase of carbonyl (-C=O) and hydroxyl (O-H) function groups on the surface of thermally exposed LLDPE pipe. This result suggests that the hydrocarbon groups locally undergo the oxidation on the LLDPE surface due to thermal-degradation.