• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.428-434
• /
• 2008

The purpose of this study was to compare the microtensile bond strength in Class I cavities associated with different light curing modes of same light energy density. Occlusal enamel was removed to expose a flat dentin surface and twenty box-shaped Class I cavities were prepared in dentin. Single Bond (3M Dental product) was applied and Z 250 was inserted using bulk technique. The composite was light-cured using one of four techniques, pulse delay (PD group), soft-start (SS group), pulse cure (PC group) and standard continuous cure (CC group). The light-curing unit capable of adjusting time and intensity (VIP, Bisco Dental product) was selected and the light energy density for all curing modes was fixed at $16J/cm^2$. After storage for 24 hours, specimens were sectioned into beams with a rectangular cross-sectional area of approximately $1mm^2$ Microtensile bond strength $({\mu}TBS)$ test was per- formed using a univel·sal testing machine (EZ Test, Shimadzu Co.). The results were analyzed using oneway ANOVA and Tukey's test at significance level 0.05. The ${\mu}TBS$ of PD group and SS group was higher than that of PC group and CC group. Within the limitations of this in vitro study, modification of curing modes such as pulse delay and soft start polymerization can improve resin/dentin bond strength in Class I cavities by controlling polymerization velocity of composite resin.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.32 no.3
• /
• pp.184-193
• /
• 2016

Purpose: To evaluate marginal leakage of bulk fill flowable composite resin filling with different curing time by using microcomputed tomography technology. Materials and Methods: 30 previously extracted human molars were randomly divided into 6 groups based upon restorative system and different curing time. Class II cavities (vertical slot cavities) were prepared. An individual metallic matrix was used to build up the proximal wall. The SonicFill or SureFil SDR flow was inserted into the preparation by using 1 bulk increment, followed by light polymerization for different curing times. The different exposure times were 20, 40, and 60 seconds. All specimens were submitted to 5,000 thermal cycles for artificial aging. Micro-CT scanning was performed by using SkyScan 1272. One evaluator assessed microleakage of silver nitrated solution at the resin-dentin interface. The 3D image of each leakage around the restoration was reconstructed with CT-Analyser V.1.14.4. The leakage was analyzed with the Mann-Whitney test. Results: Significant differences were observed between the light curing times, but no significant differences were found between the bulk fill composite resins. Increasing in the photoactivation time resulted in greater microleakage in all the experimental groups. Those subjected to 60 seconds of light curing showed higher microleakage means than those exposed for 20 seconds and 40 seconds. Conclusion: Increasing the photoactivation time is factor that may increase marginal microlekage of the bulk fill composite resins. Further, micro-CT can nondestructively detect leakage around the resin composite restoration in three dimensions.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.1
• /
• pp.102-109
• /
• 2003

The purpose of this study was to evaluate the linear polymerization shrinkage(%) and microhardness of composite resin(Z-100, 3M, USA) according to 2-step light curing method. Conventional light curing unit(Curing Light 2500, 3M USA) and 2-step light curing unit(Elipar Highlight, ESPE, Germany) were used as light source. The strain gauge method was used for determination of polymerization shrinkage(%). Samples were divided by 3 groups according to light curing methods (Group I : $450mW/cm^2$, 40sec, Group II : $650mW/cm^2$, 40sec, Group III : $150mW/cm^2$, 10sec & $650mW/cm^2$, 30sec). Preparations of acrylic molds were followed by filling and curing. Strain gauges attached to each sample were connected to a strainmeter. Measurements were recorded at each second for the total of 10 minutes including the periods of light application. And microhardness of each group after 24hours from light irradiation were measured. Obtained data were analyzed statistically using Ore-way ANOVA and/or Scheffe test. The results of the present study can be summarized as follows: 1. Composite resin in acrylic molds showed the initial expansion at the early phase of polymerization. This was followed by the contraction with the rapid increase in volume during the first 60 seconds and gradually diminished as curing process continued. 2. The lowest linear polymerization shrinkage(%) was found in group III followed by group I, II during the measuring periods. 3. Group III using 2-step curing method showed statistically significant reduction of linear polymerization shrinkage(%) compared with group I, II at 1 minute and 10 minutes from light irradiation(p<0.05). 4. The microhardness values of each group not revealed significant difference.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.26 no.3
• /
• pp.479-485
• /
• 1999

Materials for posterior teeth includes amalgam, gold inlay and composite resin inlay. Amalgam and gold inlay have unsatisfyine esthetics. And because they simply obturate the cavity preparation, they do not strengthen the remaining tooth structure. Posterior composite resin has become established in recent years. However, its polymerization shrinkage and insufficient wear resistance were the most undesirable characteristic. The physical and mechanical properties of the composite resin inlay are further improved through heat treatment in an oven. The major part of polymerization contraction of the resin inlay takes place be fore cementation, and possible gap formation is only due to shrinkage of the thin layer of resin cement. With the semidirect technique, the inlay material is placed directly in the prepared tooth, and the primary polymerization is made by light activation with a handhold curing unit. Additional curing may take place extraorally with use of different curing ovens. It provides the patient with the benefits of luted restorations without the procedure of indirect lab-made inlay. I report three successfully treated cases by semidirect resin inlay technique. Entire clinical steps are described in detail with some discussions on the outcome.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.4
• /
• pp.479-484
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of additional acid etching and curing mechanism (light-curing or self-curing) of a composite resin on the dentin bond strength and compatibility of one-step self-etching adhesives. MATERIALS AND METHODS. Sixteen human permanent molars were randomly divided into eight groups according to the adhesives used (All-Bond Universal: ABU, Clearfil S3 Bond: CS3), additional acid etching (additional acid etching performed: EO, no additional acid etching performed: EX), and composite resins (Filtek Z-250: Z250, Clearfil FII New Bond: CFNB). Group 1: ABU-EO-Z250, Group 2: ABU-EO-CFNB, Group 3: ABU-EX-Z250, Group 4: ABU-EX-CFNB, Group 5: CS3-EO-Z250, Group 6: CS3-EO-CFNB, Group 7: CS3-EX-Z250, Group 8: CS3-EX-CFNB. After bonding procedures, composite resins were built up on dentin surfaces. After 24-hour water storage, the teeth were sectioned to make 10 specimens for each group. The microtensile bond strength test was performed using a microtensile testing machine. The failure mode of the fractured specimens was examined by means of an optical microscope at ${\times}20$ magnification. The data was analyzed using a one-way ANOVA and Scheffe's post-hoc test (${\alpha}$=.05). RESULTS. Additional etching groups showed significantly higher values than the no additional etching group when using All-Bond Universal. The light-cured composite resin groups showed significantly higher values than the self-cured composite resin groups in the Clearfil S3 Bond. CONCLUSION. The additional acid etching is beneficial for the dentin bond strength when using low acidic one-step self-etch adhesives, and low acidic one-step self-etch adhesives are compatible with self-cured composite resin. The acidity of the one-step self-etch adhesives is an influencing factor in terms of the dentin bonding strength and incompatibility with a self-cured composite resin.

• Journal of dental hygiene science
• /
• v.21 no.3
• /
• pp.178-184
• /
• 2021

Background: As the importance of the esthetic function of teeth increases, the use of esthetic restoration materials and whitening treatment are increasing. The purpose of this study was to investigate the color change of esthetic restoration materials upon using staining and whitening toothpaste. Methods: Light curing (LC) packable composite resin, LC flowable resin, LC glass ionomer (GI), and self-curing GI specimens were colored in coffee or curry for three hours a day for seven days. After that, regular toothpaste, whitening toothpaste containing hydrogen peroxide, and whitening toothpaste containing activated charcoal were applied for three minutes three times a day for two weeks. Luminosity (L), chromaticity a (a), and chromaticity b (b) were measured using a spectrophotometer once a week. Results: In the coffee-colored group, the change in L^2*a^2*b² (E²) with time was significant (p=0.004), there was no difference for different toothpaste types (p=0.646), and there was significant difference (p<0.001) for different esthetic restorative materials. The change of E² in the curry-colored group was significant only for different esthetic restorative materials (p<0.001). In the coffee-colored group, the L, a, and b values of the light-curing GI showed greater change than other materials after staining and one week after whitening, turning dark, red, and yellow. In the curry-colored group, L did not differ for different materials and times, and a and b showed the greatest difference in light-curing GI after staining and one and two weeks after whitening. Conclusion: The use of whitening toothpaste for two weeks was not different from the use of general toothpaste in the removal of staining or whitening. Since light-curing GI is the most vulnerable to coloration, it is recommended that coloring by food chromogen should be explained in advance, before using light-curing GI for teeth restoration.

• Restorative Dentistry and Endodontics
• /
• v.27 no.1
• /
• pp.87-94
• /
• 2002

The purpose of this study was to evaluate the color changes of composite resin polymerized with three type of light curing units. Composite resin (Z100, shade A2) were applied in a cylindrical metal mold(2 mm thick, 7 mm diameter). Twenty specimens according to light curing units were made. Group 1 : the specimens were polymerized with Apollo 95E for 3seconds(1370 mW/$\textrm{cm}^2$). Group 2 : the specimens were polymerized with XL 3000 for 40seconds (480 mW/$\textrm{cm}^2$). Group 3 : the specimens were polymerized with Spectrum 800 for 10 seconds(250 mW/$\textrm{cm}^2$) and 30 seconds(700 mW/$\textrm{cm}^2$). The microhardness values(VHN) of upper and lower surfaces specimens after light polymerization were measured for the degree of polymerization. All specimens were stored in distilled water at 6$0^{\circ}C$ for 30 days. The color characteristics(L$^*$, a$^*$, b$^*$) of the specimens before and after immersion were measured by spectrophotometer and the total color difference ($\Delta$E$^*$) was computed. The results obtained were as follows : 1. The microhardness values of Group I showed significantly lower than those of Group II and III (p<0.05). 2. In all groups the $\Delta$E$^*$ values presented below 2.0. 3 Group I showed the highest $\Delta$E$^*$ values followed order from highest to lowest by Group II and III (p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.21 no.2
• /
• pp.652-663
• /
• 1996

The purpose of this study was to evaluate the tensile bond strength to tooth structure of composite resin and glass ionomer cement according to filling methods and light curing units. In this study, two class V cavities were prepared on the buccal surface of each tooth of 140 extracted human molars, and they were randomly assigned into 3 experimental groups with 40 teeth and control group with 20 teeth. And then, each experimental groups subdivided into 2 groups(A,B) according to light curing units. The cavities of each group were filled with the CLEARFIL FII self curing resin(Control Group), Z-100 light curing resin(Group 1), Vitremer$^{TM}$ light curing glass ionomer cement(Group 2) and Z-100 light curing resin over the Vitrebond$^{TM}$ liner(Group 3). And subdivided A Group used Argon Laser(SPECTRUM$^{TM}$, U.S.A.), B Group used XL 1,000 curing light (3M, U.S.A.). The specimens underwent temperature changed from $5^{\circ}C$ to $55^{\circ}C$ five hundred times. After thermocycling, specimens were stored in 100% relative humidity at $37^{\circ}C$ for 24 hours. And then, the tensile bond strength of specimens were calculated with Universal Testing Machine(AGS-100A, Japan). The results were as follows : 1. Among the experimental groups, the group 2-B showed the highest tensile bond strength ($18.89{\pm}7.80$) and the group 1-A showed the lowest tensile bond strength ($11.68{\pm}2.28$). There was significant difference between group 2-B and group 1-A(p<0.01). 2. Between the light curing units, the XL 1,000 unit showed higher tensile bond strength ($16.63{\pm}3.20$) than that of the Argon Laser unit ($13.73{\pm}2.30$). There was significant difference between XL 1,000 and Argon Laser(p<0.01). 3. About filling methods and materials, the group 2 showed the highest tensile bond strength ($17.56{\pm}1.89$) and the group 1 showed the lowest tensile bond strength($13.03{\pm}1.90$). There was significant difference between group 2 and group 1,3(p<0.01). In conclusion, the results showed that the glass-ionomer cement that cured by XL 1,000 light curing unit demonstrated significantly higher tensile bond strength than other curing unit and filling methods.

• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.353-358
• /
• 2010

Objectives: The purpose of this study was to measure the power density of light curing units transmitted through resin inlays fabricated with direct composite (Filtek Z350, Filtek Supreme XT) and indirect composite (Sinfony). Materials and Methods: A3 shade of Z350, A3B and A3E shades of Supreme XT, and A3, E3, and T1 shades of Sinfony were used to fabricate the resin inlays in 1.5 mm thickness. The power density of a halogen light curing unit (Optilux 360) and an LED light curing unit (Elipar S10) through the fabricated resin inlays was measured with a hand held dental radiometer (Cure Rite). To investigate the effect of each composite layer consisting the resin inlays on light transmission, resin specimens of each shade were fabricated in 0.5 mm thickness and power density was measured through the resin specimens. Results: The power density through the resin inlays was lowest with the Z350 A3, followed by Supreme XT A3B and A3E. The power density was highest with Sinfony A3, E3, and T1 (p < 0.05). The power density through 0.5 mm thick resin specimens was lowest with dentin shades, Sinfony A3, Z350 A3, Supreme XT A3B, followed by enamel shades, Supreme XT A3E and Sinfony E3. The power density was highest with translucent shade, Sinfony T1 (p < 0.05). Conclusions: Using indirect lab composites with dentin, enamel, and translucent shades rather than direct composites with one or two shades could be advantageous in transmitting curing lights through resin inlays.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.2
• /
• pp.221-232
• /
• 2006

The purpose of this study was to investigate the effect of step-curing mode on polymerization shrinkage and contraction of composite resin restoration. Class I cavities were prepared on the extracted human premolars. The cavities were ailed with Filtek $Z-250^{TM}$ (hybrid resin, 3M ESPE, USA) and Filtek $flow^{TM}$ (flowable resin, 3M ESPE, USA) and cured with one of the following irradiation modes; Halogen 40sec with continuous curing, LED 10sec with continuous curing, and LED 13sec with step-curing. Contraction stress was measured with strain gauge which was connected to TML $Datalogger^{TM}$ (TDS-102, SOKKI, Japan) and resin-dentin interfaces were observed by scanning electron microscope. The results of present study can be summarized as follows : 1. Composite resin restoration showed transient expansion just after irradiation of curing light. Contraction stress was increased rapidly at the early phase of polymerization and reduced slowly as time elapsed (P<0.05) 2. $Filtek\;flow^{TM}$ showed lower contraction stress than Filtek $Z-250^{TM}$ regardless of curing modes. 3. LED step-curing mode showed lowest contraction stress in Filtek $Z-250^{TM}$ compared with other curing modes(P<0.05). 4. LED step-curing mode showed lowest contraction stress in $Filtek\;flow^{TM}$ compared with other curing modes(P<0.05), but difference in contraction stress was not so greate as in $Filtek\;Z-250^{TM}$. 5. Polymerization of composite resin by LED light with step-curing mode and halogen light with continuous ode resulted in better marginal sealing than LED light with continuous mode.