• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_{2}$(0 ${\times}$ 0.14) oxides have been synthesized by hydrothermal treatment of $(Co_{x}Mn_{1-x})_{3}O_{4}$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}-NaMnO_{2}$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_{2}$, comparing to orthorhombic $LiMnO_2$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_2$ (0 x 0.14) oxides have been synthesized by hydrothermal treatment of ($Co_{x}Mn_{1-x}$)$_3O_4$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}$-$NaMnO_2$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_2$, comparing to orthorhombic $LiMnO_2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.12
• /
• pp.1320-1325
• /
• 2004

In this study, in order to develop the low temperature sintering ceramics for multilayer piezoelectric transformer, PCW-PMN-PZT ceramics added with Li$_2$CO$_3$, Bi$_2$O$_3$ and CuO as sintering aids were manufactured, and their microstructural, dielectric and piezoelectric properties were investigated. When the only CuO was added, specimens could not be sintered below 98$0^{\circ}C$. However, when Li$_2$CO$_3$ and Bi$_2$O$_3$ were added, specimens could be sintered below 98$0^{\circ}C$. Li$_2$CO$_3$ and Bi$_2$O$_3$ addition were proved to lower sintering temperature of piezoelectric ceramics due to the effect of Li$_2$O-Bi$_2$O$_3$ liquid phase. Li$_2$CO$_3$ and Bi$_2$O$_3$ added specimens showed higher piezoelectric properties than those of the only CuO added specimens. At 0.2 wt% Li$_2$CO$_3$ and 0.3 wt% Bi$_2$O$_3$ added specimen sintered at 92$0^{\circ}C$, the dielectric constant of 1457, electromechanical coupling factor of 0.56 and mechanical quality factor of 1000 were shown, respectively. These values are suitable for multilayer piezoelectric transformer application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.12
• /
• pp.1034-1038
• /
• 2007

In order to develop the composition ceramics capable of being sintered at low temperature with high piezoelectric properties for multilayer piezoelectric actuator application, PZW-PMN-PZT system ceramics were manufactured according to sintering aid $Li_2CO_3$ addition and their microstructural, dielectric and piezoelectric properties were investigated. The crystal structure of the specimens showed a perovskite phase and no pyrochlore or other second phase was detected. At the sintering temperature of $900\;^{\circ}C,\;0.2\;wt%Li_2CO_3$ added specimen showed a optimum values of kp = 0.562, $d_{33}\;=\;360\;pC/N$ and Qm = 1184, respectively.

• Journal of the Korean Ceramic Society
• /
• v.45 no.3
• /
• pp.167-171
• /
• 2008

Zirconium-doped $Li_{1.1}Co_{1-x}Zr_xO_2(0{\leq}x{\leq}0.05)$ powders as cathode materials for lithium ion batteries were synthesized using an ultrasonic spray pyrolysis method. Cyclic voltammetry and cyclic stability tests were performed, and the changes of microstructure were observed. The solubility limit of zirconium into $Li_{1.1}CoO_2$ was less than 5 mol%, and monoclinic $Li_2ZrO_3$ phase was formed above the limit. The Zr-doping suppressed the grain growth and increased the lattice parameters of the hexagonal $LiCoO_2$ phase. The Zr-dopiong of 1mol% resulted in the best cyclic performance in the range of $3.0{\sim}4.3V$ at 1C rate (140 mA/g); the initial discharge capacity decreased from 158 mAh/g to 60 mAh/g in the undoped powder, while from 154 mAh/g to 135 mAh/g in the Zr-doped powder of 1 mol% after 30 cycles. The excellent cycle stability of Zr-doped powder was due to the low polarization during chargedischarge processes which resulted from the delayed collapse of the crystal structure of the active materials with Zr-doping.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 2003.11a
• /
• pp.75-78
• /
• 2003

• Journal of the Korean Electrochemical Society
• /
• v.2 no.2
• /
• pp.88-92
• /
• 1999

The apparent density. self-separation of the electrode composite from current collector in the electrolyte solution and specific resistance of electronic conduction of the electrode composite were examined by the variation of content of conductive material such as graphitic and black carbons in $LiCoO_2$ composite electrode for lithium ion battery. Increasing the content of conductive material, the apparent density of Lico02 composite electrode was decreased and that of $LiCoO_2$ in composite electrode was only rapidly decreased compared to that of composite. $LiCoO_2$ composite electrodes containing more than 4.1 weight percent of super s black as a conductive material were seU-separated by the immersion into 1 mol/I $LiPF_6$ in propylene carbonate and diethyl carbonate (1:1 volume ratio). Specific resistances related to the electronic conduction of composite electrode were decreased by the increasing the content i)f conductive material. Specific resistance of the composite electrode including $2\~3\%w/w$ of super s black as conductive material was similar to that of $12\%w/w$ of Lonza KS6. In the range of this study, super s black as conductive material is better than Lonza KS6 on battery capacity because of apparent density of $LiCoO_2$ in electrode composite including super s black is higher than that of Lonza KS6.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.5
• /
• pp.421-424
• /
• 2007

Thermal behavior of $Li_{1-x}CoO_2$ has been investigated employing DSC (Differential Scanning calorimetry) and TGA (Thermogravimetry Analyzer), and the crystal parameters were calculated from XRD (X-ray diffraction).for the commercial rectangular pouch cell(1000 mAh).The cathode materials coated over aluminium foil current collector is made up of a blend consisting of active material $LiCoO_2$(size $20\;{\mu}m$, 94 wt%), conducting material super p black (SPB, 3 wt%) and binder polyvinylidene fluoride (PVDF, 3 wt%). The anode is a mix consisting of carbon (92 wt%) and PVDF(8 wt%) coated over copper foil. The cells for the experiments were first preconditioned by cycling three times and stabilized at OCV=3.0, 3.5, 4.2, 4.35 and 4.5 V. The stabilized cathode material was used for thermal and crystal parameter investigations.

• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.312-316
• /
• 2005

Adsorption characteristics of $CO_2$ on activated carbons were evaluated using dynamic adsorption method in a fixed bed with acid treatment, LiOH impregnation and water vapor supply. Physical and chemical properties of the activated carbons were measured using SEM, EDS, nitrogen adsorption, FTIR and XRD. Nitric acid treatment led to the decrease in BET surface area and the increase in oxygen content of virgin activated carbon, and it produced a new functional group that included nitrogen. For the reduction of BET surface area by LiOH impregnation, the nitric acid treated activated carbon (NAC) was less than the virgin activated carbon (AC). Large particles of LiOH were present on the carbon surface when the content of LiOH was over 2 wt%. The adsorbed amount of $CO_2$ on activated carbon in a fixed bed increased with the acid treatment, LiOH impregnation and water vapor supply. The XRD results indicated that LiOH was converted to $Li_2CO_3$ after the adsorption of $CO_2$ on LiOH precursor.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.413-413
• /
• 2011

최근 전기, 전자, 반도체 산업의 발전으로 전 고상 박막리튬전지는 초소형, 초경량의 마이크로 소자의 구현을 위한 고밀도 에너지원으로 각광받고 있다. 현재 양극박막은 대부분LCO(LiCoO2)계열이 이용되고 있으나, 코발트는 높은 가격과 인체 유해성 뿐만 아니라 상대적으로 낮은 용량(~140 mAh/g)등의 단점을 갖고 있어 향후 보다 고용량의 양극박막이 요구된다. 3원계 양극활물질 LiMO2(M=Co,Ni,Mn,etc.)은 우수한 충방전 효율 과 열적 안정성 뿐 아니라 277mAh/g의 높은 이론용량을 갖고 있어 고용량 양극박막으로의 적용시 고용량 박막이차전지 제작이 가능하다. 본 연구에서는 전 고상 박막 전지의 구현을 위하여 RF 스퍼터링법을 사용하여 Li[Li0.2Mn0.54Co0.13Ni0.13]O2 박막을 증착하였다. Li/MnCoNi의 몰 비율을 변화시켜 높은 전기화학적 특성을 갖는 분말을 합성하여 제조한 타겟으로 Pt/TiO2/SiO2/Si 기판위에 RF 스퍼터법을 이용하여 박막을 성장시켰다. 박막 증착 시 가스의 비율은 Ar:O2=3:1로 하고 증착 압력의 조절(0.005~0.02 torr)을 통하여 박막의 두께와 표면 특성을 조절하며 성장시켰다. 또한 박막을 다양한 온도에서($400{\sim}550^{\circ}C$) 열처리하여 결정화도와 전기화학적 특성을 측정하였다. 증착 된 박막의 구조적 특성은 X-ray diffraction(XRD) 과 scanning electron microscopy(SEM)로 관찰되었다. 박막의 전기화학적 특성 평가를 위하여 Cyclic voltammatry를 측정하여 가역성의 정도를 확인하고 WBC3000 battery cycler를 이용한 half-cell 테스트를 통하여 박막의 용량을 평가하였다.