• Journal of the Korean Society of Clothing and Textiles
• /
• v.13 no.3 s.31
• /
• pp.259-267
• /
• 1989

In this paper, the fabric specimen undergoes repeated laundering under given condition. After this cyclic laundering was applied, the crease recoveries of the specimen were measured using shirley crease revovery tester in order to evaluate the effect of factors at given condition during crease deformation. 5 samples of grey plain cloth were desized, alkali-scoured, bleached, whased with water, and air-dried. All tests were made on samples preconditioned to $65\%\;RH\;and\;20^{\circ}C$. The experimental results were analysed statistically to relate crease recoveries and the properties of smaples, recovery periods (time) of crease. Furthermore, the crease recoveries of core-spun yarn woven fabrics were discussed in comparison with those values for $100\%$ combed cotton yarn woven fabric and $65\%$ polyester $35\%$ carded cotton blended yarn woven fabric. The results obtained are as follows; 1. Regardless of materials, remarkable decrease are observed in crease recoveries about 1-5 cycles of the repeated laundering, but slack decrease are observed in crease recoveries after 5 cycle of the re-peated laundering. 2. Crease recoveries ($\alpha$) of core-spun yarn woven fabrics are relate to recovery periods (t) of crease as follows; log$\alpha$=0.01415 log t+2.1168 ($r^2=0.94$) 3. Core-spun yarn woven fabrics were superior to $100\%$ combed cotton yarn woven fabrics and $65\%$ polyester $35\%$ carded cotton blended yarn woven fabric in crease recoveries. 4. Crease recoveries ($\alpha$) of core-spun yarn woven fabrics are relate to cover factor (CF), thickness (T) at pressure 0.5 $gf/cm^2$, weight (W) as follows; log$\alpha$=-0.3482 log CF-0.4924 log T-0.4727 W+2.4243 ($r^2=0.88$) 5. Crease recoveries ($\alpha$) of core-spun yarn woven fabrics are relate to 2HB/B, 2HB/W, $\sqrt[3]{B/W}$, WC/T which are concerning to formation of weared clothes and bending Iran formation behavior as follows: log $\alpha$=0.0091 2HB/B+0.4667 2HB/W+0.0185 $\sqrt[3]{B/W}$+0.0114 WC/T+1.8433 ($r^2=0.86$)

• Journal of the Korean Society of Costume
• /
• v.49
• /
• pp.73-84
• /
• 1999

The purpose of this study was to investigate dyeing properties of silk and wool fabric by Cassia tora extracts according to the conditions such as extraction(temperature time) dyeing(temperature time) condition kinds of mordants temperature of mordanting. The color fastness of laundering irradiation were examined. The results were as follows: The wavelength of maximum absorpthion by extracts appeared at 201, 277, 382nm in UV-Vis spectrum. Absorbance of extracts were increased with temperature and time. The extraction efficiency of Cassia tora was determined as $95^\circ{C}$ of extraction temperature 120 minutes of extraction time. Silk fabric had highest K/S value when dyeing for 90min at $40^\circ{C}$. Wool fabric had highest K/S value when dyeing for 60min at $80^\circ{C}$. Surface color of silk and wool fabric dyed with Cassia tora extracts was 3,9Y and 0.4Y but it was changed from 9.3YR to 7,4Y and from 9.4YR to 5Y by mordants. The fabrics of mordanted by metal ion dyed the depth of color. Laundering and irradiation fastness of mordanted fabrics were improved as compared with nonmordanted fabrics.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.25 no.3
• /
• pp.569-576
• /
• 2001

The purpose of this study is to develop multifunctional fibers by sticking cinnamon microcapsules on cotton knit. The prepolymer was made from urea-formaldehyde for usage of wall materials of microcapsules. The parameters for adoptable condition are 5000rpm of agitation speed, 1% of dispersions concentration according to the observation with SEM and particle analyzer. The Antimicrobial activity of cotton knit treated with capsule was increased greatly and maintained on the laundering cycle.

• The Journal of Natural Sciences
• /
• v.11 no.1
• /
• pp.159-164
• /
• 1999

The study was investigated to the effect of antimicrobial finishing of towel treated by organic antimicrobial agent. It was measured for the optimal condition such as treated time, treated concentration and temperature. After amtimicrobial treatment, mechanical and fastness properties, anti-laundering property were measured.The antimicrobial activity of samples was analyzed quantitatively by masureing the number of colonies of Staphylococcus aureus using the shake flask method. Towel samples treated with the optimal condition such as treated time of 10 minute, and treated temperature of $30^{\circ}C$, concentration of organic antimicrobial agent of 3.5% were shown a high reduction rate in the number of colonies grown and clear zones of inhibition.The effect of reduction rate for laundering until the number of 20 times was shown high reduction rate of over 80%. And the mechanical properties of samples treated with organic antimicrobial agent were not changed approximately.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.6 no.1
• /
• pp.9-15
• /
• 1982

The influence of builders on calcium deposition on the fabric was studied by laundering the cotton fabric with sodium carbonate, sodium metasilicate, sodium tripolyphosphate and built detergents in hard water. The laundry variables were: 1) Washing cycles: 5, 10, 20, 30 and 40 cycles. 2) Water hardness: 100 ppm, 150 ppm, 200 ppm and 300 ppm. 3) Builders: $Na_2\;CO_3,\;Na_2\;SiO_3$ and STPP. 4) Detergents: Na-DBS, $Na-DBS+Na_2CO_3,\;Na-DBS+Na_2\;SiO_3,\;Na-DBS+STPP,\;Na-DBS+Na_2\;CO_3+STPP$, and $Na-DBS+Na_2\;SiO_3+STPP$. The fabric was washed for 15 minutes at 23+$1^{\circ}C$ in a washing machine(Gold Star WP 3007) under the similar condition with those of home laundering, and rinsed 3 times in the same water hardness for 5 minutes. The calcium deposits on the fabric was determined by EDTA-BACK titration methods. The results of this study were as follows: 1) The amount of calcium deposits on the fabric was increased with increasing wash cycles. This deposit was due to the build up of insoluble calcium carbonate. 2) As the water hardness increased, the amount of calcium deposits on the fabric was increased. 3) Alkaline builders, such as, $Na_2CO_3$ and $Na_2SiO_3$, promoted calcium deposition on the fabric, however STPP prevented calcium deposition on the fabric. 4) Fabric laundered with $Na-DBS+Na_2CO_3$ showed the highest calcium deposits on the fabric, and decreased with the order of $Na_2CO_3$, $Na-DBS+Na_2SiO_3$, and Na-DBS. And fabrics washed with phosphate-built detergents showed a small amount of calcium deposition.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.12 no.1 s.26
• /
• pp.69-80
• /
• 1988

In this study, we have compared the relative importance of various washing condition affecting on soil release for P/C blended fabrics. P/C blended fabrics were soiled by the pad-dry method with aqueous and oily soil. The washing procedures of soiled samples were performed by Atlas Launder-Ometer with 27 wash conditions which are combinations of wash temp. wash time and detergent cone. The degree of soil-release was evaluated with CIE 1976 Lab color difference before and after washing. Multiple regression analysis was used to evaluate the optimum wash conditions and the relative importance of the factors providing maximum soilremoval.

• Textile Coloration and Finishing
• /
• v.2 no.4
• /
• pp.251-256
• /
• 1990

Bis-(p-bromopheny)phosphate(BBPP) , which serves as flame retardant for PET fabric, was synthesized from phenol and phosphorus oxychloride, and from bromine. In order to investigate the flame retardancy of BBPP, PET fabrics were steam-cured with diluted BBPP solution. The following conclusions were drawn : 1. Flame retardancy of PET fabrics treated with BBPP was excellent, and optimal treating condition was 10% concentration of flame retardant at $170^{\circ]C$ 2. Clark softness and tensile strength before and after the laundering of PET fabrics treated with flame retardant remained nearly unchanged.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.8 no.2
• /
• pp.19-25
• /
• 1984

The experiment was undertaken to investigate the optimum condition in the effect of seam balance on seam puckering. Four kinds of fabrics were sewed with three kinds of yarns which were used with a seam balance of 90, 100, 110 and $120\%$. In this experiment, the following conclusions were obtained; The best appearance was achieved by a seam balance of $100\~120\%$ in Cotton fabrics, $100\~110\%$ in Rayon fabrics, $110\~120\%$ in Polyester fabrics and $120\%$ in Wool fabrics after laundering.

• Textile Coloration and Finishing
• /
• v.10 no.6
• /
• pp.49-54
• /
• 1998

The antimicrobial activities of the copolymer of N,N'-dimethyl-N,N'-diallyl ammonium chloride (DMDAAC) and acrylamide(AA) were investigated. A series of copolymers with various ratios of DMDAAC and AA were prepared by free radical initiation via an intra-intermolecular propagation mechanism, ie, cyclopolymerization, and the antimicrobial activities of the prepared copolymers were measured by minimum inhibitory concentration(MIC) test. The copolymers were, then, methylolated under basic condition for reactivity with hydroxyl group of cellulose. Both antimicrobial activity and fastness to laundering of the cotton fabrics finished using the methylolated copolymers were evaluated. From the results it was shown that the copolymers with different ratios of DMDAAC and AA have MIC values in the range of 1∼100ppm. As the ratio of AA in the copolymers increases, the anitmicrobial activity decreases. The fastness of the cotton fabric finished by the methyolated copolymers to 10 repeated launderings in anionic commercial detergent is good enough to show colony reduction above 90％ regardless of DMDAAC and AA ratios.

• Textile Coloration and Finishing
• /
• v.16 no.2
• /
• pp.8-14
• /
• 2004

The purpose of this study was to investigate dyeing properties and antibacterial activities of cotton and silk fabrics treated with Ginkgo biloba leaf extracted with three kinds of aqueous solvents: distilled water, electrolytic reduction water and electrolytic oxidation water. The optimum dyeing condition of Ginkgo biloba leaf was 120 min at 8$0^{\circ}C$. Electrolytic reduction water had the highest dyeability to both cotton and silk compared with electrolytic oxidation water and distilled water. A color of extract by distilled water and electrolytic oxidation water showed yellowish Yellow Red, extract by electrolytic reduction water showed reddish Yellow Red. Irrespective of kinds of extraction solvents, appropriate acidity of medium was pH 9∼11 and pH 3 for cotton and silk fabrics, respectively. Colorfastness to laundering and Light fastness showed generally low but crocking fastness was excellent. Antibacterial activities of the treated fabrics above were 99.9%.