Scandia ($Sc2O_3$)-stabilized zirconia (ScSZ) electrolyte-supported symmetrical solid oxide electrolyzer cells (SOECs), in which lanthanum strontium cobalt ferrite (LSCF)-gadolinia ($Gd_2O_3$)-doped ceria (GDC) composite materials are used as both the cathode and anode, were fabricated and their high temperature steam electrolysis (HTSE) performance was investigated. Current density-voltage curves were obtained for cells operated in 10% $H_2O$/90% Ar at 750, 800, and $850^{\circ}C$. It was possible to determine the ohmic, cathodic, and anodic contributions to the total overpotential using the three-electrode technique. The HTSE performance was significantly improved in the symmetrical cell with LSCF-GDC electrodes compared to the cell consisting of an Ni-YSZ cathode and LSCF-GDC anode. It was found that the overpotential due to the LSCF-GDC cathode largely decreased and, at a given current density, the total cell voltage decreased, which resulted in the enhanced hydrogen production rate in the symmetrical cell.

• Korean Chemical Engineering Research
• /
• 제48권2호
• /
• pp.172-177
• /
• 2010

본 논문에서는 SOFC 금속연결재로서 Crofer22APU를 적용하고자 표면에 전도성 산화막($La_{0.8}Sr_{0.2}CoO_3$)을 습식코팅 후, SOFC 작동환경에서 산화거동, 전기적 특성변화 및 미세구조 변화를 관찰하였다. 코팅 전 샌드블러스트 장치를 이용한 Crofer22APU 표면처리를 통하여 코팅막/금속의 접합특성을 개선시킬 수 있었으며, 320 mesh의 입자크기를 갖는 알루미나 분말을 이용하여 표면처리한 경우 접착특성이 극대화되었다.$La_{0.8}Sr_{0.2}CoO_3$ 코팅된 시편의 전기적 특성 평가는 4-wire 법을 이용하여 SOFC 작동환경에서 약 4,000 시간 장기성능 평가하였으며 $12mW{\cdot}cm^2$의 낮은 면저항값을 얻을 수 있었다. 실험종료 후 미세구조 분석결과에서도 전도성 산화막($La_{0.8}Sr_{0.2}CoO_3$) 코팅이 금속의 부식으로 인한 산화층의 생성속도를 늦추고 이로 인한 금속의 전기적 특성이 감소하는 것을 방지하는데 유효함을 확인하였다.