• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 1996.11a
• /
• pp.45-52
• /
• 1996

The goal is to assess the effect of fatigue loading on mechanical properties of Fiberite 934/T300 laminates of pressure vessel using the recent variational mechanics analysis. This analysis has been useful in providing fracture mechanics interpretation of matrix microcracking in cross-ply laminates. This paper describes using the new energy release rate analysis for a fracture mechanics based interpretation of microcrack formation during fatigue loading. The master plot by modified Paris-law gives a complete characterization of a material system's resistance to microcrack formation.

• Advanced Composite Materials
• /
• v.16 no.3
• /
• pp.223-244
• /
• 2007

This study experimentally and numerically investigated the tensile damage progress in stitched laminates. In particular, it focused on the effects of stitching on the damage progress. First, we experimentally confirmed that ply cracks and delamination appeared under load regardless of stitching. We then performed damage-extension simulation for stitched laminates using a layer-wise finite element model with stitch threads as beam elements, in which the damage (ply cracks and delamination) was represented by cohesive elements. A detailed comparison between observation and the simulated results confirmed that stitching had little effect on the onset and accumulation of ply cracks. Furthermore, we demonstrated that the stitch threads significantly suppressed the extension of the delamination.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.10a
• /
• pp.150-153
• /
• 2003

Longitudinal strains({$varepsilon}_x$) of the core and skin layers in glass fiber reinforced plastic(GFRP) cross-ply composite laminates have been studied using the embedded optical fiber sensor of totally-reflected extrinsic Fabry-Perot interferometer(TR-EFPI). Foil-type strain gauges bonded on both the upper and lower surfaces were used for the measurement of the surface strains. Both TR-EFPI sensor and strain gauge bonded on the specimen surface showed excellent agreement within -0.0086 ~ +0.0302% strain. It was shown that values of {$varepsilon}_x$ in the interior of the surface layer and the core layer measured by embedded TR-EFPI sensor was significantly higher than that of the specimen surface measured by strain gauges. The experimental results were ascertained with finite element analysis. Embedded TR-EFPI optical fiber sensor could measure accurately the internal strains which were different from the surface.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.10a
• /
• pp.158-162
• /
• 2003

The PVDF(polyvinylidene fluoride) film sensor as one of smart sensors has good characteristics to detect the impact damages of composite structures. The capabilities of the PVDF film sensor for evaluating impact behaviors and damages of Gr/Ep laminates subjected to low-velocity impact were examined. From sensor signals, the specific wave-forms implying the damage were detected. The wavelet transform(WT) and Short Time Fourier Transform(STFT) were used to decompose the piezoelectric sensor signals in this study. The impact behaviors of Gr/Ep laminates were simulated and the impact forces were reconstructed using the sensor signals. Finally, the impact damages were predicted by finite element analysis with the reconstructed forces. For experimental verification, a series of low-velocity impact tests from low energy to damage-induced energy were carried-out. The extent of damage in each case was examined by means of ultrasonic C-scan and the measured damage areas were agreed well with the predicted areas by the F.E.A.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.6
• /
• pp.1535-1541
• /
• 1994

The void content of carbon fiber reinforced composite laminates was determined by the ultrasonic nondestructive technique. The ultrasonic immersion, through-transmission method developed stresses the utilization of spectral analysis and frequency dependence of the attenuation due to porosity. The measured attenuation shows approximately linear behavior over the frequency range investigated. The linear relationship between the void content and the attenuation slop (d $\alpha$/df) is found to hold, but the constant of proportionality is quite different for samples with different pore morphology. The void volume fraction determined by the attenuation slope agreed very well with that obtained by the acid digestion analysis.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.278-285
• /
• 2001

Aluminum/Aramid Fiber Reinforced Plastic(Al/AFRP) laminates are applied to the fuselage-wing intersection. The main objective of this study was to evaluate the delamination zone behavior of Al/AFRP with a saw-cut and circular hole using average stress criterion and the effect of notch geometry. Mechanical tests were carried out to determine the cyclic-bending moment and delamination zone observed ultrasonic C-scan pictures. In case of Al/AFRP containing saw-cut specimen, the shape and size of the delamination zone formed along the fatigue crack. However, in case of Al/AFRP containing circular hole specimen, the shape and size of delamination zone formed two types. first type, delamination zone formed along the fatigue crack. Second type, not observed fatigue crack. Therefore, delamination zone was formed dependently of the circular hole shape.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.4
• /
• pp.21-27
• /
• 1998

In the case of existing in free-edge delaminations of composite laminates which are symmetry with respect to mid-plane in laminates also, in the case of asymmetry and anti-symmetry, the generalized quasi-three dimensional displacement field equations developed from quasi-three dimensional displacement field equations can be applied to solve above cases. We introduce three paramenters in this paper, which have not been used in quasi-three dimensional displacement field equations until now. To the laminate subjected to the axial extension strain $\varepsilon$0(C1) in $\chi$-direction, the bending deformation $\chi$$\chi$(C$_2$) around у-direction, the bending deformation w$\chi$(C$_4$) around z-direction and the twisting deformation $\chi$$\chi$y(C$_3$) around $\chi$-direction .The generalized quasi-three dimensional displacement field equations are able to be analyzed efectively.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.773-776
• /
• 1997

This paper presents an investigation of the energy absorption of composite laminates during ballistic impact. Three components are responsible for the absorption of energy-the tensile failure of fiber, the elastic deformation of the composite, the delamination of composite laminates. The ballistic limit, V/sub 0/, of the laminates is determined using a previous model implemented to determine the energy absorption of the three components listed above. The size of the deformed zone during impact was estimated by an approximate solution for impacts on plates. The carbon/epoxy plates were examined for this research.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.11
• /
• pp.2853-2865
• /
• 2000

During the curing process of thick glass/epoxy laminates, a substantial amount of temperature lag and overshoot at the center of the laminates is usually experienced due to the large thickness and low thermal conductivity of the glass/epoxy composites. Also, it takes a longer time for full and uniform consolidation. In this work, temperature, degree of cure and consolidation of a 20 mm thick unidirectional glass/epoxy laminate were investigated using an experiment and a 3-dimentional numerical analysis. From the experimental and numerical results, it was found that the experimentally obtained temperature profile agreed well with the numerical one, and the cure cycle recommended by the prepreg manufacturer should be modified to prevent a temperature overshoot and to obtain full consolidation.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.5 s.176
• /
• pp.1084-1092
• /
• 2000

Responses of ultrasonic back scattered energy and AE (Acoustic Emission) characteristics related to the progressive damage of $[0/90-{2}]_s$ and $[0/90-{4}]_s$ crossply laminates were studied. It was found that the ultrasonic backscattered energy was sensitive to the matrix cracking but not sensitive to other failure mechanisms. However, AE was proved to be sensitive to matrix cracking as well as other failure mechanisms.AE signals were analyzed by investigating the amplitude and number of counts per event for corresponding applied strain. Loading and unloading tests were conducted separately. AE results showed Kaiser effect in the crossply composite laminates and ultrasonic results supported the AE results.