Schizandra fruit (Schizandra chinensis fructus) were dried by three processes, $50^{\circ}C$ (50HAD), $70^{\circ}C$ hot air (70HAD) and freeze drying process (FRD). Terpenoid were collected by SDE(Simultaneous Steam Distillation-Extraction) and followed by GC-MSD analysis. Also colour profile of each dried samples were measured by Hunter colorimeter. From fresh schizandra fruit, were detected 15 kinds of monoterpene, 28 kinds of sesquiterpene and 7 kinds of terpene alcohol. Myrcene(56.97 ${\mu}g/g$) and ${\gamma}$-terpinene(58.49 ${\mu}g/g$) were the major monoterpenes, ${\beta}$-elemene(120.16 ${\mu}g/g$), ${\alpha}$-bergamotene (103.45 ${\mu}g/g$), ${\gamma}$-selinene (75.97 ${\mu}g/g$), ${\beta}$-cubebene(66.69 ${\mu}g/g$), aristolene (51.25 ${\mu}g/g$) and ${\alpha}$-ylangene(28.06 ${\mu}g/g$) were the sesquiterpenes, and T-muurolol (96.45 ${\mu}g/g$) and terpinen-4-ol(46.02 ${\mu}g/g$) were the terpene alcohols. The dried samples lost more than half of terpenoid content of fresh schizandra fruit during early stage of drying process, and then the level of terpenoid content was not significantly changed. The content of sesquiterpenes appeared to increase until 6 day of FRD. The amount of residual terpene alcohols contained in schizandra fruit dried by FRD was more than those remained after drying by other processes, and schizandra fruit dried by 70HAD exhibited the least residual terpene alcohols. Brightness parameter $L^{\ast}$ decreased with the rise in the level of drying temperature, to which redness parameter $a^{\ast}$ and yellowness $b^{\ast}$ appeared to be similar.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.4
• /
• pp.158-163
• /
• 2011

$CuInS_2$ thin films were prepared using a sol-gel spin-coating method. That makes large scale substrate coating, simple equipment, easy composition control available. The structural and optical properties of $CuInS_2$ thin films that include less toxic materials (S) instead of Se, tetragonal chalcopyrite structure. Copper acetate monohydrate ($Cu(CH_3COO)_2{\cdot}H2O$) and indium acetate ($In(CH_3COO)_3$) were dissolved into 2-propanol and l-propanol, respectively. The two solutions were mixed into a starting solution. The solution was dropped onto glass substrate, rotated at 3000 rpm, and dried at $300^{\circ}C$ for Cu-In as-grown films. The as-grown films were sulfurized inside a graphite container box and chalcopyrite phase of $CuInS_2$ was observed. To determine the optical properties measured optical transmittance of visible light region (380~770 nm) were less than 30 % in the overall. The XRD pattern shows that main peak was observed at Cu/In ratio 1.0 and its orientation was (112). As annealing temperature increases, the intensity of (112) plane increases. The unit cell constant are a = 5.5032 and c = 11.1064 $\AA$, and this was well matched with JCPDS card. The optical transmittance of visible region was below than 30 %.