• 한국도로학회논문집
• /
• 제14권5호
• /
• pp.93-99
• /
• 2012

PURPOSES: The purpose of this study is to compare the alkali-silica reactivity for mortar bar and concrete prism specimens using crushed aggregates of 5 types in Korea. And the alkali-silica reactivity for those aggregates are measured by chemical test method. METHODS: The alkali-silica reactivity for those aggregates was measured by chemical test method of KS F 2545, mortar-bar test of KS F 2546, accelerated mortar-bar test method of ASTM C 1260 and concrete prism test method of ASTM C 1293, relatively. RESULTS: The alkali-silica reactivity for those aggregates was verified by chemical test of KS F 2546 and accelerated mortar-bar test of ASTM C 1260. However, it was not by mortar-bar test of KS F 2546 and concrete prism test of ASTM C 1293. CONCLUSIONS: The above results showed that relationship among the four test methods were very low. The results from 3 types of test methods using cement-aggregate combinations appeared to be different. Because the environmental conditions of test methods for measuring the alkali-silica reactivity such as equivalent alkali content(external source), humidity, temperature, and times were different though the aggregates were same. Moreover, alkali-silica reactivity showed the biggest impact when alkalis were supplied form outside and exposed to environmental conditions. The accelerated mortar-bar test method seems to be most appropriate test method for concrete structures exposed to alkali environment.

• 한국도로학회논문집
• /
• 제13권3호
• /
• pp.1-6
• /
• 2011

국내에서는 콘크리트 포장용 굵은 골재를 대상으로 화학적인 시험방법과 모르타르 봉 시험방법을 이용한 결과 알칼리-실리카 반응 유해 가능성이 낮은 것으로 알려져 왔으나, 최근에 알칼리 - 실리카 반응에 의한 파손이 발생되었고, ASTM C 1260을 이용한 결과 일부 골재에서 유해한 팽창이 발생된다고 보고되었다. 따라서 본 논문에서는 모르타르 봉 시험방법인 KS F 2546과 ASTM C 1260을 이용하여 길이 팽창 유도기간의 환경조건이 알칼리 - 실리카 팽창 반응 특성에 미치는 영향을 평가하고자 하였다. KS F 2546의 경우 대상 골재 모두 반응성 없음으로 판정되었으나 ASTM C 1260에서는 일부 골재에서 잠재반응성 이상으로 판정되었다. 이는 외부로부터의 알칼리 이온의 공급, 온도 및 습도 차이에 의하여 발생한 것으로 판단된다. 또한 ASTM C 1260에서 NaOH의 농도변화 실험을 통하여 NaOH의 농도가 증가할수록 길이팽창이 현저하게 증가한다는 것을 확인하였으며, 온도 및 습도가 증가함에 따라 길이팽창이 증가한다는 것을 확인하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2009년도 춘계 학술대회 제21권1호
• /
• pp.255-256
• /
• 2009

본 연구는 광물성 혼화재를 이용하여 알칼리-골재 반응성 저감 효과를 평가하는 것으로 국내 골재를 대상으로 KS F 2545(화학적 방법), KS F 2546(모르타르 봉 시험 방법), ASTM C 1260(촉진 모르타르 봉 시험방법)을 이용하여 알칼리-골재 반응성 저감 효과를 측정하였다.

• 콘크리트학회지
• /
• 제6권2호
• /
• pp.108-117
• /
• 1994

국내에서는 아직 알칼리-골재 반응으로 인한 피해가 보고되지는 않았지만, 해사와 쇄석의 사용이 증가하고 있어 이에 대한 연구가 시급히 진행되어야 할 것으로 사료되어, 화학법(KS F 2545, ASTMC 289)과 모르터바법(KS F 2546, ASTM C 227)을 중심으로 실험을 행하여 국내산 쇄석1종과 국외산 쇄석 1종이 유해로 판정되었으며, 첨가알칼리성량 및 종류를 달리하여 실시한 모르터바법 시험결과 첨가 알카리로 NaCl사용시 가장 높은 팽창을 하였다. 또한, 모르터바의 표면 및 내부의 반응생성물을 SEM에 의한 관찰과 EDXA에 의한 성분분석을 실시하여 알칼리와 실리카성분으로 이루어진 알칼리 실리케이트 겔임이 판명되어 국내에서 알칼리 반응성을 나타내는 골재의 존재가 처음으로 확인되었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.98-101
• /
• 2003

The Alkali-Aggregate Reaction (AAR) may cause a serious failure in the concrete structures. Several researchers in some nations have performed the continuous studies to prevent failure of a concrete structures by the AAR distress as well as the studies to manifest the mechanism. The ASTM Standards to prevent failure by potential AAR aggregates were established in 1950. The KS F2545 and KS F 2546 were established to test the susceptibility of aggregate to potential AAR in 1982. But the researches on the AAR have not been performed affluently in Korea because the distress due to AAR has seldom been reported officially. In this study, the Chemical Method and Scanning Electron Microscopy (SEM) were used to verifying the cause of the pattern crack on the surface and internal crack in the plain concrete pavement. It can be concluded that the distress of a specific site in plain concrete pavement was mainly due to AAR, and the chemical method and SEM may be the effective tools for verifying the cause of AAR distresses.

• 콘크리트학회논문집
• /
• 제13권1호
• /
• pp.54-61
• /
• 2001

천연자원 보존의 일환으로서 폐타이어, 폐플라스틱 재료 등에 대한 재활용 연구가 활발히 진행되고 있다. 따라서 본 연구의 목적은 폐유리를 시멘트 대체재료로서 개발하기 위한 것이다. 이를 위하여, 먼저 보통강도 및 고강도 콘크리트 각각에 대해서 폐유리 분말의 혼입률을 변화시킨 콘크리트를 제조한 다음 그것의 압축강도 시험을 통하여 폐유리 분말의 최적 혼입률을 도출하였다. 또한, 최적 혼입률에 의하여 제작된 보통강도 및 고강도 콘크리트 각각에 대해서 압축, 인장 및 휨강도와 탄성적 성질 등 역학적 특성을 구명하였다. 한편, 시멘트 속의 알칼리와 폐유리 속에 다량 함유된 실리카 성분은 서로 반응하려는 경향이 있기 때문에, 현재 모프타르봉 시험 방법(KS F 2546)에 의한 알칼리.실리카 반응 시험을 진행하고 있다. 본 실험연구 결과로부터 폐유리 분말을 혼입한 콘크리트는 실리카흄 콘크리트보다 작업성은 다소 우수하며, 강도특성은 유사한 것으로 나타나, 폐유리 분말에 대해서 경제적이고 환경친화적인 콘크리트 혼화재로서의 가능성을 입증하였다.

• 지질공학
• /
• 제5권2호
• /
• pp.193-200
• /
• 1995

광물과 암석으로 구성된 골재와 이를 둘러싼 시멘트 페이스트 사이에 알카리-골재반응이 콘크리트 구조물에 팽창을 일으킨다는 사실은 잘 알려져 있다. 그러한 팽창은 구조물에 심각한 손상을 야기시키기 때문에 많은 나라에서는 구조물에 사용된 동일한 골재와 시메트로 공시체를 제작하고 실험실에서 이의 팽창 촉진 실험을 통하여 팽창선의 상한선을 규정하고 있는데 이는 0.1%이다. 위 실험의 규정은 미국의 경우 ASTM C227과 490에, 우리나라의 경우 한국공업표준협회에서 발간한 KS핸드북 F2503, F2546 및 L5107에 명시되어 있다. 양자의 내용은 거의 동일하다. 이 규정에 따라 실험용 공시체를 제작하고 팽창정도를 측정하는데 위에 소개한 규정은 현장에서 현실적으로는 적합하계으나 연구의 목적으로 정밀한 실험을 위해서는 아래와 같은 문제점이 발견된다. 첫째, 골재, 시메트 및 물의 배합비를 규정함에 있어서 골재를 무게로 표현한 점. 들째, 팽창률계산에 있어서 분모의 값을 254mm로 고정시킨 점. 셋째, 골재의종류에 관계없이 초기길이 측정시기를 24$\pm$2시간 후로 통일시킨 점. 네째, 골재의 비중측정 방법은 목적에 따라 선택되어야 하나 그 중에서 진비중에 의한 측정이 가장 정밀도가 높다.