• Journal of the Korean Magnetics Society
• /
• v.19 no.5
• /
• pp.180-185
• /
• 2009

Fe$_3$O$_4$ particles, prepared by a sol-gel method, were examined for their structural characteristic, particle shapes and sizes, and their magnetic properties. Two different chemical compositions (using a mol rate Fe$^{2+}$/Fe$^{3+}$ = 1/2 and only Fe$^{2+}$) and 2-methoxyethanol were used for making proper solutions. And the solutions were refluxed and dry in a dry oven and the samples were fired at 200$\sim$600$^{\circ}C$ in the N$_2$ atmosphere. The formation of single-phased spinel ferrite powders was identified with the X-ray diffraction measurement as they were fired at above 250$^{\circ}C$. The result of scanning electron microscopy measurement showed the increase of annealing temperature yielded the particle size increased. The magnetic transition was observed using the Mossbaur spectroscopy measurement. As the ferrite, prepared with the chemical composition (Fe$^{2+}$/Fe$^{3+}$ = 1/2), was fired at 250$^{\circ}C$, 78% of the ferrite had a ferrimagnetic property and 22% of the ferrite was non-magnetic. In case of preparing the sample with only Fe$^{2+}$ and annealed at 200$^{\circ}C$, it had a single phased spinel structure but its particle size was too small to be ferrimagnetic. The annealing temperature above 250$^{\circ}C$ made powders a spinel structure regardless of the preparation method. They had a typical soft magnetic property and their saturation magnetization and coercivity became larger as the annealing temperature increased.

• Journal of the Korean Magnetics Society
• /
• v.18 no.2
• /
• pp.67-70
• /
• 2008

$Tb_2Bi_1Ga_xFe_{5-x}O_{12}$(x=0, 1) fabricated by sol-gel and vacuum sealed annealing process. $Tb_2Bi_1Ga_xFe_{5-x}O_{12}$(x=0, 1) have been studied by x-ray diffraction(XRD), vibrating sample magnetometer, and $M\ddot{o}ssbauer$ spectroscopy. The crystal structures were found to be a cubic garnet structure with space group Ia3d. The determined lattice constants $a_0$ of x = 0, and 1 are $12.497\AA$, and $12.465\AA$, respectively. The distribution of gallium and iron in $Tb_2Bi_1Ga_xFe_{5-x}O_{12}$ is studied by Rietveld refinement. Based on Rietveld refinement results, the terbium and bismuth ions occupy the 24c site, iron ions occupy the 24d, l6a site, and nonmagmetic gallium ions occupy the 16a site. In order to verify the magnetic site occupancy of iron and gallium, we have taken $M\ddot{o}ssbauer$ spectra for $Tb_2Bi_1Ga_xFe_{5-x}O_{12}$(x=0, 1) at room temperature. From the results of $M\ddot{o}ssbauer$ spectra analysis, the absorption area ratios of Fe ions for $Tb_2Bi_1Fe_5O_{12}$ on 24d and 16a sites are 60.8 % and 39.2 %, respectively, and the absorption area ratios of Fe ions for $Tb_2Bi_1Fe_5O_{12}$ on 24d and 16a sites are 74.7 % and 25.3 %, respectively. It is noticeable that all of the nonmagnetic Ga atoms occupy the 16a site by vacuum annealing process.

• Journal of the Korean Magnetics Society
• /
• v.14 no.1
• /
• pp.46-50
• /
• 2004

Compounds of $Y_{3-x}Ce_{x}Fe{5}O_{12}$(x=0.0, 0.1, 0.2, and 0.3) were prepared using the sol-gel method. The XRD measurements show that these samples have only a single phase of the garnet structure regardless of the amount of Ce substitution. The lattice constants of x = 0.0 and x = 0.3 were found to be a$_0$ = 12.3758 ${\pm}$0.0005 ${\AA}$ and 12.4062 ${\pm}$0.0005 ${\AA}$, respectively. The lattice constant increases linearly with increasing Ce concentration. The saturation magnetization was not changed flirty, with increasing Ce concentration, but coercivity decreased form 18.3 Oe to 5.8 Oe as x increased form x = 0.0 to x = 0.1. Mossbauer spectra of $Y_{3-x}Ce_{x}Fe{5}O_{12}$ were measured at various absorber temperatures from 13 K to Neel temperature. The Mossbauer spectra were fitted by least-squares technique with two subpatterns of Fe sites in the structure and corresponding to the 16a and 24d site. The temperature dependence of the magnetic hyperfine field in $^{57}$/Fe nuclei at the tetrahedral 240 and octahedral 16a sites were analyzed based on the Neel theory of ferrirnagnetism. The result of the Debye temperatures indicated that the inter-atomic binding force for the 24d site was larger than that for the 16a site.

• Journal of the Korean Magnetics Society
• /
• v.13 no.2
• /
• pp.53-58
• /
• 2003

Annealing effects of exchange bias fields ($H_{2ex}$(top), $H_{lex}$ (bottom)) on composite type NiFe/[FeMn/Mn]$_{80}$/NiFe multilayers have been studied. Three samples with ultra-thin Mn inserted layers on glass/Ta(50 $\AA$)/NiFe(150 $\AA$)/[F $e_{53}$M $n_{47}$(1.25 $\AA$)/Mn(0 $\AA$, 0.11 $\AA$, 0.3 $\AA$)]$_{80}$/NiFe(90 $\AA$)/Ta(50 $\AA$) were prepared by ion beam sputtering. The average x-ray diffraction peak ratios NiFe(111) of FeMn (111) fcc textures for the Mn inserted total thicknesses of 0 $\AA$, 9 $\AA$, and 24 $\AA$ were about 0.65, 0.90, and 1.5, respectively. For the sample without Mn inserted layer, the $H_{2ex}$ of 260 Oe up to 300 $^{\circ}C$ disappeared at 350 $^{\circ}C$. For two multilayer samples with ultra-thin Mn layers of 0.11 $\AA$ and 0.3 $\AA$, the $H_{2exs}$ of 310 Oe and 180 Oe up to 300 $^{\circ}C$ endured of 215 Oe and 180 Oe at 350 $^{\circ}C$, respectively. The $H_{ex}$ (bottom)s of three samples decreased from 100 Oe to 70 Oe up to 250 $^{\circ}C$, while these values increased beyond 300 $^{\circ}C$. This observation can be attributed to less diffusive path of Mn atoms in bottom NiFe than top NiFe layer. The top and bottom coercive fields slightly varied about 5 Oe∼10 Oe. From these results, we could obtain the enhancement of exchange coupling intensity and thermal stability by an ultra-thin Mn inserted layer on NiFe/[FeMn/Mn]$_{80}$/NiFe Multilayers.

• Journal of the Korean Magnetics Society
• /
• v.14 no.1
• /
• pp.38-44
• /
• 2004

The iron doped colossal magnetoresistance materials with La-Ba-Mn-O perovskites structure have been synthesized by chemical reaction of sol-gel methods. Their crystallographic and magnetic properties have been studied with x-ray diffraction, VSM, RBS, Mossbauer spectroscopy, and magnetoresistance measurements. The crystal structure of the La$\_$0.67/Ba$\_$0.33/Mn$\_$0.99/Fe$\_$0.01/ $O_3$ at room temperature was determined to be orthorhombic of Pnma. The lattice parameters a$\_$0/ and c$\_$0/ increased gradually, but b$\_$0/ deceased with increase of iron substitution. The magnetization and coercivity deceased, also the Curie temperature decreased from 360 K as x increased from 0.00 to 0.05. Magnetoresistence measurements were carried out, and the maximum MR ($\Delta$$\rho$/$\rho$(0)) was observed at 281 K, about 9.5 % in 10 kOe. The temperature of maximum resistance (R$\_$MAX/) decreased with increasing substitution of Fe ions and a semiconductor-metal transition temperature (T$\_$SC-M/) decreased too. This phenomena show that ferromagnetic transition temperature decreased by substituting Fe for Mn ions, it decreases double exchange interaction. This result accords with magnetic structure of neutron diffraction. Mossbauer spectra of La$\_$0.67/Ba$\_$0.33/Mn$\_$0.99/Fe$\_$0.01/ $O_3$were taken at various temperatures ranging from 15 to 350 K. With lowering temperature of the sample, two magnetic phases were increased and finally it showed the two sharp sextets of spectra at 15 K. The isomer shift at all temperature range is about 0.3 mm/s relative to Fe metal, which means that both Fe ions are Fe$\^$3+/ states.Fe$\^$3+/ states.

• Journal of the Korean Magnetics Society
• /
• v.26 no.4
• /
• pp.124-128
• /
• 2016

We have investigated the electronic structures of intermetallic multilayer (ML) films of [$Co(2{\AA})/Pd(x{\AA})$] (x: the thickness of the Pd sublayer; x = $1{\AA}$, $3{\AA}$, $5{\AA}$, $7{\AA}$, $9{\AA}$) by employing soft X-ray absorption spectroscopy (XAS) and soft X-ray magnetic circular dichroism (XMCD). Both Co 2p XAS and XMCD spectra are found to be similar to one another, as well as to those of Co metal, providing evidence for the metallic bonding of Co ions in [Co/Pd] ML films. By analyzing the measured Co 2p XMCD spectra, we have determined the orbital magnetic moments and the spin magnetic moments of Co ions in [$Co(2{\AA})/Pd(x{\AA})$] ML films. Based on this analysis, we have found that the orbital magnetic moments are enhanced greatly when x increases from $1{\AA}$ to $3{\AA}$, and then do not change much for $x{\geq}3{\AA}$. This finding suggests that the interface spin-orbit coupling plays an important role in determining the perpendicular magnetic anisotropy in [Co/Pd] ML films.

• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.81-85
• /
• 2007

MnTe layers of high crystalline quality were successfully grown on Si(100) : B and Si(111) substrates by molecular beam epitaxy (MBE). Under tellurium-rich condition and the substrate temperature around $400^{\circ}C$, a layer thickness of $700{\AA}$ could be easily obtained with the growth rate of $1.1 {\AA}/s$. We investigated the structural, magnetic and transport properties of MnTe layers by using x-ray diffraction (XRD), superconducting quantum interference device (SQUID) magnetometry, and physical properties measurement system (PPMS). Characterization of MnTe layers on Si(100) : B and Si(111) substrates by XRD revealed a hexagonal structure of polycrystals with lattice parameters, ${\alpha}=4.143{\pm}0.001{\AA}\;and\;c=6.707{\pm}0.001{\AA}$. Investigation of magnetic and transport properties of MnTe films showed anomalies unlike antiferromagnetic powder MnTe. The temperature dependence of the magnetization data taken in zero-field-tooling (ZFC) and field-cooling (FC) conditions indicates three magnetic transitions at around 21, 49, and 210 K as well as the great irreversibility between ZFC and FC magnetization in the films. These anomalies are attributable to a magnetic-elastic coupling in the films. Magnetization measurements indicate ferromagnetic behaviour with hysteresis loops at 5 and 300 K for MnTe polycrystalline film. The coercivity ($H_c$) values at 5 and 300 K are 55 and 44 Oe, respectively. In electro-transport measurements, the temperature dependence of resistivity revealed a noticeable semiconducting behaviours and showed conduction via Mott variable range hopping at low temperatures.

• Journal of the Korean Magnetics Society
• /
• v.26 no.5
• /
• pp.173-178
• /
• 2016

This study is to evaluate the effect of a Contrast Media (CM) on dose calculations and clinical significance in Radiation (Electromagnetic wave) Therapy (RT) plans for head & neck (H&N) and prostate cancer. Pinnacle 8.0 system was used to measure the change of Electron Density (ED) of the tissue for CM. To determine the effect of dose calculation due to CM, we did the RT planning for 30 patients. To compare the ED and dose calculations of RT plans, 3D CRT and IMRT plans were do with pinnacle and Tomotherapy planning system. Mean difference of ED between enhanced and unenhanced CT was less than 4%: H&N Target Volume (TV) 2.1%, parotid 1.9%, SMG 3.6%, tongue 0.9%, spinal cord 0.3%, esophagus 2.6%, mandible 0.1% and prostate TV 0.7%, lymph node 1.1%, bladder 1.2%, rectum 1.5%, small bowel 1.2%, colon 0.6%, penile bulb 0.8%, femoral head -0.2%. The dose difference between RT plan using CM and without CM showed an increase of dose in TV. The rate of increase was less than 2.5% (3D CRT: H&N 0.69~2.51%, prostate 0.04~1.14%, IMRT: H&N 0.58~1.31%, prostate 0.36~1.04%). RT plans using a CM has the insignificant effect on the organs and TV, so this error is allowable clinically. However, the much more accurate plan is possible as to image fusion (CM and without CM images) to ROI contour and when dose calculation, use the without CM image. Using the fusion of 'ROI import' perform calculations on without CM, it will be able to reduce the error (1~3%) caused by the CM.

• Journal of the Korean Magnetics Society
• /
• v.26 no.3
• /
• pp.92-98
• /
• 2016

To aim of this study was to assess the full scan and half scan of imaging with half scan factor. Patients without a cerebral vascular disease (n = 30) and were subject to the full scan half scan, and set a region of interest in the cerebral artery from the three regions (C1, C2, C3) in the range of 7 to 8 mm. MIP (maximum intensity projection) to reconstruct the images in signal strength SNR (signal to noise ration), PSNR (peak signal noise to ratio), RMSE (root mean square error), MAE (mean absolute error) and calculated by paired t-test for use by statistics were analyzed. Scan time was half scan (4 minutes 53 seconds), the full scan (6 minutes 04 seconds). The mean measurement range (7.21 mm) of all the ROI in the brain blood vessel, was the SNR of the first C1 is completely scanned (58.66 dB), half-scan (62.10 dB), a positive correlation ($r^2=0.503$), for the second C2 SNR is completely scanned (70.30 dB), half-scan (74.67 dB) the amount of correlation ($r^2=0.575$), third C3 of a complete scan SNR (70.33 dB), half scan SNR (74.64 dB) in the amount of correlation between the It was analyzed with ($r^2=0.523$). Comparative full scan with half of SNR ($4.75{\pm}0.26dB$), PSNR ($21.87{\pm}0.28dB$), RMSE ($48.88{\pm}1.61$), was calculated as MAE ($25.56{\pm}2.2$). SNR is also applied to examine the half-scans are not many differences in the quality of the two scan methods were not statistically significant in the scan (p-value > .05) image takes less time than a full scan was used.

• Journal of the Korean Magnetics Society
• /
• v.15 no.1
• /
• pp.42-47
• /
• 2005

Nanocrystalline Nd-Fe-B powder was synthesized by a new thermochemical process that combined with past reduction-diffusion process and spray-dry process. In this process, Ca reduction process is vary important due to formation of hard magnetic$Nd_{2}Fe_{14}B$ phase from various oxides by Ca powder. Therefore, the final products are essentially affected a shape, size, and composition etc. of the Ca reduced powders. Ca reduction was performed to way that raw powders just mixed with Ca powder in proper ratio unlike to compress into compact. The powders after mixture-type Ca reduction mainly composited with $Nd_{2}Fe_{14}B$ phase even relativily low reaction temperature ($800^{\circ}C$) and all particle size of powder were distributed less than 1 ${\mu}m$ except for powder after Ca oxides as magnetic properties of powders after cake-type Ca reduction, with the consequence that high magnetic properties has been expected. The magnetic properties of powders prepared by mixture-type Ca ruduction, with the conseqence that high magnatic properties has been expected. The magnetic properties of powders prepared by mixture-type Ca reduction process showed $_iH_c$ = 5.9 kOe, $B_r$ = 5.5 kG, (BH)max = $Nd_{2}Fe_{14}B{\to}Nd_{2}Fe_{17}B$ decomposition by violent exothermic reaction during washing.