• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.4
• /
• pp.96-101
• /
• 2011

The thin films of TiN have been used extensively as wear-resistant materials, for instance, such as tools of high-speed cutting, metal mold forming etc. In these days, because the thin films capable of being used more severe conditions are needed, the technologies of arc ion plating are tried to improve its characteristics. The purpose of this study is to investigate the characteristics of thin films of (Ti,Cr)N compared with those of TiN. The method of arc ion plating, which is known as showing good tight-adherence and productivity, was used. After manufacturing thin films of ($Ti_{1-x}Cr_{x}$)N (x=0~1) with change of Cr in (Ti,Cr) target, atomic concentration, structure, size of crystallite, residual stress and surface roughness of thin films on substrate were investigated. As the results, it was confirmed that Cr atomic concentrations of thin films were proportionally changed with Cr atomic concentrations of target, and thin films of ($Ti_{1-x}Cr_{x}$)N (x=0~1) showed NaCl type and CrN existed as solid solution to TiN.

• Textile Coloration and Finishing
• /
• v.22 no.1
• /
• pp.77-82
• /
• 2010

Highly conductive yarn was successfully obtained using electroless nickel plating method with palladium activation. In the presence of palladium seed on surface of fibers as a catalyst, continuos nickel layer produced on surface of fibers by reducing $Ni${2+}$ ion in the electroless plating bath to $Ni^0$. It was found that the Pd-activation using $SnCl_2$ and $PdCl_2$ to deposit palladium seeds on the surface of fibers plays a key role in the subsequent electroless plating of nickel. It also found that electroless nickel plating on the fibers can induce the nickel-plated $ELEX^{(R)}$ fibers to improve the electrical conductivity of the fibers. The thickness of nickel coating layer on the Pd-activated $ELEX^{(R)}$ fibers and specific conductivity of the fiber were increased through electroless plating time. The temperature of nickel plating bath was very effective to enhance the nickel deposition rate.

• Journal of Electrochemical Science and Technology
• /
• v.11 no.1
• /
• pp.92-98
• /
• 2020

SnO₂-based high-capacity anode materials are attractive candidate for the next-generation high-performance lithium-ion batteries since the theoretical capacity of SnO₂ can be ideally extended from 781 to 1494 mAh g^-1. Here 3D etched Cu foam is applied as a current collector for electron path and simultaneously a substrate for the SnO₂ coating, for developing an integrated electrode structure. We fabricate the 3D etched Cu foam through an auto-catalytic electroless plating method, and then coat the SnO₂ onto the self-supporting substrate through a simple sol-gel method. The catalytic dissolution of Cu metal makes secondary pores of both several micrometers and several tens of micrometers at the surface of Cu foam strut, besides main channel-like interconnected pores. Especially, the additional surface pores on etched Cu foam are intended for penetrating the individual strut of Cu foam, and thereby increasing the surface area for SnO₂ coating by using even the internal of Cu foam. The increased areal capacity with high structural integrity upon cycling is demonstrated in the SnO₂-coated 3D etched Cu foam. This study not only prepares the etched Cu foam using the spontaneous chemical reactions but also demonstrates the potential for electroless plating method about surface modification on various metal substrates.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.1
• /
• pp.49-55
• /
• 2006

The effect of coating temperature with regard to surface properties of TiN-coated layer on hard metal(WC-Co) are experimentally investigated. Hardness, surface roughness, TiN coating thickness and adsorption force were measured in order to evaluate the effect of coating temperature. The two-way ANOVA method is used in order to evaluate the experimental data. In AIP processing, It is concluded that the furnace temperature in the range of $400^{\circ}C\~500^{\circ}C$ affected to a little increasing the number of production with the coating temperature.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.6
• /
• pp.343-351
• /
• 1995

Titanium nitride films have been prepared on various substrates (silicon wafer, HSS) by cathode arc ion plating process to measure microhardness, adhesion and wear-resistant behaviors by changing the substrate bias voltages (0∼-300V), thickness and roughness. Microhardnesses were measured by micro vickers hardness tester, the adhesion strengths were evaluated by acoustic signals through the scratch test with incremental applied load. As the substrate bias voltages were increased, the ｛111｝ orientation was predominant, the microhardnesses and adhesion strengths of tool steel were observed to be stronger than those of without subatrate bias voltage. Adhesion strengths of the substrate bias were 4-7 times higher than those of without the substrate bias, confirmed by SEM with EDX. Wear resistances were used pin-on-disk tribotester and TiN costing reduced the abrasive wear. As the substrate bias was increased, the weight loss and the friction coefficient was decreased.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.233-238
• /
• 2011

The friction and wear characteristics of CrN and TiN coatings on SKD61 which is mold material using for extrusion of AZ80 magnesium alloy were investigated. The coatings were deposited by the arc ion-plating method, and the thickness were about $3.59{\mu}m$ and $3.28{\mu}m$, respectively. Reciprocating friction wear tests were conducted by varying pin load and temperature of counter substrate at un-lubricated condition. The pin loads were 11, 15 and 19 kgf, and the substrate temperatures were room temperature and $120^{\circ}C$. CrN coating which has a lower friction coefficient and a smaller adhesive wear with AZ80 magnesium alloy showed better wear resistance than TiN coating.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.111-111
• /
• 2012

• Journal of the Korean institute of surface engineering
• /
• v.31 no.4
• /
• pp.181-190
• /
• 1998

Al ion plating was carried to improve corrosion resistance of Nd-based permanent magnet made by prwder molding method. The effects of applied votage, pressyre and temperature were investigated to find the reation between coating parameters and their properties. Density of coating layer increased with voltage and thus corrosion resistance improved. However when voltage was applied more than 1000V, corrosion resistance whet down because of resputtering effect. Good corrosion resistance was acquired when gas pressure was $5.0\times10^-2$>torr, which is satisfied momentum energy of Ar, Al ions as well as quantity of plasma. The layer coated in low temperature range have better surface density and corrosion resistance than in high temperature. This result is seemed due to the characteristics of substrate itself. All coating layers were showed stong adhesion with substrate.

• Journal of the Korean institute of surface engineering
• /
• v.25 no.3
• /
• pp.133-143
• /
• 1992

Titanium nitride(TiN) films have been prepared by HCD plasma enhanced reactive ion plating. Density and temperature of the plasma generated by the HCD were investigated. It was shown that parameters such as the substrate bias voltage(0 350V) and N2 flow rate(10 180SCCM) influenced the growth, the growth, the microstructure and the color tone of the film mostly. In order to study the interface region, surface analysis by AES combined with sputter depth profiling was performed. Microhardness of the coated TiN films were measured by micro Vickers hardness tester. Also, the effect of coating parameters on composition, coating surface and fracture morphology, grain size and growth rate were examined.

• Polymer(Korea)
• /
• v.26 no.1
• /
• pp.105-112
• /
• 2002

The low actuation voltage and quick bending response of IPMC(ion-exchange polymer metal composite) are considered attractive for the construction of various types of actuators. In this study, in order to develop a new type actuators by using the IPMC platinum electrode of IPMC are fabricated by using electroless impregnation-reduction method plating. As the platinum-plating times are increased, IPMC performance was improved in terms of bending displacement and force due to the enhanced surface conductivity. In addition, we investigated the basic actuation characteristics of resonance frequency and actuator length as well as the effect of water uptake and ion mobility. Using the classical laminate theory(CLT), a modeling methodology was developed to predict the deformation, bending moment, and residual stress distribution of anisotropic IPMC thin plates. In this modeling methodology, the internal stress evolved by the unsymmetric distribution of water inside IPMC was quantitatively calculated and subsequently the bending moment and the curvature were estimated for various geometry of IPMC actuator.