• Journal of Surface Science and Engineering
• /
• v.27 no.4
• /
• pp.234-240
• /
• 1994

A large area impurity doping method for poly-Si TFT LCD has been developed. The advantage of this method is the doping of impurities into Si over a large area without mass separation and beam scanning. Phosphorus diluted in hydrogen was discharged by RF(13.56MHz) power and ions from discharged gas were accelerated by DC acceleration voltage and were implanted into deposited Si films. The annealing characteristic of this method was similar to that of the ion implantation method in the low doping concentration. Three mechanisms were evolved in the annealing characteristics of phosphorus doped Si films. Point defects annihilation and the retrogradation of dopant atoms at grain boundaries as a result of grain growth played a major role at low and high annealing temperature, respectively. However, due to the dopant segregation, the reverse annealing range existed at intermediate annealing temperature.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.289-300
• /
• 2002

In this study, the experiments are carried out by boron ion implantation at energies ranging from 700keV to 2MeV in silicon. The distribution of boron profiles are measured by SIMS(Cameca 6f). Boron dopants profiles after high temp]erasure annealing are also explained by comparisons of experimental and simulated data. A new electronic stopping model for Monte Carlo simulation of high energy implantation is presented. Also the comparisons of profiles by profiles boron ion implantations are demonstrated and interpreted with theoretical models. Finally range moments of SIMS and SRP profiles are calculated and compared with simulation results.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.222-225
• /
• 2000

BSCCO thin films have been fabricated by co-deposition at an ultralow growth rate using ion beam sputtering(IBS) method. Bi 2212 phase appeared in the temperature range of 750 and $795^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785^{\circ}C$. Whereas, $Po_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with $T_c$ (onset) of about 90 K and $T_c$(zero) of about 45 K is obtained. Only a smd amount of CuO in some films was observed as impurity, and no impurity phase such as $CaCuO_2$ was observed in d of the obtained films.

• Journal of the Korean Society of Industry Convergence
• /
• v.25 no.5
• /
• pp.715-724
• /
• 2022

In many electric vehicles, large-capacity pouch-type lithium-ion battery packs are mainly used to increase the mileage on a single charge. The lithium ion battery should be operated within the temperature range of 25℃ to 40℃ because the battery performance can be rapidly deteriorated due to an increase in internal temperature. Battery thermal management system (BTMS) can give the suitable temperature conditions to battery by water cooling method. In this research, the heat transfer characteristics (the battery temperature distributions and the water flow characteristics) were analyzed by CFD method to investigate the thermal performance of the cooling plate with 4-pass water flow structure. Moreover, the effect of the presence of fins between the battery cell was identified. The fins made smooth temperature distributions between the battery cells due to the heat spreading and lower the average battery cells temperature.

• Korean Chemical Engineering Research
• /
• v.61 no.3
• /
• pp.463-471
• /
• 2023

Nitrogen-rich carbon dots (NDots) were synthesized by using uric acid as carbon and nitrogen sources. The as-synthesized NDots showed strong dual emissions at 420 nm and 510 nm with excitation at 350 nm and 460 nm, respectively. The physicochemical analyses such as X-ray photoelectron spectroscopy, Transmission electron microscopy and Fourier transform infrared spectroscopy were used to analyze the chemical, physical and morphological structures of NDots. The as-synthesized NDots exhibited wide linear range (0-100 µM) and very low detection limit (124 nM) in Ag⁺ ion sensing. In addition, Ag⁺ saturated NDots could be used as an EDTA sensor by the EDTA induced PL recovery.

• Journal of Periodontal and Implant Science
• /
• v.28 no.4
• /
• pp.601-611
• /
• 1998

Ion irradiation is a very promising tool to modify the chemical structure and physical properities of polymers. This study was aimed to evaluate the cellular adhesion to ion beam-irradiated surface of biodegradable poly-l-lactide(PLLA) membrane. The PLLA membrane samples were irradiated by using 35 KeV $Ar^+$ to fluence of $5{\times}10^{13}$, $5{\times}10^{14}$ and $5{\times}10^{15}\;ion/cm^2$. Water contact angles to control and each dose of ion beam-irradiated PLLA membranes were measured. Cultured fetal rat calvarial osteoblasts were seeded onto control and each dose of ion beam-irradiated PLLA membranes and cultured. After 24 hours, each PLLA membranes onto which osteoblasts attached were examined by scanning electron microscopy(SEM). Osteoblasts were removed from each PLLA membrane and then, the vitality and the number of cells were calibrated. Alkaline phosphatase of detached cells from each PLLA membranes were measured. Ion beam-irradiated PLLA membranes showed no significantly morphological change from control PLLA membranes. In the measurement of water contact angle to each membrane, the dose range of ion beam employed in this study reduced significantly contact angles. Among them, $5{\times}10^{14}\;ion/cm^2$ showed the least contact angle. The vitalities of osteoblastes detached from each membranes were confirmed by flow cytometer and well attached cells with their own morphology onto each membranes were observed by SEM. A very strong improvement of the cell adhesion and proliferation was observed for ion beam-irradiated surfaces of PLLA membranes. $5{\times}10^{15}\;ion/cm^2$ exhibited the most strong effect also in cellular adherence. ALPase activities also tended to increase in ion beam-irradiated membranes but statistical differences were not found. These results suggested that ion beam irradiation is an effective tool to improve the adhesion and spreading behaviour of the cells onto the biodegradable PLLA membranes for the promotion of membrane-tissue integration.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.3 no.1
• /
• pp.41-47
• /
• 2005

Preparation of ferrocyanide-anion exchange resin and adsorption test of the prepared resin on the Cs$^{+}$$ion were performed. Adsorption capability of the prepared resin on the Cs$^{+}$ion in the simulated citric acid based soil decontamination waste solution was 4 times greater than that of the commercial cation exchange resin. Adsorption equilibrium of the prepared resin on the Cs$^{+}$ion reached within 360 minutes. Adsorption capability on the Cs$^{+}$ion became to decrease above the necessary Co$^{2+}$ion concentration in the experimental range. Recycling test of the spent ion exchange resin by the successive application of hydrogen peroxide and hydrazine was also performed. It was found that desorption of Cs$^{+}$ion from the resin occurred to satisfy the electroneutrality condition without any degradation of the resin.

• Korean Journal of Medicinal Crop Science
• /
• v.23 no.6
• /
• pp.446-453
• /
• 2015

Background : Excessively high concentration of sodium ion causednutrient deficiency and significantly decrease growth. This study was carried out to determine the limiting concentration range of sodium ion in the soil of ginseng field. Methods and Results : The growth of the ginseng cultivar Chunpoong reduced with increase in salinity, and the rate of growth reduction was higher in shoots than that of roots. Particularly, ginseng plants cultivated at high level of nitrate nitrogen or sodium may suffer delayed development and stunted growth. Chlorophyll damage occurred on the leaves of ginseng planted in relatively high levels (> $0.2cmol^+/kg$) of sodium ion, as determined by the fluorescence reaction. The incidence of physiological disorder in ginseng cultivated at 249 sites was correlated with the concentration of sodium ion in the soils. About 74% of ginseng fields in which physiological disorders occurred had concentrations of sodium ion in soil greater than $0.2cmol^+/kg$. In contrast, the concentration of sodium ions at 51 of 85 sites where no damage occurred was relatively ($0.05cmol^+/kg-0.15cmol^+/kg$). Conclusions : The concentration of sodium ion in soil of ginseng fields can be classified into three levels optimum (${\leq}0.15$), permissible allowance (0.15 - 0.2) and excessive (> 0.2).

• Analytical Science and Technology
• /
• v.5 no.2
• /
• pp.169-176
• /
• 1992

Analytical detection limits and Relative Ion Yield (RIY) by a jet type ion source glow discharge mass spectrometer(GD/MS) have been measured. With a jet type ion source, the sample loss rate for a Cu sample is 0.23 mg/min with 0.1 L/min gas flow rate and 0.11 mg/min with no gas flow rate. However, the ion intensity of Cu does not change significantly with thee variation of the gas flow rate. The RIY values obtained from the calibration curves of the six copper based standards were between 0.57 of Fe and 3.5 of Cr. The detection limits of most elements were in the range of 0.9 and 2.0 ppm when the glow discharge was operated at 4 mA, 1000V.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.13 no.6
• /
• pp.1121-1126
• /
• 2010

Borosilicate glass (81% $SiO_2$-2% $Al_2O_3$-13% $B_2O_3$-4% $Na_2O_3$) was prepared, and the glass was ion exchanged in $KNO_3$ powder containing different temperature and time. The $K^+-Na^+$ ion exchange takes place at the glass surface and creates compressed stress, which raise the mechanical strength of the glass. The depth profile of $Na^+$ and $K^+$ was observed by electron probe micro analyzer. With the increasing heat-treatment time from 0min to 20min, the depth profile was increased from 17.1um to 29.4um, but mechanical properties were decreased. It was also found out that excessive heat treatment brings stress relaxation. The Vickers hardness, Fracture Toughness and bending strength of ion exchanged samples at $570^{\circ}C$ for 10min were $821.8H_v$, $1.3404MPa{\cdot}m^{1/2}$, and 953MPa, which is about 120%, 180%, and 450% higher than parent borosilicate glass, respectively. Transmittance was analyzed by UV-VIS-NIR spectrophotometer. Transmittance of ion exchanged borosilicate glass was decreased slightly at visible-range. It can be expected that transparent bulletproof materials in more light-weight and thinner by ion exchanged borosilicate glass.