• Applied Chemistry for Engineering
• /
• v.32 no.1
• /
• pp.117-123
• /
• 2021

In this study, the composite was prepared by mixing SiOx, soft carbon, and carbon black and the electrochemical properties of lithium ion battery were investigated. The content of SiOx added to improve the capacity of the soft carbon anode material was varied to 0, 6, 8, 10, 20 wt%, and carbon black was added as a structural stabilizer for reducing the volume expansion of SiOx. The physical properties of prepared CB/SiOx/C composite were investigated through XRD, SEM, EDS and powder resistance analysis. In addition, the electrochemical properties of prepared composite were observed through the charge/discharge capacity, rate and impedance analysis of the lithium ion battery. The prepared CB/SiOx/C composite had an inner cavity capable of mitigating the volume expansion of SiOx by adding carbon black. The formed internal cavity showed a low initial efficiency when the SiOx content was less than 8 wt%, and low cycle stability when the content of SiOx was less than 20 wt%. The CB/SiOx/C composite containing 10 wt% of SiOx showed an initial discharge capacity of 537 mAh/g, a capacity retention rate of 88%, and a rate of 79 at 2C/0.1C. SiOx was added to improve the capacity of the soft carbon anode material, and carbon black was added as a structural stabilizer to buffer the volume change of SiOx. In order to use the CB/SiOx/C composite as a high-efficiency anode material, the mechanism of the optimal SiOx and the use of carbon black as a structural stabilizer was discussed.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.2
• /
• pp.38-45
• /
• 1999

This study was to figure out proper Formaldehyde/Urea molar ratio of UF resin with satisfactory bonding strength of plywood and properties of particleboard. The six kinds of UF resins were manufactured with F/U molar ratio 1.0, 1.2, 1.4, 1.6, 1.8, and 2.0. The boards were made of three kinds of raw materials : Veneer, Sliver-Particle and Strand-Particle. Manufacturing condition of plywood : amount of mixing resin was 150g/$m^2$. The fourty secs/mm simple-pressing schedule in the pressure 10kgf/$m^2$ was applied for 480mm${\times}$700mm board at the temperature of $110^{\circ}C$ in a hot press. Manufacturing condition of particleboard : Target density was 0.65g/$cm^2$. The stepwise 9 minutes- multi-pressing schedule in the maximum pressure 40kgf/$cm^2$, the minimum pressure 15kgf/$cm^2$ was applied for $480mm{\times}634mm{\times}12mm$ board at the temperature of $150^{\circ}C$ in a hot press. The results are as follows : I. In bonding strength, plywood which was made by F/U molar ratio 1.2 showed the highest value. Other molar ratio resin also gave the satisfied value of KS standard, 7.5kgf/$cm^2$. 2. In internal bond strength of particleboard, Sliver-Particleboard(SLPB) and Strand-Particleboard(STPB) varied respectively from 5.9kgf/$cm^2$ to 4.8kgf/$cm^2$, from 6.7kgf/$cm^2$ to 5.4kgf/$cm^2$. SLPB with F/U=1.2 and STPB with F/U=1.6 had higher IB value. Also, both SLPB and STPB showed lower IB value in F/U molar ratio 2.0 and 1.0. 3. SLPB and STPB with six kinds of UF resin respectively satisfied bending strength of KS standard 150 Type(130kgf/$cm^2$) and 200 Type(180kgf/$cm^2$). Bending strength data for both of SLPB and STPB showed little or no loss from F/U=1.8 to F/U=1.2. Also, STPB was approximately two times higher than that of SLPB. Therefore, the raw material's shape had more effect on bending strength than the FlU molar ratio. 4. F/U=1.6 and 1.4 showed the lower thickness swelling in SLPB and STPB. All of STPBs satisfied thickness swelling of KS standard, under 12%.