• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.10 s.181
• /
• pp.2461-2468
• /
• 2000

In this paper, single fiber pull-out test is used to measure the interfacial bonding shear strength of $Ti_{50}-Ni_{50}$ shape memory alloy composite with temperature. Fiber and matrix of $Ti_{50}-Ni_{50}$ shape memory alloy composite are respectively $Ti_{50}-Ni_{50}$ shape memory alloy and epoxy resin. To strengthen the interfacial bonding shear stress, various surface treatments are used. They are the hand-sanded surface treatment, the acid etched surface treatment and the silane coupled surface treatment etc.. The interfacial bonding shear strength of surface treated shape memory alloy fiber is greater than that of surface untreated shape memory alloy fiber by from 10% to 16%. It is assured that the hand-sanded surface treatment and the acid etched surface treatment are the best way to strengthen the interfacial bonding shear strength of $Ti_{50}-Ni_{50}$ shape memory composite. The best treatment condition of surface is 10% HNO$_3$ solution in the etching method to strengthen the interfacial bonding shear strength of $Ti_{50}-Ni_{50}$ shape memory alloy composite.

• Journal of Welding and Joining
• /
• v.5 no.3
• /
• pp.28-37
• /
• 1987

To clarify the debonding phenomena of clad steel, the effect of thermal treatment (temperature, holding time) on the interfacial strength of clad steel was preliminarily investigated. From this study, it was confirmed that the interfacial strength of clad steel was deteriorated by thermal treatment and the amount of strength deteriorated, depending on the condition of thermal treatment, could be evaluated by the following equation. ${\sigma}_{ HT}/{\sigma}_{i}/=A_{0}-A\;exp(-Q/RT)log(t/t_{0})$ This equation implies that temperature has a far strong effect on strength deterioration than tiem. The deterioration of interfacial strength of clad steel after thermal treatment may be derived from the thermal stress caused by the difference in thermal expansion coefficient between component materials and microstructural change along the interface.

• Macromolecular Research
• /
• v.16 no.5
• /
• pp.411-417
• /
• 2008

The surfaces of henequen fibers, which can be obtained from the leaves of agave plants, were treated with two different media, tap water and sodium hydroxide, that underwent both soaking and ultrasonic methods for the fiber surface treatment. Various biocomposites were fabricated with untreated and treated, chopped henequen fibers and polypropylene using a compression molding method. The result is discussed in terms of interfacial shear strength, flexural properties, dynamic mechanical properties, and fracture surface observations of the biocomposites. The soaking (static method) and ultrasonic (dynamic method) treatments with tap water and sodium hydroxide at different concentrations and treatment times significantly influenced the interfacial, flexural and dynamic mechanical properties of henequen/polypropylene biocomposites. The alkali treatment was more effective than the water treatment in improving the interfacial and mechanical properties of randomly oriented, chopped henequen/PP bio-composites. In addition, the application of the ultrasonic method to each treatment was relatively more effective in increasing the properties than the soaking method, depending on the treatment medium and condition. The greatest improvement in the properties studied was achieved by ultrasonic alkalization of natural fibers, which was in agreement with the other results of interfacial shear strength, flexural strength and modulus, storage modulus, and fracture surfaces.

• Journal of Adhesion and Interface
• /
• v.5 no.4
• /
• pp.9-16
• /
• 2004

Silk fibers were subjected to argon and ethylene plasma treatments in order to improve the interfacial adhesion with polylactic acid (PLA). After the plasma surface treatment, the surface morphology and surface adhesion of silk fibers to the PLA resin were largely changed. Various plasma treatment conditions were used in this work: 10, 25, 50, 100 and 150 W of electric power, 1, 3, 5, 7 and 10 minutes of treatment time, and 10 and 50 sccm of a gas flow rate. The interfacial shear strength of plasma-treated Silk/PLA biocomposites was measured by a single fiber micro-droplet debonding test method. The result provided an optimal plasma treatment condition to obtain the improved interfacial adhesion in the Silk/PLA biocomposites.

• Journal of Welding and Joining
• /
• v.5 no.4
• /
• pp.22-27
• /
• 1987

The debonding of clad steel was often occurred at interface between stainless steel and carbon steel during the fabrication of pressure vessel. In order to clarify the causes of debonding phenomena, the fabrication sequences were fully analyzed. As a result, possible factors were noticed for causing the debonding of clad steel, that is, thermal treatment on weldment and welding. Moreover the existence of hydrogen diffused from surroundings also expedites the debonding of clad steel. In this stud, the effect of welding thermal cycle, hydrogen and mixed condition under thermal treatment on the interfacial strength of clad steel were investigated to understand the debonding mechanism of clad steel. From this study, it has been confirmed that the interfacial strength of clad steel was remarkablely deteriorated due to welding and/or existence of hydrogen under thermal treatment. In the case of welding thermal cycle effect, the higher temperature at interface experienced by welding, the more reduction in interfacial strength of clad steel resulted in. And the existence of diffusible hydrogen also reduced the interfacial strength. It is also found that the interfacial strength of clad steel became much lower value than that of the as-received plate under coexistence of above mentioned factors.

• Textile Coloration and Finishing
• /
• v.15 no.4
• /
• pp.1-7
• /
• 2003

We investigated the effect of color depth on polyester fabrics by plasma treatment. In this study, although it have many paper about effects of plasma treatment, we observed interfacial electrokinetic potential of polyester fabrics by plasma treatment and also we investigated relationship between deep coloring agent and plasma treatment to get the effect of color depth on polyester fabrics. The results obtained are as follows, 1. Plasma treatment did not enhanced the effect of color depth of polyester fabrics by plasma treatment independently. 2. In the case of using the deep coloring agent with plasma treatment on polyester fabrics, lightness was more decreased than using the deep coloring agent itself. 3. Plasma treatment could not affect surface shape and tensile strength of treated polyester fabrics.

• Korean Journal of Materials Research
• /
• v.17 no.4
• /
• pp.215-221
• /
• 2007

The effect of $CF_4$ plasma treatment condition on the interfacial adhesion energy of inkjet printed Ag/polyimide system is evaluated from $180^{\circ}$ peel test by calculating the plastic deformation energy of peeled metal films. Interfacial fracture energy between Ag and as-received polyimide was 5.5 g/mm. $CF_4$ plasma treatment on the polyimide surface enhanced the interfacial fracture energy up to 17.6 g/mm. This is caused by the increase in the surface roughness as well as the change in functional group of the polyimide film due to $CF_4$ plasma treatment on the polyimide surface. Therefore, both the mechanical interlocking effect and the chemical bonding effect are responsible for interfacial adhesion improvement in ink jet printed Ag/polyimide systems.

• Advanced Composite Materials
• /
• v.18 no.3
• /
• pp.221-232
• /
• 2009

The allylamine plasma treatment is used to modify the surface properties of vapor grown carbon fibers (VGCF). It is to improve the interfacial bonding between the VGCF and epoxy matrix. The allylamine plasma process was performed by batch process in a vacuum chamber, using gas injection followed by plasma discharge for the durations of 20, 40 and 60 min. The interdependence of mechanical properties on the VGCF contents, treatment time and interfacial bonding between VGCF/ep was investigated. The interfacial bonding between VGCF and epoxy matrix was observed by scanning electron microscopy (SEM) micrographs of nanocomposites fracture surfaces. The changes in the mechanical properties of VGCF/ep, such as the tensile modulus and strength were discussed. The mechanical properties of allylamine plasma treated (AAPT) VGCF/ep were compared with those of raw VGCF/ep. The tensile strength and modulus of allyamine plasma treated VGCF40 (40 min treatment)/ep demonstrated a higher value than those of other samples. The mechanical properties were increased with the allyamine plasma treatment due to the improved adhesion at VGCF/ep interface. The modification of the carbon nanofibers surface was observed by transmission electron microscopy (TEM). SEM micrographs showed an excellent dispersion of VGCF in epoxy matrix by ultrasonic method.

• The Transactions of the Korean Institute of Electrical Engineers D
• /
• v.52 no.5
• /
• pp.206-206
• /
• 2003

It is hard to expect excellent electrical, mechanical and chemical properties from most of the composite materials presently used as insulators due to insufficient wettability property caused by the difference of interfacial properties between the matrix material and the reinforcer. Therefore, various interfacial coupling agents have been developed to improve the interfacial properties of composite materials. But if the wettable coupling agents are used outdoor for a long time, change in quality takes place in the coupling agents themselves, bringing about deterioration of the properties of the composite materials. In this study, glass surface was treated by plasma to examine the effect of dry interface treatment without coupling agent. It was identified that the optimum parameters for the best wettability of the samples at the time of generation of plasma were oxygen atmosphere, 0.1 torr of system pressure, 100 W of discharge power, and 3 minutes of discharge time. Also, the surface resistance rate and dielectric property were improved.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.5
• /
• pp.206-212
• /
• 2003

It is hard to expect excellent electrical, mechanical and chemical properties from most of the composite materials presently used as insulators due to insufficient wettability property caused by the difference of interfacial properties between the matrix material and the reinforcer. Therefore, various interfacial coupling agents have been developed to improve the interfacial properties of composite materials. But if the wettable coupling agents are used outdoor for a long time, change in quality takes place in the coupling agents themselves, bringing about deterioration of the properties of the composite materials. In this study, glass surface was treated by plasma to examine the effect of dry interface treatment without coupling agent. It was identified that the optimum parameters for the best wettability of the samples at the time of generation of plasma were oxygen atmosphere, 0.1 torr of system pressure, 100 W of discharge power, and 3 minutes of discharge time. Also, the surface resistance rate and dielectric property were improved.