• Journal of Periodontal and Implant Science
• /
• 제50권2호
• /
• pp.106-120
• /
• 2020

Purpose: A new form of porous polyethylene, characterized by higher porosity and pore interconnectivity, was developed for use as a tissue-integrated implant. This study evaluated the effectiveness of porous polyethylene blocks used as an onlay bone graft in rabbit mandible in terms of tissue reaction, bone ingrowth, fibrovascularization, and graft-bone interfacial integrity. Methods: Twelve New Zealand white rabbits were randomized into 3 treatment groups according to the study period (4, 12, or 24 weeks). Cylindrical specimens measuring 5 mm in diameter and 4.5 mm in thickness were placed directly on the body of the mandible without bone bed decortication, fixed in place with a titanium screw, and covered with a collagen membrane. Histologic and histomorphometric analyses were done using hematoxylin and eosin-stained bone slices. Interfacial shear strength was tested to quantify graft-bone interfacial integrity. Results: The porous polyethylene graft was observed to integrate with the mandibular bone and exhibited tissue-bridge connections. At all postoperative time points, it was noted that the host tissues had grown deep into the pores of the porous polyethylene in the direction from the interface to the center of the graft. Both fibrovascular tissue and bone were found within the pores, but most bone ingrowth was observed at the graft-mandibular bone interface. Bone ingrowth depth and interfacial shear strength were in the range of 2.76-3.89 mm and 1.11-1.43 MPa, respectively. No significant differences among post-implantation time points were found for tissue ingrowth percentage and interfacial shear strength (P>0.05). Conclusions: Within the limits of the study, the present study revealed that the new porous polyethylene did not provoke any adverse systemic reactions. The material promoted fibrovascularization and displayed osteoconductive and osteogenic properties within and outside the contact interface. Stable interfacial integration between the graft and bone also took place.

• Journal of Welding and Joining
• /
• 제29권1호
• /
• pp.99-106
• /
• 2011

Joint strength between a solder ball and a pad on a substrate is one of the major factors which have effects on electronic device reliability. The effort to improve solder joint strength via surface cleaning, heat treatment and solder composition change have been in progress. This paper will discuss the method of solder ball joint strength improvement using LF hydrogen radical cleaning treatment and focus on the effects of surface treatment condition on the solder ball shear strength and interfacial reactions. In the joint without radical cleaning, voids were observed at the interface. However, the specimens cleaned by hydrogen-radical didn't have voids at the interface regardless of cleaning time. The shear strength between the solder ball and the pad was increased over 120%(about 800gf) when compared to that without the radical treatment (680gf) under the same reflow condition. Especially, at the specimen treated for 5minutes, ball shear strength was considerably increased over 150%(1150gf). Through the observation of fracture surface and cross-section microstructure, the increase of joint strength resulted from the change of fracture mode, that is, from the solder ball fracture to IMC/Ni(P) interfacial fracture. The other cases like radical treated specimen for 1, 3, 7, 9min. showed IMC/solder interfacial fracture rather than fracture in the solder ball.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 추계학술발표대회 논문집
• /
• pp.153-157
• /
• 2001

Interfacial properties and microfailure modes of electrodeposition (ED) treated carbon fiber reinforced polyetherimide (PEI) toughened epoxy composite were investigated using microdroplet test and the measurement of surface wettability. As PEI content increased, Interfacial shear strength (IFSS) increased due to enhanced toughness and plastic deformation of PEI. In the untreated case, IFSS increased with adding PEI content, and IFSS of pure PEI matrix showed the highest. On the other hand, for ED-treated case IFSS increased with PEI content with rather low improvement rate. The work of adhesion between fiber and matrix was not directly proportional to IFSS for both the untreated and ED-treated cases. The matrix toughness might contribute to IFSS more likely than the surface wettability. Interfacial properties of epoxy-PEI composite can be affected efficiently by both the control of matrix toughness and ED treatment.

• Advanced Composite Materials
• /
• 제16권4호
• /
• pp.315-334
• /
• 2007

In the present study, chopped henequen natural fibers without and with surface modification by electron beam (E-beam) treatment were incorporated into a polypropylene matrix. Prior to composite fabrication, a bundle of raw henequen fibers were treated at various E-beam intensities from 10 kGy to 500 kGy. The effect of E-beam intensity on the interfacial, mechanical and thermal properties of randomly oriented henequen/polypropylene composites with the fiber contents of 40 vol% was investigated focusing on the interfacial shear strength, flexural and tensile properties, dynamic mechanical properties, thermal stability, and fracture behavior. Each characteristic of the material strongly depended on the E-beam intensity irradiated, showing an increasing or decreasing effect. The present study demonstrates that henequen fiber surfaces can be modified successfully with an appropriate dosage of electron beam and use of a low E-beam intensity of 10 kGy results in the improvement of the interfacial properties, flexural properties, tensile properties, dynamic mechanical properties and thermal stability of henequen/polypropylene composites.

• 대한치과기공학회지
• /
• 제23권1호
• /
• pp.31-43
• /
• 2001

This study was performed to observe the micro-structure change of surface, behavior of oxide change of element, the component transformation of the alloy and the bonding strength between the porcelain interface in order to investigate effects of indium, tin on interfacial properties of porcelain fused to low gold alloy. Hardness of castings was measured with a micro-Vicker's hardness tester. The compositional change of the surface of heat-treated specimen was analyzed with an EDS and an EPMA. The interfacial shear bonding strength between alloy specimen and fused porcelain was measured with a mechanical testing system(MTS 858.20). The results were as follows: 1) The hardness value of alloy increased as increasing amount of indium addition. 2) The formation of oxidation increased as increasing indium and tin contents after heat treatment. 3) Diffusion of indium and tin elements increased as increasing indium and tin contents in metal-porcelain surface after porcelain fused to metal firing. 4) The most interfacial shear bonding strength was increased as increasing a composition of adding elements, and a heat-treatment time, and an oxygen partial pressure. From the results of this study it was found that the addition of alloying elements such as indium and tin increase hardness of as-cast alloy, produce surface oxide layer of adding elements by heat-treatment which may improve interfacial bonding strength between alloy and porcelain.

• Restorative Dentistry and Endodontics
• /
• 제20권1호
• /
• pp.289-302
• /
• 1995

The purpose of this study was to estimate the shear bond strength and observe the fractured and interfacial surfaces of various dentin bonding agents used conjunction with a visible light cured composite. The senentytwo human premolars and molars extracted due to periodontal or orthodontic reasons were used and randomely divided into six groups. All the prepared dentin surfaces were treated with Superbond D-liner, Scotchbond Multi-Purpose, All-Bond 2 and Prisma Universal Bond 3 accroding to the manufacturer's instructions. Six specimens were then demineralized in 10 % HCl for 24 hours and the other six specimens were not demineralized in order to observe the interfacial surfaces with Hitachi X-450 SEM at 25Kv. Also shear bond strength were obtained using an Instron Testing Machine with a crosshead speed of 1mm/min. The following results were obtained : 1. Although shear bond strength of Superbond D-Liner(17.35 MPa) and Scotch-bond Multi-Purpose group(17.29 MPa) were higher than the All-Bond 2(12.80 MPa) and Prisma Universial Bond 3 (13.43 MPa), there were no significant statistic differences in the shear bond strength between 4 groups.(P<0.05) As a result of etching to dentin in Prism a Universial BOND 3 experimentally, the resin tag was formed, but shear bond strength was decreased. 2. The resin tag into the opened dentinal tubule was formed in Superbond D-Liner, Scotchbond Multi-Purpose, All-Bond 2(etching) and Prisma Universial Bond 3(etching), but not in the All-Bone 2 and Prism a Universial Bond 3(non-etching). 3. Strong, durable bonds between dentin and dentinal bonding agents are essential, not only resin tag into the dentinal tubules, but also hybrid layer.

• Composites Research
• /
• 제24권4호
• /
• pp.11-16
• /
• 2011

극저온 응용에서 사용하는 고분자복합재료의 계면물성 유지가 아주 중요하다. 본 연구에서는 상온과 극저온에서 사용하는 단일 탄소섬유강화 에폭시 복합재료를 마이크로드롭넷 시험과 전기-미세역학시험법을 이용한 계면전단강도와 겉보기 강성도를 평가하였다. 탄소섬유와 저온용 에폭시의 극저온에 따른 기계적 물성변화를 확인하였다. 극저온에서 탄소섬유 인장실험 결과, 상온과 비교하여 강성도는 유지하면서 강도와 연신율이 감소하였다. 이에 비해, 에폭시 기지는 상온보다 극저온에서 강도가 증가되었으나, 연신율이 감소하는 결과를 보여주었다. 이는 탄소섬유에 비해 에폭시 수지내 존재하는 빈 공간이 극저온에서 열적 수축이 최대로 일어나기 때문이다. 계면전단강도는 $-10^{\circ}C$에서 최대를 보인 후에 극저온까지 점차 감소를 보여 주었다. 그러나, 탄소섬유와 YDF-175 에폭시가 극저온에서도 여전히 상온보다 양호한 계면전단강도를 보여주었다. 이 결과는 아주 유용하며 선정된 저온용 에폭시의 인성과 계면접착력이 극저온에서도 유지되기 때문이다.

• Carbon letters
• /
• 제17권1호
• /
• pp.33-38
• /
• 2016

In the present study, exfoliated graphite nanoplatelets (xGnP) with different particle sizes were coated onto polyacrylonitrile-based carbon fibers by a direct coating method. The flexural properties, interlaminar shear strength, and the morphology of the xGnP-coated carbon fiber/phenolic matrix composites were investigated in terms of their longitudinal flexural strength and modulus, interlaminar shear strength, and by optical and scanning electron microscopic observations. The results were compared with a phenolic matrix composite counterpart prepared without xGnP. The flexural properties and interlaminar shear strength of the xGnP-coated carbon fiber/phenolic matrix composites were found to be higher than those of the uncoated composite. The flexural and interlaminar shear strengths were affected by the particle size of the xGnP, while the particle size had no significant effect on the flexural modulus. It seems that the interfacial contacts between the xGnP-coated carbon fibers and the phenolic matrix play a role in enhancing the flexural strength as well as the interlaminar shear strength of the composites.

• Composites Research
• /
• 제12권6호
• /
• pp.15-21
• /
• 1999

비닐에스테르 수지와 탄소섬유의 계면접착력 향상을 위하여 탄소섬유에 물에 분산된 carboxy modified poly(hydroxy ether) (C-PHE)와 수용성 고분자인 poly(hydroxy ether ethanol amine) (PHEA) 및 비수용성인 poly(hydroxy ether) (PHE) 로 코팅하였다. 고분자로 코팅된 탄소섬유와 수지의 계면전단강도는 micro-droplet 시편을 제조하여 측정하였으며,각 시료마다 30개 이상의 시편을 사용하였다. 접착기구 규명을 위하여 코팅재로 사용된 고분자와 비닐에스테르 수지와 계면에서 확산현상을 고찰하였으며, 접착성 시험 후 탄소섬유의 표면을 SEM을 이용하여 분석하였다. PHE와 C-PHE코팅으로 탄소섬유의 계면전단강도가 크게 증가하였으며, 이는 이들 고분자의 비닐에스테르에 대한 우수한 용해도(solubility)때문으로 보여진다. 하지만 용해도가 낮은 PHEA코팅은 접착력 향상에 효과가 없었다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 1999년도 추계학술발표대회 논문집
• /
• pp.28-31
• /
• 1999

Carbon fiber/epoxy composites using electrodeposited monomeric and polymeric coupling agents were compared with the dipping and the untreated cases. Treating conditions such as time, concentration and temperature were optimized. Four-fibers embedded micro-composites were prepared for fragmentation test. Interfacial properties of four-fiber composites with different surface treatments were investigated with simultaneous acoustic emission (AE) monitoring. The microfailure mechanisms occurring from fiber break, matrix and interlayer crackings were examined by AE parameters and an optical microscope. It was found that interfacial shear strength (IFSS) of electrodeposited carbon fibers was much higher than the other cases under dry and wet conditions. Well separated and different-shaped AE groups occurs for the untreated and ED treated case, respectively.