• 한국세라믹학회지
• /
• 제55권1호
• /
• pp.61-66
• /
• 2018

In this study, fabrication method of inorganic insulation were studied to reduce $CO_2$ from buildings. Main materials for inorganic insulation were used cement, blast furnace slag and aluminum powder as foaming agent. Mixing ratio of cement and slag was controlled and physical properties of inorganic insulation were analyzed. When inorganic insulation was fabricated using cement and slag, expanded slurries were not sunken and hardened normally. Pore size was 0.5 - 2 mm; mean pore size was about 1mm in inorganic insulation. Compressive strength of inorganic insulation increased with curing time and increased slightly with cement fineness. However, specific gravity decreased slightly with curing time; this phenomenon was caused by evaporation of adsorptive water. When inorganic insulation was dried at $60^{\circ}C$, compressive strength was higher than that of undried insulation. The highest compressive strength was found with a mixture of cement (50%) and slag (30%) in inorganic insulation. Compressive strength was 0.32 MPa, thermal conductivity was 0.043 W/mK and specific gravity was $0.12g/cm^3$.

• 한국건축시공학회지
• /
• 제16권6호
• /
• pp.529-534
• /
• 2016

칼슘실리케이트계 무기단열소재는 주원료로 시멘트를 90%를 사용하는 다공성 무기단열소재이다. 기존 무기단열소재와 달리 고온의 수화반응 처리가 없기 때문에 가격이 저렴하며, 불연소재의 원료를 사용하여 화제의 위험성도 적다. 칼슘실리케이트 단열소재는 $0.13g/cm^3$의 밀도와 0.050W/mK이하의 우수한 열전도도를 갖는 단열소재이다. 칼슘실리케이트 단열소재는 경량화 될수록 내부 기포를 다량 함유해야 하며 기포를 다량 함유함에 따라 단열성 또한 우수해진다. 본 연구에서는 다량의 기포를 함유하며 일정강도발현을 목표로, 칼슘실리케이트계 무기단열소재의 주성분인 시멘트가 수화반응에 따라 초기 및 장기강도발현하는 특성을 이용하여 칼슘실리케이트계 무기단열소재에 적용하여 물리적 특성을 알아보고자 하였다.

• 전기학회논문지
• /
• 제67권11호
• /
• pp.1463-1470
• /
• 2018

In this study, 20 types of samples were prepared by mixing different kinds of inorganic materials to develop insulation materials for epoxy - based GIS substation equipment used under high voltage environmentally friendly insulation gas. One of the electrical characteristics, AC insulation breakdown experiment was performed. As mixing ratio of mixed heterogeneous inorganic materials, the dielectric breakdown strength was increased with increasing filler ratio of micro silica, micro silica : micro Alumina, 1:9, 3:7, 5:5, 7:3, 9:1, and decreased as the filling amount of micro alumina increased. The AC insulation breakdown characteristics were the best when the composition ratio was 9:1. The higher the content of silica, the better the interfacial properties, and the larger the alumina content ratio, the worse the interfacial properties.

• 한국건설순환자원학회논문집
• /
• 제9권4호
• /
• pp.642-649
• /
• 2021

건축물의 에너지 절약기준이 강화되면서 외단열 공법의 적용과 단열재 두께가 증가하고 있다. 유기계 단열재는 시공성, 경제성 등 시공비용 절감 효과와 뛰어난 단열성능을 가지고 있다. 하지만, 유기계 단열재 특성상 열에 매우 취약하므로 화재 발생 시 급격한 화재확산과 유독가스 발생으로 심각한 피해가 발생한다. 무기계 단열재는 기본적으로 불연성능을 가지나 무겁고 유기계 단열재에 비해 단열성능이 떨어진다. 글라스 버블은 소다 라임 보로실리케이트 유리로 밀도가 매우 낮고, 내부가 비어 있는 구형의 입자로 볼베어링 효과로 유동성이 개선된다. 또한, 무기계 단열재에 혼입하여 사용할 경우 밀도와 단열성능이 개선된다. 본 연구는 시멘트계 재료와 글라스 버블을 혼합하여 무기 단열재를 제조하였고 단열, 난연 및 불연성능을 평가하였다. 연구 결과, 글라스 버블의 혼입률이 증가할수록 열린 기공을 형성하고 있으나, 기공 및 셀 벽에 분포됨에 따라 충분한 단열성능을 보인다. 또한, 글라스 버블의 혼입률은 10% 이하로 사용하는 것이 바람직하다.

• 한국표면공학회지
• /
• 제22권3호
• /
• pp.109-117
• /
• 1989

The effect of heft treatment on the characteristic properties of insulation layer is studied for two kinds of non-oriented silicon steels, which were insulation-coates with various kinds of inorganic and inorganic-organic complex coating solutions. In addition, how the carbon contained in the insulation layer would affect the carbon content and the magnetic properties of the steel substrates is examined. Lower temperature heat treftment ($480^{\circ}C$ for 0.5hr) is found to render morw favorable surface qualities, wheras higher temperature heat treatment ($790^{\circ}C$ for 2hr) better core loss due to grin growt occurred during the heat treatment. Decarburization of the steel substrate is also found unaffectrd by the presence of carbon in the insulation layer.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.120-121
• /
• 2021

The organic insulation material has excellent thermal insulation property, but it is difficult to expect fire stability, and semi inorganic insulation only delays combustible hour but it is difficult to expect fire stability. In this study, thermal insulation property of cement-based non-combustible inorganic insulation using cement and non combustible materials and redispersible polymer powder was studied. As a result of the experiment, the thermal insulation property decreased as the use of redispersible polymer powder increased, but the heat insulation property improved when using the appropriate amount.

• 한국화재소방학회논문지
• /
• 제5권1호
• /
• pp.29-36
• /
• 1991

The purpose of this study is to understand the variations of the properties of matters according to the heated temperature of inorganic insulation. As a result, form the variation of heat conductivity and maintaining from of insulation, the range of reusable heated temperature of inorganic insulation is as follows. Glass wool : $400^{\circ}C$, Rock wool : $600^{\circ}C$, Perlite : $800^{\circ}C$.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2018년도 춘계 학술논문 발표대회
• /
• pp.222-223
• /
• 2018

Recent government policies are increasing interest in zero-energy housing, a building that minimizes energy consumption (90% reduction). As the importance of building passive performance is emphasized, the role of insulation is increasing as a way to reduce indoor heat loss in order to minimize the use of cooling and heating energy. There are two main types of insulation. Organic insulation is widely used for various construction structures such as construction and industrial due to some merits such as the convenience of construction and construction cost. However, it has been pointed out as a main cause every time a fire accident occurs, Jecheon Sports Center', the fire damage of buildings caused by the use of organic insulation materials is expanding to social problems, so it is urgent to research on nonflammable inorganic insulation materials.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 춘계 학술논문 발표대회
• /
• pp.217-218
• /
• 2012

To prevent energy waste in buildings used heat insulator. Heat insulator materials can be classified inorganic and organic. The organic material is be toxic gas emission, when a fire occurs. And it has lower water resistance. The inorganic material is heavy and worse thermal performance than organic materials. This study focused on thermal conductivity and density of inorganic foam material for using industrial by-products materials.

• 한국건설순환자원학회논문집
• /
• 제3권4호
• /
• pp.328-334
• /
• 2015

건축용 단열재는 에너지 절약을 목적으로 적용되며 불연 및 내화성능이 요구되는 부위는 무기계 섬유를 주재료로 사용하는 미네랄울 및 글라스울 소재가 적용된다. 하지만 무기계 소재인 미네랄울이나 글라스울은 특성상 수분에 취약하여 뭉침 및 처짐 현상 등이 발생하여 단열효과가 떨어지며 유기계 소재인 폴리스티렌폼이나 우레탄폼 등은 화재에 취약하고 일산화탄소 발생에 의한 가스유해성 등으로 적용에 한계를 갖고 있다. 본 연구에서는 폐유리분말과 플라이애시를 사용하여 가볍고 열전도율이 낮은 무기계 경량 발포소재를 제조하고 물리적 특성을 분석하여 단열용 제품으로서의 가능성을 확인하고자 하였다. 연구결과 폐유리분말과 플라이애시를 사용한 경량 발포소재는 균일한 공극을 형성하며 발포하였고 경량이며 불연재료이므로 불연성능 요구되는 부위에 사용이 가능하다.