• 한국해양공학회지
• /
• 제22권5호
• /
• pp.94-99
• /
• 2008

Three types of salt resistant concrete beams reinforced with glass fiber reinforced polymer-ribbed bars (GFRP-ribbed bars) were selected, and their applicable properties were investigated with the goal of improving the problem of capacity deterioration in marine structures due to sea water corrosion. In this study, the structural behaviors were similar to RC beams in relation to the development of the strength and stiffness up to the generation of the initial crack. After the growth of this initial crack, the structural properties decreased owing to a sudden loss of bond strength. Also these beams showed the trends of brittle failure. As a result, it was confirmed that a GFS beam replaced with Fly Ash (20%) and Silica Fume (5%) has the best application as a marine structural element.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2001년도 추계학술대회(한국공작기계학회)
• /
• pp.298-303
• /
• 2001

Most of mechanical failures are caused by repeated loadings and therefore they are strongly related to fatigue. To avoid the failures caused by fatigue, determination of an optimal shape of a structure is one of the very important factors in the initial design stage. Shape optimization for a compact tension specimen in opening mode in fracture mechanics, was accomplished by the linear elastic fracture mechanics and the growth-strain method in this study. Also shape optimization for a cantilever beam in mixed mode was carried out by the same techniques. The linear elastic fracture mechanics was used to estimate stress intensity factors and fatigue lives. And the growth-strain method was used to optimize the shape of the initial shape of the specimens. From the results of the shape optimization, it was found that shapes of two types of specimens and a cantilever beam optimized by the growth-strain method prolong their fatigue lives very much. Therefore, it was verified that the growth-strain method is an appropriate technique for shape optimization of a structure having a crack.

• 터널과지하공간
• /
• 제2권2호
• /
• pp.251-264
• /
• 1992

In this study, the size effect in measuring the fracture toughness of rock was investigated using the ISRM Suggested Method for Fracture toughness using Chevron Bend Specimens. Total 58 specimens were prepared with 4 different diameters, 29, 42, 54, 68mm and center cut-chevron notch. In addition to this, to evaluated the effect of anisotropy of Jecheon granite, which is the sample for this study, core drilling direction was adjusted perpendicular(short transverse) and parallel(arrester) to the rift plane in the sample and the measured fracture toughness for each direction were compared. Important results obtained from this study are as follows. Level ll test condition is more adequate than l, because of low data scattering and precision and corrected fracture toughness of Jechoen granite measured and 2.2MPa{{{{ SQRT { m} }}}} for arrester direction with minimum initial crack length 0.7cm. From the relationship between core diameter and initial crack length presented in the ISRM testing method, the specimen diameter should be bigger than 47mm. The fracture toughnesses measured for arrester and short transverse directon show 10% difference. This is to the anisotropy of Jecheon granite possessing rift plane.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.667-670
• /
• 2005

This study is concerned with application of SWP-2H with performance which could be improved compressive strength, crack control of high strength concrete ranged from 35MPa to 70MPa. Expermental data showed that initial. behavior of SWP-2H added concrete had a similar tendency that of non-added concrete. As well crack resulted from autogeneous and drying shrinkage and compressive strength were well controled or elevated by application of SWP-2H.

• 한국해양공학회지
• /
• 제15권1호
• /
• pp.52-56
• /
• 2001

This study were looks at the effect of the initial cut length or stress concentration level, on the wave forms produced by crack propagation. The signals were collected, then classified visually for each type of sample. They were put into three classes according to their shapes in the time and frequency domain. Each class should domain signals which could be correlated to a certain micro-failure mechanism that occurs during the fatigue process. Classes of these signals compared, with each sample. To see if there were any classes common to the three samples. The fatigue test attempted to determine if the initial cut length has any influence on the type of signals.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.577-582
• /
• 2002

The solidification cracking susceptibilities of AI-Mg-Si alloy laser welds were assessed using the self-restraint tapered specimen crack test. The cracking susceptibility of 6061 and 6082 Al-Mg-Si alloy laser welds was substantially reduced when the filler wire containing high Si such as Al-12 wt.% Si (4047A) was used. The amount of eutectic was observed to affect the solidification cracking of Al-Mg-Si alloy laser welds. Abundant eutectic seems to heal the cracking and reduces the cracking susceptibility, while an initial increase in eutectic liquid leads to the increased cracking tendency.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.623-628
• /
• 2000

In this paper, the behavior for transfer girder of the upper-wall and lower-frame structures was studied by the nonlinear finite element analysis. It was analyzed and compared with the experimental results. Analysis results showed that failure modes were progressed by a initial diagonal crack in the shear span between the edges of the load and intermediate support plate. The nonlinear finite element analysis could predict deformation, principal stress, ultimate load and concrete crack. Also analysis results showed good agreement the test results.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1992년도 봄 학술발표회 논문집
• /
• pp.53-58
• /
• 1992

This research is related to the experimental investigation of the inelastic behavior of R/C columns with high strength concrete. A total of eight specimens have been tested with different span ratios, steel reinforcements and load applications. Through tests bending moments were applied incrementally while axial forces being kept constantly at 80 tons. Careful observation were given to initial crack formation, crack patterns and propagation paths. Comparative studies have been made on the load carrying capacity for R/C columns with high strength concrete versus normal strength concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1990년도 가을 학술발표회 논문집
• /
• pp.69-72
• /
• 1990

This research is related to the experimental investigation of the inelastic behavior of reinforced concrete columns. A total of 12 specimens have been cast with different span ratios, steel reinforcements and load applications. Through the tests axial forces have been kept constantly at 40 tons while the bending moments were applied incremently and careful observations were given to the initial crack formation, crack pattern and propagation.

• International Journal of Korean Welding Society
• /
• 제2권2호
• /
• pp.42-46
• /
• 2002

The solidification cracking susceptibilities of Al-Mg-Si alloy laser welds were assessed using the self-restraint tapered specimen crack test. The cracking susceptibility of 6061 and 6082 Al-Mg-Si alloy laser welds was substantially reduced when the filler wire containing high Si such as Al-12 wt.% Si (4047A) was used. The amount of eutectic was observed to affect the solidification cracking of Al-Mg-Si alloy laser welds. Abundant eutectic seems to heal the cracking and reduces the cracking susceptibility, while an initial increase in eutectic liquid leads to the increased cracking tendency.