• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.393-400
• /
• 2012

The characteristics of indium tin oxide (ITO) thin film deposited on polyethersulfone (PES) film by low temperature E beam has been studied for the flexible photovoltaic devices. It was found that the substrate temperature in the deposition process affected the crystallization behavior of ITO during the post low temperature annealing process. Higher substrate temperature resulted in the increase of crystallinity of annealed ITO. Consequently, the lowering of sheet resistivity and better transmittance were obtained. Crystallization of ITO during the annealing process was facilitated by using oxygen gas in the deposition process and resulted in the enhancement on sheet resistivity and transmittance of ITO. The surface roughness of PES film prohibited the crystallization of ITO during the annealing process and it caused the increase of sheet resistivity and the decrease of transmittance of ITO.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.11a
• /
• pp.302-305
• /
• 1995

ITO(indium tin oxide) that is both conductive in electricity and transparent to the visible ray is called transparent conducting thin film. Nowaday, according to the development of flat panel display such as LCD(Liquid Crystal display, EL(electolumine- scence display), PDP(plasma display panel), ECD(electrocromic display), the higher quality in the low temperature process has been asked to reduce the production cost and to have a good uniformity on a large substrate. In this study, we prepared indium tin oxide(ITO) by a cylindrical DC magnetron sputtering with Indium-tin (9:1) alloy target instead of indium-tin oxide target. To reduce the defact in ITO, the effect on ITO by varing the magnetic field intensity and the applied voltage ares studied. the resistivity of the film deposited in oxygen partial pressure of 5% and substrate temperature of 140$^{\circ}C$. is 1.6${\times}$10$\^$-1/$\Omega$$.$cm with 85% optical transmission in viaible ray.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.209-209
• /
• 2012

High-efficient transparent conductive oxide (TCO) film-embedding Si heterojunction solar cells were fabricated. An additional doping was not applied for heterojunction solar cells due to the spontaneous junction formation between TCO films and an n-type Si substrate. Three different TCO coatings were formed by sputtering method for an Al-doped ZnO (AZO) film, an indium-tin-oxide (ITO) film and double stacks of ITO/AZO films. An improved crystalline ITO film was grown on an AZO template upon hetero-epitaxial growth. This double TCO films-embedding Si heterojunction solar cell provided significantly enhanced efficiency of 9.23% as compared to the single TCO/Si devices. The effective arrangement of TCO films (ITO/AZO) provides benefits of a lower front contact resistance and a smaller band offset to Si leading enhanced photovoltaic performances. This demonstrates a potential scheme of the effective TCO film-embedding heterojunction Si solar cells.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.2
• /
• pp.77-80
• /
• 2010

Indium tin oxide (ITO) films with a 5 nm thick Au interlayer were prepared on glass substrates. The effects of the Au interlayer on the gas sensitivity for detecting methanol vapors were investigated at room temperature. The conductivity of the film sensor increased upon exposure to methanol vapor and the sensitivity also increased proportionally with the methanol vapor concentration. In terms of the sensitivity measurements, the ITO film sensor with an Au interlayer shows a higher sensitivity than that of the conventional ITO film sensor. This approach is promising in gaining improvement in the performance of ITO gas sensors used for the detection of methanol vapor at room temperature.

• Journal of the Korean Vacuum Society
• /
• v.9 no.1
• /
• pp.30-35
• /
• 2000

Indium-Tin Oxide (ITO) thin films were deposited on the commercial glass substrate by rf-magnetron sputtering. The ITO films with the thickness of 2,000~2,400 $\AA$ were prepared by changing the oxygen partial pressures of 2, 3, and 5%, as well as by changing the substrate temperature of $300^{\circ}C$ and $500^{\circ}C$. spectrophotometer, XRD, SEM, AFM, 4-point probe and Hall effect system were employed to characterize the ITO films. The optimum deposition conditions were the substrate temperature of $500^{\circ}C$ and oxygen partial pressure of 2-3%. At theses conditions, the ITO film showed the transmittance of 91%, the resistivity of $5.4\times10^{-3}\Omega$cm, the carrier concentration of $1.0\times10^{19}\textrm{cm}^{-3}$, and the carrier mobility of 150$\textrm{cm}^2$/Vsec. In XRD spectra, the (222) and (400) $In_2O_3$ planes were dominant under the optimum deposition conditions When the substrate was cleaned only by the method of ultrasonic cleaning without both pre-annealing and chemical treatment of the substrate, the ITO film exhibited the transmittance of 86%, the carrier concentration of $5.4\times10^{19}\textrm{cm}^{-3}$ and the mobility of 24$\textrm{cm}^2$/Vsec.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.516-519
• /
• 2011

Indium tin oxide (ITO) coatings were made using an ITO slurry and an ITO sol. This was achieved by dispersing nanosized ITO powder in a mixed solvent without any dispersant and developing an adhesive ITO sol from indium acetate and tin tetrachloride in a mixture of DMF and n-butanol. Coating was carried out in one step by spin coating an ITO slurry, which was then followed by an ITO sol over it. Here, the sol penetrates into the nano ITO particle layers to make them adhere to each other as well as to a glass substrate. This is then followed by sintering at 500$^{\circ}C$ for 1 h to produce a uniform film consisting of ITO particles of about 50 nm and 10 nm. ITO films were obtained with sheet resistances from 450 to 1500 ohm/${\Box}$ by varying spin speed and concentration. Transmittance is higher than 90% at 550 nm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.367-367
• /
• 2013

Commercial applications of indium tin oxide (ITO) can be separated into two useful areas. As it is perceived to bear electrical properties and optical transparency at once, its chance to apply to promising fields, usually for an optical device, gets greater in the passing time. ITO is one of the transparent conducting oxides (TCO), and required to carry the relative resistance less than $10^{-3}{\Omega}$/cm and transmittances over 80 % in the visible wavelength of light. Because ITO has considerable refractive index, there exist applications for anti-reflection coatings. Anti-reflection properties require gradual change in refractive index from films to air. Such changes are obtained from film density or nano-clustered fractional void. Glancing angle deposition (GLAD) method is a well known process for adjusting nanostructure of the films. From its shadowing effects, GLAD helps to deposit well-controlled porous films effectively. In this study, we are comparing the reference sample to samples coated with controlled ITO multilayer accumulated by an e-beam evaporation system. At first, the single ITO layer samples are prepared to decide refractive index with ellipsometry. Afterwards, ITO multilayer samples are fabricated and fitted by multilayer ellipsometric model based on single layer data. The structural properties were measured by using atomic force microscopy (AFM), and by scanning X-ray diffraction (XRD) measurements. The ellipsometry was used to determine refractive indices and extinction coefficient. The optical transmittance of the film was investigated by using an ultraviolet-visible (UV-Vis) spectrophotometer.

• Journal of Sensor Science and Technology
• /
• v.16 no.3
• /
• pp.229-233
• /
• 2007

The indium tin oxide (ITO) films were deposited on CR39 substrate using DC magnetron sputtering. The ITO thin films deposited at room temperature because CR39 substrate its glass-transition temperature is $130^{\circ}C$. The ITO thin films used bottom and top electrode and for organic thin film transparent transistors (OTFTs). The ITO thin film electrodes electrical properties and optical transparency properties in the visible wavelength range (300-800 nm) strongly dependent on volume of oxygen percent. For the optimum resistivity and transparency of the ITO thin film electrode achieved with a 75 W plasma power, 10 % volume of oxygen and a 27 nm/min deposition rate. Above 85 % transparency in the visible wavelength range (300-800 nm) measured without post annealing process and a low resistivity value $9.83{\times}10^{-4}{\Omega}cm$ was measured thickness of 300 nm. All fabrication process of ITO thin films did not exceed $80^{\circ}C$.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.2
• /
• pp.59-62
• /
• 2013

At an infra-red (IR) wavelength of 1,064 nm, a diode-pumped Q-switched $Nd:YVO_4$ laser was used for the direct patterning of various transparent conductive oxide (TCO) thin films on glass substrate. With various laser beam conditions, the laser ablation results showed that the indium tin oxide (ITO) film was removed completely. In contrast, zinc oxide (ZnO) film was not etched for any laser beam conditions and indium gallium zinc oxide (IGZO) was only ablated with a low scanning speed. The difference in laser ablation is thought to be due to the crystal structures and the coefficient of thermal expansion (CTE) of ITO, IGZO, and ZnO. The width of the laser-patterned grooves was dependent on the film materials, the repetition rate, and the scanning speed of the laser beam.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1411-1413
• /
• 1997

The thin film that is electrically conductive and optically transparent is called conductive transparent thin film. ITO(Indium-Tin Oxide) which is a kind of conductive transparent thin film has been widely used in solar cell, transparent electrical heater, selective optical filter, FDP(Flat Display Panel) such as LCD (Liquid Crystal Display), PDP(Plasma Display Panel) and so on. Especially in PDP, ITO films is used as a transparent electrode in order to maintain discharge and decrease consumption power through the improvement of cell structure. In this study, we prepared ITO by reactive r.f. sputtering with indium-tin(Sn wt 10%) alloy target instead of indium-tin oxide target. The ITO films deposited at low temperature $150^{\circ}C$ and 8% $O_2$ partial pressure showed about $3.6{\Omega}/{\square}$. At the end of firing, the resistance of ITO was decreased, the optical transparence was improved above 90%.