The purpose of this study was to evaluate the microtensile bond strength (${\mu}TBS$), failure modes and bonding interfaces of self-etching and three self-adhesive resin cements to dentin and indirect composite resin. Cylindrical composite blocks (Tescera, Bisco Inc.) were luted with resin cements (PA: Panavia F 2.0, Kuraray Medical Inc., RE: RelyX Unicem Clicker, 3M ESPE., MA: Maxem, Kerr Co., BI: BisCem, Bisco Inc.) on the prepared occlusal dentin surfaces of 20 extracted molars. After storage in distilled water for 24 h, $1.0\;mm\;{\times}\;1.0\;mm$ composite-dentin beams were prepared. ${\mu}TBS$ was tested at a cross-head speed of 0.5 mm/min. Data were analyzed with one-way ANOVA and Tukey's HSD test. Dentin sides of all fractured specimens and interfaces of resin cements-dentin or resin cements-composite were examined at FESEM (Field Emission-Scanning Electron Microscope). In conclusion, PA and RE showed higher bond strength and closer adaptation than MA and BI when indirect composite blocks were luted to dentin using a self-etching and three self-adhesive resin cements.

• Restorative Dentistry and Endodontics
• /
• v.43 no.4
• /
• pp.40.1-40.10
• /
• 2018

Objectives: This study evaluated the microtensile bond strength (${\mu}TBS$) of polymer-ceramic and indirect composite resin with 3 classes of resin cements. Materials and Methods: Two computer-aided design/computer-aided manufacturing (CAD/CAM)-fabricated polymer-ceramics (Enamic [ENA; Vita] and Lava Ultimate [LAV; 3M ESPE]) and a laboratory indirect composite resin (Gradia [GRA; GC Corp.]) were equally divided into 6 groups (n = 18) with 3 classes of resin cements: Variolink N (VAR; Vivadent), RelyX U200 (RXU; 3M ESPE), and Panavia F2 (PAN; Kuraray). The ${\mu}TBS$ values were compared between groups by 2-way analysis of variance and the post hoc Tamhane test (${\alpha}=0.05$). Results: Restorative materials and resin cements significantly influenced ${\mu}TBS$ (p < 0.05). In the GRA group, the highest ${\mu}TBS$ was found with RXU ($27.40{\pm}5.39N$) and the lowest with VAR ($13.54{\pm}6.04N$) (p < 0.05). Similar trends were observed in the ENA group. In the LAV group, the highest ${\mu}TBS$ was observed with VAR ($27.45{\pm}5.84N$) and the lowest with PAN ($10.67{\pm}4.37N$) (p < 0.05). PAN had comparable results to those of ENA and GRA, whereas the ${\mu}TBS$ values were significantly lower with LAV (p = 0.001). The highest bond strength of RXU was found with GRA ($27.40{\pm}5.39N$, p = 0.001). PAN showed the lowest ${\mu}TBS$ with LAV ($10.67{\pm}4.37N$; p < 0.001). Conclusions: When applied according to the manufacturers' recommendations, the ${\mu}TBS$ of polymer-ceramic CAD/CAM materials and indirect composites is influenced by the luting cements.

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.1
• /
• pp.27-32
• /
• 2013

Purpose: The aims of this study were to evaluate the effect of a resin coating on the shear bond strength of indirect composite restoration bonded to dentin with a self adhesive resin cement and to compare the shear bond strength with that of a conventional resin cement. Materials and methods: The occlusal enamels of thirty six extracted noncarious human molars were removed until the dentin flat surfaces of the teeth were exposed. Then, they were divided into 3 groups. The dentin surfaces of group 1 and 3 were left without any conditioning, while the dentin surfaces of group 2 were resin-coated with Clearfil SE bond and a flowable resin composite, Metafil Flo. After all specimens were temporized for 24 hours, indirect composite resin blocks fabricated by Tescera were bonded to dentins by Unicem for group 1 and 2, and by Panavia F for group 3. After 48 hours of water storage, shear bond strengths were measured. The data was analyzed with one-way analysis of variance and multiple comparison test (Tukey method). Results: The shear bond strengths of Unicem applied to resin coated dentin surfaces were significantly higher than those of Unicem and Panavia F used to uncoated dentin surfaces (P<.0001). Conclusion: Application of a resin coating to the dentin surface significantly improved the shear bonding strength of a self adhesive resin cement in indirect restoration.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.593-593
• /
• 2001

Esthetic restoration techniques can be categorized into "Direct techniques" consist only of intraoral procedures and "Indirect techniques" include intraoral as well as extraoral laboratory steps. Those made extraorally exhibit generally enhanced esthetic potential and anatomy and better hardness and wear resistance, indirect esthetic restorations numerously applied in contemporary dentistry. Indirect restorative materials can be divided into two categories; composite resin-based materials and ceramic-based materials. These materials shows various were resistance, modulus of elasticity, repair postenital, chemical stability, and different laboratory procedures. In this session, benefit of indirect techinques, case selection of this kind of restorations, and material characteristics and fabrication produre of those materials will ber reviewed; Targis, Sculpture, Belleglass, and Post-curing of restorative composite resins in resin-based materials; Dicor, Empress, Cerec, Celay, and conventional firing porcelain in ceramic based materials.

• The Journal of Advanced Prosthodontics
• /
• v.11 no.4
• /
• pp.223-231
• /
• 2019

PURPOSE. The purpose of this study was to evaluate the shear bond strength (SBS) of an indirect resin composite (IRC) to the various resin matrix ceramic (RMC) blocks using different surface treatments. MATERIALS AND METHODS. Ninety-nine cubic RMC specimens consisting of a resin nanoceramic (RNC), a polymer-infiltrated hybrid ceramic (PIHC), and a flexible hybrid ceramic (FHC) were divided randomly into three surface treatment subgroups (n = 11). In the experimental groups, untreated (Cnt), tribochemical silica coating (Tbc), and Neodymium-Doped Yttrium Aluminum Garnet (Nd:YAG) laser irradiation (Lsr) with 3 W (150 mJ/pulse, 20 Hz for 20 sec.) were used as surface treatments. An indirect composite resin (IRC) was layered with a disc-shape mold ($2{\times}3mm$) onto the treated-ceramic surfaces and the specimens submitted to thermal cycling (6000 cycles, $5-55^{\circ}C$). The SBS test of specimens was performed using a universal testing machine and the specimens were examined with a scanning electron microscope to determine the failure mode. Data were statistically analyzed with two-way analysis of variance (ANOVA) and Tukey HSD test (${\alpha}=.05$). RESULTS. According to the two-way ANOVA, only the surface treatment parameter was statistically significant (P<.05) on the SBS of IRC to RMC. The SBS values of Lsr-applied RMC groups were significantly higher than Cnt groups for each RMC material, (P<.05). Significant differences were also determined between Tbc surface treatment applied and untreated (Cnt) PIHC materials (P=.039). CONCLUSION. For promoting a reliable bond strength during characterization of RMC with IRC, Nd:YAG laser or Tbc surface treatment technique should be used, putting in consideration the microstructure and composition of RMC materials and appropriate parameters for each material.

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.22 no.1
• /
• pp.4-8
• /
• 2013

This clinical report shows the importance of selecting appropriate materials in fabricating laminate veneer restorations. Such cases should be carefully selected to ensure bonding durability, providing consistently reliable prognosis.

• Restorative Dentistry and Endodontics
• /
• v.22 no.1
• /
• pp.334-346
• /
• 1997

Incidence of using esthetic composite resin in the posterior area is increasing but there were lots of inconsistent reports about their microleakage and marginal adaptation. The purpose of this study was to evaluate the differences of microleakage and marginal adaptation according to restorative techniques. 30 cavities with enamel gingival margin were prepared and restored with 3 types of composite resin [Z-100($Scotchbond^{TM}$ MP), AELITEFIL ($Onestep^{TM}$), Her culite XRV(Fuji BOND LC)] in direct technique and another 30 cavities were restored with preformed CR inlays and 3 different modern resin and resin-modified GI cements (Superbond C&B, Choice, Fuji Duet). Samples were chemically stressed in 75% ethanol for 24 hours and were thermocycled (5-$55^{\circ}C$(500 times. The degree of microleakage through proximal and gingival margins was examined by 1 % MB dye and the degree of marginal adaptation by examining the margins via SEM. The following results were obtained ; 1. In direct groups, Herculite XRV [Fuji BOND LC, 35.13 (15.50) %] group showed statistically different, less microleakage than Z-100 [$Scotchbond^{TM}$ MP, 72.91 (16.91 %] group and AELITEFIL [One-step, 93.73 (13.66) %] group (p<0.05). 2. In indirect groups, the degree of microleakage in Mean(S.D.) were: Super bond C & B [39.00 (24.35) %], Choice [57.19 (33.80) %], Fuji Duet [58.22 (40.36) %]. But there was no significant difference. 3. There was no significant difference between resin cement and resin-modified GI cement. 4. There were gaps at the interface with the tooth structure, but no gap was seen at the interface with restoration in all specimens. 5. In direct groups, Herculite XRV(Fuji BOND LC) group made little gap compared with other groups, but 40-$50{\mu}m$ thickness of bonding agent, Fuji BOND LC, looked like a cement used in indirect technique. 6. All indirect groups showed a variety of cement thickness, from less than $20{\mu}m$ to over $100{\mu}m$ and that dimension of buccal/lingual margin was less than that of gingival margin.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.1
• /
• pp.21-33
• /
• 2007

Statement of problem: The esthetic component of dental care has become increasingly more important, while new tooth-colored materials are continually marketed. Various new indirect composite materials have been developed with required advantages. The most recent development in the indirect composites has been the introduction of the second-generation laboratory composite or poly-glass materials. They are processed by different laboratory techniques based on combinations of heat, pressure, vacuum and light polymerization. Although, second generation products became available in 1995, their characteristics and clinical performance have not been adequately investigated. Purpose: The aim of this study was to measure the mechanical properties of the second generation indirect resin system and compare these with an existing universal direct composite resin. Material and method: In this study four indirect composite material (Adoro LC, BelleGlass HP, Tescera, Synfony) were tested for flexural strength, wear resistance, hardness and their degree of conversion against Z250, a light cure direct composite. Results: Within the limitations of this study, the following conclusions were drawn: 1. From the abrasion wear result, Adoro showed the least volume loss while Synfony showed the greatest volume loss. Z250 and BelleGlass HP didn't show significant difference (p>0.05), but they showed significant difference with other groups (p<0.05). From the attrition wear, BelleGlass HP showed the least volume loss and it didn’t show significant difference with Tescera (p>0.05). While Synfony showed the greatest volume loss that it showed significant difference with other groups (p>0.05). 2. Mean values of flexural strength by means of three point bending test was in the order of Z250, Adoro, Belleglass HP, Tescera and Synfony. Mean elastic modulus was in the order of Z250, BelleGlass HP, Tescera, Adoro and Synfony. 3. The result of Vicker‘s microhardness value showed that significantly higher value in Z250 (p<0.05), and is in the order of BelleGlass HP, Tescera, Adoro and Synfony. 4. The degree of conversion measured by FT-IR showed significantly higher value in BelleGlass HP (p<0.05), and is in the order of Adoro, Synfony, Tescera and Z250. Conclusion: Significant differences were found in the flexural strength, wear resistance, hardness and their degree of conversion.

• Journal of Technologic Dentistry
• /
• v.30 no.2
• /
• pp.79-86
• /
• 2008

The purpose of this study was to investigate the effect retention element formed by metal surface treatment method on the bond strength of indirect composite resin and metal. The metal specimens were cast from Ni-Cr alloy($Rexillium^{(R)}$ III). They were divided into 5 groups by applied retention element: $50{\mu}m$ aluminium oxide sandblasting group, $250{\mu}m$ aluminium oxide sandblasting group, 0.2mm retention crystal group, 10% $H_{2}SO_{4}$ solution etching group, $110{\mu}m$ $Rocatec^{TM}$ Plus system group. Total 50 metal specimens were veneered with Sinfony indirect composite resin system. Specimens were tested for shear bond strength on an Instron universal testing machine and fracture mode of fractured specimens were analyzed by SEM and EDS. 1. 0.2 mm retention crystals were most effective in improving the resin-metal shear bond strength (p<0.05). 2. Sandblasting by $250{\mu}m$ aluminium oxide were more effective than sandblasting by $50{\mu}m$ aluminium oxide in improving the resin-metal shear bond strength(p<0.05). 3. Fracture mode of resin-metal fractured surface were cohesive failure mode in 0.2mm retention crystal, mixed failure mode in sandblasted specimens, etched specimens and the specimens sandblasted with $110{\mu}m$ $Rocatec^{TM}$ Plus system.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.611-620
• /
• 2007

Statement of problem: Second-generation indirect composite resins have been improved flexural strength, compressive strength, hydrolytic degradation resistance, wear resistance compared to first-generation indirect composite resins, but there are still some problems as hydrolysis and low wear resistance. Some manufacturers claim that wear resistance of their materials has been improved, but little independent study has been published on wear properties of these materials and the properties specified in the advertising materials are largely derived from in-house or contracted testing. Purpose: This study was to evaluate the wear of indirect composite resins (SR Adore, Sinfony, Tescera ATL) and gold alloy against the human enamel. Material and method: Extracted human incisors and premolars were sectioned to $2{\times}2{\times}2mm$ cube and embedded in the clear resin and formed conical shaped antagonist to fit the jig of pin-on-disk tribometer. Total 20 antagonists were stored in distilled water. Five disk samples, 24mm in diameter and 1.5mm thick, were made for each of three groups of indirect composite resins and gold alloy group, and polished to #2,000 SiC paper on auto-polishing machine. Disk specimens were tested for wear against enamel antagonists. Wear test were conducted in distilled water using a pin-on-disk tribometer under condition (sliding speed 200rpm contact load 24N, sliding distance 160m). The wear of the enamel was determined by weighing the enamel antagonist before and after test, and the weight was converted to volumes by average density. The wear tracks were analyzed by scanning electron microscopy and surface profilometer to elucidate the wear mechanisms. Statistical analysis of the enamel wear volume, wear track depth and wear tract width of disk specimens were accomplished with one-way ANOVA and the means were compared for significant differences with Scheffe's test. Results: 1. The enamel wear was most in gold alloy, but there were no statistically significant differences among all the groups (P>.05). 2. In indirect composite resin groups, the group to make the most shallow depth of wear tract was Sinfony, followed by Tescera ATL, SR Adoro (P<.05). Gold alloy was shallower than Sinfony, but there was no statistically significant difference between Sinfony and gold alloy (P>.05). 3. The width of wear tract of SR Adore was larger than the other groups (P<.05), and there were no statistically significant differences among the other groups (P>.05). 4. SEM analysis revealed that Sinfony and gold alloy showed less wear scars after test, Tescera ATL showed more wear scars and SR Adore showed the most. Conclusion: Within the limits of this study, Sinfony and gold alloy showed the least wear rates and showed similar wear patterns.