• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.3
• /
• pp.481-490
• /
• 2005

The aim of this study was to investigate the relationship between the C-factor and shrinkage strain values of composite resin and examine the strain values in different incremental filling techniques. The strain gauge method was used for measurement of polymerization shrinkge strain. Experiment was divided two step. In a first experiment, we compared with strain value in three different depth (2mm, 3mm, 4mm) and microhardness of each samples after 24hours were measured. In a second experiment, we examined the strain values in five different filling techniques(Group 1: bulk filling, Group 2: oblique incremental filling, Group 3: horizontal incremental filling, Group 4: vertical incremental filling, Group 5: lining of flowable resin and bulk filling) The results of the present study can be summarized as follows: 1. Composite resin in acrylic molds showed the initial expansion at the early phase of polymerization. 2. Contraction stress was not revealed significant difference between depth of 2mm and 3mm(P>0.05). 3. Contraction stress in sample of 4mm was showed the lowest value(P<0.05). 4. Microhardness of specimen was revealed more difference between upper and lower surface in depth of 4mm than 2 and 3mm(P<0.05). 5. Lining of flowable resin and bulk filling (Group 5) was showed the lowest contraction stress, Group 2 and 3 was showed the highest contraction stress(P<0.05). On the basis above results, the stress that result from the polymerization shrinkage, when incremental curing techniques are used, showed that there is no advantage in incremental placement and curing.

• Geomechanics and Engineering
• /
• v.15 no.1
• /
• pp.695-710
• /
• 2018

Formation of a soil plug in an open-ended pile is a very important factor in determining the pile behavior both during driving and during static loading. The degree of soil plugging can be represented by the incremental filling ratio (IFR) which is defined as the change in the plug length to the change of the pile embedment length. The experimental tests carried out in this research contain 138 tests that are divided as follows: 36 tests for single pile, 36 tests for pile group ($2{\times}1$), 36 tests for pile group ($2{\times}2$) and 30 pile group ($2{\times}3$). All tubular piles were tested using the poorly graded sand from the city of Karbala in Iraq. The sand was prepared at three different densities using a raining technique. Different parameters are considered such as method of installation, relative density, removal of soil plug with respect to length of plug and pile length to diameter ratio. The soil plug is removed using a new device which is manufactured to remove the soil column inside open pipe piles group installed using driving and pressing device. The principle of soil plug removal depends on suction of sand inside the pile. It was concluded that the incremental filling ratio (IFR) is changed with the changing of soil state and method of installation. For driven pipe pile group, the average IFR for piles in loose is 18% and 19.5% for L/D=12 and 15, respectively, while the average of IFR for driven piles in dense sand is 30% and 20% for L/D=12 and L/D=15 respectively. For pressed method of pile installation, the average IFR for group is zero for loose and medium sand and about 5% for dense sand. The group capacity increases with the increase of IFR. For driven pile with length of 450 mm, the average IFR % is about 30.3% in dense sand, 14% in medium and 18.3% for loose sand while when the length of pile is 300 mm, the percentage equals to 20%, 17% and 19.5%, respectively.

• Restorative Dentistry and Endodontics
• /
• v.34 no.4
• /
• pp.350-355
• /
• 2009

Bond strength depends on characteristics of bonding surface and restorative technique. The majority of studies dealing with dentin bond strength were carried out on flat bonding surface, therefore, difference of bond strength between axial wall and pulpal wall is not clear yet. This study evaluated bonding difference between cavity walls in class I composite resin restoration with different filling techniques. Twenty extracted caries-free human third molars were used. Cavities were prepared in 6 ${\times}$4 ${\times}$3 mm box-type and divided into four groups according to filling technique and bonding surface: Group I; bulk filling - pulpal wall, Group II; bulk filling - axial wall, Group III; incremental filling - pulpal wall, Group IV; incremental filling - axial wall. Cavities were filled with Filtek $Z250^{(R)}$(3M/ESPE., USA) and Clearfill SE $bond^{(R)}$(Kuraray, Japan). After 24 hour-storage in $37^{\circ}C$water, the resin bonded teeth were sectioned bucco-lingualy at the center of cavity. Specimens were vertically sectioned into 1.0 ${\times}$1.0 mm thick serial sticks perpendicular to the bond surface using a low-speed diamond saw (Accutom 50, Struers, Copenhagen, Denmark) under water cooling. The trimmed specimens were then attached to the testing device and in turn, was placed in a universal testing machine (EZ test, Shimadzu Co., Kyoto, Japan) for micro-tensile testing at a cross-head speed of 1 mm/min. The results obtained were statistically analyzed using 2-way ANOVA and t-test at a significance level of 95%. The results were as follows: 1. There was no significant difference between bulk filling and incremental filling. 2. There was no significant difference between pulpal wall and axial wall, either. Within the limit of this study, it was concluded that microtensile bond strength was not affected by the filling technique and the site of cavity walls.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.3
• /
• pp.337-344
• /
• 1989

The upper bound elemental technique (UBET) is used to simulate the bulk flow characteristics in axisymmetric closed die forging process. Internal flow inside the cavity is predicted using a kinematically admissible velocity field that minimizes the rate of energy consumption. Application of the technique includes an assessment of the formation of flash and of degree of filling in rib-web type cavity using billets with various aspect rations. The technique considering bulging effect is performed in an incremental manner. The results of simulation show how it can be used for the prediction of forging load, metal flow, and free surface profile. The experiments are carried out with plasticine. There are good agreements in forging load and material flow in cavity between the simulation and experiment. The developed program using UBET can be effectively applied to the various forging problems.

• Restorative Dentistry and Endodontics
• /
• v.26 no.1
• /
• pp.16-22
• /
• 2001

The purpose of this study was to evaluate the marginal microleakage of condensable composite resin restorations according to flowable resin lining of internal cavity wall. The eighty extracted human molar teeth without caries and/or restorations are used The experimental teeth were randomly assigned into four groups of ten teeth each. Eighty caries-free extracted human molars were used in this study. The conventional class II cavities (box-shaped on mesial and distal surface, faciolingual width : 3mm, gingival wall depth : 1.5mm) were prepared 1mm below cementoenamel junction with a # 701 carbide bur. The teeth were divided into four groups, and then each group were subdivided into A & B group according to flowable resin & compomer lining ; Group 1-A : Tetric Ceram filling, Group 1-B : Tetric Flow lining and Tetric Ceram filling, Group 2-A Ariston pHc filling, Group 2-B : Tetric Flow lining and Ariston pHc filing, Group 3-A SureFil filling, Group 3-B : Dyract Flow lining and SureFil filling, Group 4-A : Pyramid filling, Group 4-B : Aeliteflo lining and Pyramid filling. To simulate as closely as possible the clinical situation during retoration placement, a "restoration template" was fabricated, and the condensable resin was filled using a three-sited light-curing incremental technique. All the materials used were applied according to the manufacturers' instructions. The specimens were stored in the 100% humidity for 7 days prior to thermocycling (100 thermal cycles of 5~55$^{\circ}C$ water with a 30-second dwell time) The specimens were immersed in 2% metyleneblue dye for 24 hours, and then embedded in transparent acrylic resin and sectioned mesiodistally with diamond wheel saw. The degree of marginal leakage was scored under stereomicroscope ($\times$20) and the data were analyzed by Kruskal-Wallis test and Wilcoxon signed ranks test. The results were as follows : 1. In the gingival margins of all the group, microleakage of subgroup B was less than subgroup A. 2. In the group 1, 2, 4, there was significant differences between subgroup A and B (p<0.05), but in the group 3, there was not significant different between group 3-A (SureFil) and group 3-B (Dyract flow/SureFil) (p>0.05). 3. In the subgroup A and B, there was significant different between all group except group 4 of subgroup A. From the results above, it was suggested that the cavity lining of flowable resin and flowable compomer in condensable resin restoration decrease microleakage at gingival margin, and does improve their ability to seal the gingival margin of class II preparation.

• Restorative Dentistry and Endodontics
• /
• v.26 no.6
• /
• pp.492-498
• /
• 2001

The purpose of this study was to evaluate four different composite resins in vitro for microleakage in Class II box type restorations that have gingival margins apical to the cementoenamel junction. Forty caries free extracted human molars were used in this study. The Class II cavities were prepared 1.0mm below cementoenamel junction with a #701 carbide bur. The teeth were randomly divided into four groups, each group comprising 20 treated cavities according to adhesives and filling materials ; Group 1: Scotchbond Multipurpose/Z 100. Group 2: Ariston Liner/Ariston pHc, Group 3: One Step/Pyramid, Group 4: Prime & Bond NT/SureFil. To simulate the clinical situation during restoration placement, a restoration template was fabricated and composite resin was filled using a three sited light-curing incremental technique. The specimens were stored in the 100% humidity for 7 days prior to thermocycling. The specimens were immersed in 2% methylene blue dye solution for 24 hours and then embeded in transparent acrylic resin and sectioned mesiodistally with a diamond wheel saw. The degree of marginal leakage was scored under the stereomicroscope($\times$20) and the data were analyzed by Kruskal Wallis test and Mann Whitney test. (omitted)

• Restorative Dentistry and Endodontics
• /
• v.24 no.2
• /
• pp.346-355
• /
• 1999

To evaluate the micro leakage of compomer, 4 materials were divided into 4 groups of 15 cavities each.(Group 1: Z-100, Group 2: Dyarct AP, Group 3: Fuji II LC, Group 4: Compoglass) After the class II cavities were prepared using carbide bur No. 553, all specimen were restored by incremental filling technique. In group 3, Z-100 was filled with a base of a light curing glass-ionomer. After 7 days, all specimens were thermocycled between $5^{\circ}C$ and $55^{\circ}C$ for 500 cycles, followed by placement in 50% silver nitrate dye for 2 hours at $37^{\circ}C$. After rinsed in distilled water, these teeth were immersed in photodeveloping solution and exposed to fluorescent light for 6 hours. Teeth were then washed in distilled water to remove the photodeveloping solution, sectioned mesio-distally and evaluated. The results were as follows : 1. In the cervical portion, there was significant difference between Fuji II LC and other groups(Z-100, Dyract AP, Compoglass), Fuji II LC had the least value.(p<0.05) 2. In the cervical portion, there was not significant difference among Dyract AP, Z-100 and Compoglass. 3. In the occlusal portion, there was not significant difference among Dyract AP, Z-100 and Compoglass. From the results above, In enamel, microleakage of compomer such as Dyract AP and Compoglass resemble to that of composite resin. It is thought that it is due to characteristics of composite resin portion of compomer. But in dentin, microleakage of compomer is higher than that of resin modified glass ionomer cement, it is thought that in compomer, acid-base reaction is not developed with dentin.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.2
• /
• pp.233-243
• /
• 2006

The aim of this study was to investigate the relationship between the C-factor and shrinkage strain values of composite resin and examine the strain values in different incremental filling techniques. Experiment consisted two aims. First, we compared with strain value in two different C-factors(3.7 and 1.0). Second, we examined the strain values in three different filling techniques. The results of the present study can be summarized as follows : 1. High C-factor groups showed higher contraction stress values than low C-factor groups at 900 sec after polymerization. 2. Hybrid resin showed higher contraction stress values than flowable resin in high C-factor cavities. But contraction stress was not revealed significant difference between hybrid resin and flowable resin in low C-factor cavities (P>0.05). 3. Bulk felling with hybrid resin(Group 1) showed high contraction stress and lining with flowable resin followed hybrid resin (Group 5) showed lower contraction stress. 4. Contraction stress were increased during 900 sec after polymerization in high C-factor groups but decreased gradually after 900 sec. 5. Low C-factor groups showed tight marginal seal between resin and cavity wall but high C-factor groups showed gaps formed between resin and cavity wall in part. On the basis above results, layering techniques in high C-factor cavity showed advantages in reducing contraction stress and gap formation between cavity wall and resin restoration.