• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.492-497
• /
• 2017

In this study, we investigated the effect of thermal aging on mechanical characteristics of Inconel 600 nickel-based alloy. The thermal aging was conducted up to 1000 hours at an atmosphere of $650^{\circ}C$. The microstructure of thermally aged specimens was investigated by an optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). In addition, tensile test (strain rate: 2 mm/min) and micro Vickers hardness test were conducted to evaluate mechanical properties with time. As a result of the experiment, Cr-rich carbide continuously precipitated during thermal aging, leading to the change of the mechanical characteristics and fracture mode. With the increase of aging time, tensile strength, yield strength, and hardness gradually decreased. The fracture mode changed from ductile to brittle with the increase of grain boundary carbide.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.115-121
• /
• 2001

The wear test has been performed to evaluate the wear mechanism of steam generator (SG) tube materials against ferritic stainless steel in water environment. The wear rates of SG tube materials depend on the change of mechanical properties between contact surfaces during wear test. From the subsurface hardness test, Inconel 690 is more work-hardened than Inconel 600 even though these materials have similar hardness values before the wear test. Main cause is due to the difference of stacking fault energy with the chromium content. In water environment, wear mechanism is closely related with the continuous formation and fracture of deformation layers at the contact surfaces.

• Journal of Welding and Joining
• /
• v.24 no.3
• /
• pp.49-54
• /
• 2006

The Plasma Transferred Arc (PTA) overlaying method is lately introduced as one of the most useful surface modification method of the engine component. In this paper, the characteristics of the Co-base and Ni-base super alloy overlay layers by PTA method were investigated through the metallurgical, abrasive and cavitation erosion test. Experimental results showed that the abrasive wear resistance of the Co-base Stellite 6 overlayer was the most superior and followed in order of Nimonic 80A, Inconel 625 and Inconel 718. However, the cavitation erosion characteristic of the Stellite 6 overlayer was the most inferior and it was better in order of Inconel 625, Inconel 718 and Nimonic 80A.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.612-615
• /
• 2005

Low cycle fatigue tests are performed on the Incollel 617 that be used fur a hot gas casing. The relation between strain energy density and numbers of cycles to failure is examined in order to predict the low cycle fatigue life of Inconel 617. The life predicted by the strain energy method is found to coincide with experimental data and results obtained from the Coffin-Mansun method. Also the cyclic behavior of Inconel 617 is characterized by cyclic hardening with increasing number of cycle at room temperature.

• Nuclear Engineering and Technology
• /
• v.34 no.2
• /
• pp.132-141
• /
• 2002

The effects of microstructure on fretting wear were investigated in Inconel 690 tube. The microstructure observation indicated that the solution annealing temperature and time affected the grain size of the Inconel 690 tubes. The carbide morphology, along grain boundaries, was mainly affected by thermal treatment time and temperature. The wear test results showed that specimens with larger grain size and with coarse carbides along grain boundaries had better wear resistance. Cracks were found in specimens with carbides along the grain boundary, while few cracks were found in carbide free specimens. It seemed that the carbides on grain boundary assisted crack formation and propagation in carbide containing specimens. On the other hand, the micro-hardness of specimen did not have a major role in fretting wear. It could be inferred from the SEM images of worn surfaces that the main wear mechanism of carbide containing specimen was delamination, while that of carbide free specimen was abrasion.

• Nuclear Engineering and Technology
• /
• v.54 no.10
• /
• pp.3778-3787
• /
• 2022

The stress-assisted oxidation behaviour of Inconel 52 M/316 austenitic stainless-steel (SS) dissimilar weld joints (DMWJ) in a simulated pressurised water reactor environment was investigated. A corrosion galvanic couple formed between the Inconel 52 M and 316 SS due to differences in their nonferrous metal content. The electric field from the corrosion couple attracted metal cations (e.g. Fe²⁺, Cr³⁺) to the Inconel 52 M that were deposited as FeCr₂O₄. An additional corrosion galvanic couple was generated due to variations in the plastic deformation of the DMWJ. The superposition of electric fields from the different couples resulted in ridge-like oxide depositions in the fusion zone.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.11a
• /
• pp.116-116
• /
• 1994

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.90-90
• /
• 2003

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.11a
• /
• pp.22-22
• /
• 1993

• Proceedings of the KWS Conference
• /
• 1994.05a
• /
• pp.109-112
• /
• 1994