• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.7
• /
• pp.1051-1057
• /
• 2003

This study is about controlled impurities, which make metal alloys, especially AC4CH alloy that is made by restraining 0.2％ Fe and Aluminum to make a matrix material. A metal matrix composite is produced using the squeeze casting method. The first step in the squeeze casting method is to add some organic binder including aluminum borate whisker into the matrix. After the fabrication of a metal matrix composite, each is individually appended to an inanimate binder such as SiO$_2$, Al$_2$O$_3$, and TiO$_2$. Through experiments the mechanical property changes were investigated between the metal matrix composite and AC4CH alloy. This study proves the superiority of the mechanical property of a metal matrix composites over AC4CH according to the previous tests and results that were mentioned above. One excellent property of matrix material composites is the infiltrated TiO$_2$ reinforcement. This material is a good substitute for the existing materials that are used in the development of industries today.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.198-203
• /
• 2001

This study is about controlled impurities, which make metal alloys, especially AC4CH alloy that is made by restraining 0.2% Fe and Aluminum to make a matrix material. A metal matrix composite is produced using the squeeze casting method. The first step in the squeeze casting method is to add some organic binder including aluminum borate whisker into the matrix. After the fabrication of a metal matrix composite, each is individually appended to an inanimate binder such as $SiO_2,\;Al_2O_3$, and $TiO_2$. Through experiments the mechanical property changes were investigated between the metal matrix composite and AC4CH alloy. This study proves the superiority of the mechanical property of a metal matrix composites over AC4CH according to the previous tests and results that were mentioned above. One excellent property of matrix material composites is the infiltrated $TiO_2$ reinforcement. This material is a good substitute for the existing materials that are used in the development of industries today.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.61-66
• /
• 2003

In this paper, the effect of binder additive on the fracture toughness was metal matrix composite produced by squeeze casting method. In this study using the matrix is AC4CH and reinforcement used Aluminum borate whisker. Each MMC was produced by add inanimate binder ($SiO_2,\;Al2O_3,\;TiO_2$) to whiskers for increase the binding together of whiskers. Fracture toughness test were carry out in accordance with the ASTM E-399 standard test method, W=25mm, b=12.5mm CT(half size) specimen. However Base metal AC4CH was not meet the qualification of $P_m/P_Q<1.1$, so that test were performed $J_{IC}$ test. $K_{J_{IC}}$ value was measuring by $J_{IC}$ value change into $K_{IC}$. $J_{IC}$ test was carry out in accordance with the ASTM 1820.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.6
• /
• pp.171-177
• /
• 2002

Metal matrix composites had generated a lot of interest in recent times because of significant in specific properties, it was also highlighted as the material of frontier industry because strength, heat-resistant, corrosion-resistant and wear-resistant were superiored. In recent years, the study of metal matrix composite has increased by aluminum alloy. The study is based on the tribological properties of AC4CH that is a part of the mechanical property of metal matrix composites. Metal matrix composite that is produced from matrix material AC4CH and reinforcement SiO$_2$, Al$_2$O$_3$ and TiO$_2$ are added to the metal matrix composite fur strength so binding among the whisker can take place. Each metal matrix composite is produced using the squeeze casting method. To test for tribe a pin-on-disk machine and lubricant is used without paraffine 8.2CST at room temperature which is 40$\^{C}$. As the results of this study, the tribological properties of each specimen are more improved than AC4CH. The variation of coefficient resistance is more stable at the AC4CH and TiO$_2$, but the variation rates are higher at the inanimate binder.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.10a
• /
• pp.335-340
• /
• 2002

In recent years, the study of metal matrix composite has increased specially, aluminum alloy, research and development are briskly progress to find new metal matrix composite. this study is following the this purpose; This study is used metal matrix composite that was produced by matrix, AC4CH. and reinforcement $A_{18}B_4O_{33}$ metal matrix composite to add $Al_2O_3,\;TiO_2$ for strengthen of binding together among the Whisker. Each Metal matrix composite is produced using the squeeze casting method. Fracture tounghness test was in accordance with the provisions of ASTM E399; Specimen was produced half-size CT specimen W=25mm, B=12.5mm, Cross head speed 0.05mm/min in room temperature. The plane strain fracture toughness $K_{IC}$ is $8.7MPa-m^{0.5}$ for $Al_{18}B_4O_{33}$/AC4CH., $9.28MPa-m^{0.5}$ for $Al_{18}B_4O_{33}$/AC4CH added $TiO_2$. and $Al_2O_3$ but AC4CH alloy was violated the critical stipulated by ASTM standard for a valid measurement of $K_{IC}$. In case of, it was performed $I_{IC}$ test instead of $K_{IC}$ based on ASTM E 1820