• 대한치과기공학회지
• /
• 제34권2호
• /
• pp.75-81
• /
• 2012

Purpose: All ceramic crown, made from zirconia instead of metal for core material, is recognized the best esthetical prosthesis. Recently, high-priced zirconia blocks and expensive CAD/CAM machines come into use for making zirconia core. In this study, slip casting process is adapted to evaluate the possibility of the recycling the remained parts of zirconia block after machining. Methods: Remained zirconia blocks were reduced to powders with zirconia mortar, and screened with 180 mesh sieve. Passed powders were ball milled under various conditions to obtain the optimum zirconia slip for casting. Solid casting method was used for casting the specimens with plaster mold. Formed specimens were dried and biscuit fired at $1,000^{\circ}C$ for 1 hour. Biscuit fired specimens were finished with exact shape of square pillar. Finished specimens were fired from $1,200^{\circ}C$ to $1,550^{\circ}C$ at $50^{\circ}C$ intervals for 1 hour. Linear shrinkage, apparent porosity, water absorption, bulk density, and flexural strength were tested. Microstructures were observed by SEM. Results: Above examinations indicated that the optimum firing temperture was $1,500^{\circ}C$, and when fired at this temperature for 1 hour, apparent porosity was 0% and flexural strength was 680MPa. SEM photomicrographs showed uniform 200~300nm grain size, which is equal with microcture of sintered commercial zirconia block. when compare 24% linear shrinkage of cast specimen with 20% linear shrinkage of CAD/CAM machined block, it was estimated that the size controlling of cast core was not so difficult. Conclusion: According to the all of this experimental results, the cast zirconia core produced from the remained parts of zirconia block was possible to use for all ceramic denture.

• 한국표면공학회지
• /
• 제56권6호
• /
• pp.451-456
• /
• 2023

Transparent conducting films having a three layered structure of ZnO/Cu/ZnO (ZCZ) were deposited onto the glass substrates by using RF and DC magnetron sputtering at room temperature. The emissivity and opto-electrical properties of the films were investigated with a varying thickness(5, 10, 15 nm) of the Cu interlayer. With increasing the Cu thickness to 15 nm, the films showed a enhanced electrical properties. Although ZnO 30/Cu 15/ZnO 30 nm film shows a lower resistivity of 5.2×10^-5 Ωcm, it's visible transmittance is deteriorated by increased optical absorbtion of the films. In addition, X-ray diffraction patterns indicated that the insertion of Cu interlayer improve the grain size of ZnO films, which is favor for the electrical and optical properties of transparent conducting films. From the observed low emissivity of the films, it is concluded that the ZCZ thin films with optimal thickness of Cu interlayer can be applied effectively for the car's window coating materials.

• 대한치과보철학회지
• /
• 제35권1호
• /
• pp.221-243
• /
• 1997

The objective of this study was to characterize the mechanical properties of $Y_{2}O_{3}$-containing glass infiltrated ceramic core material, which was made by pressureless powder packing method. A pure alumina powder with a grain size of about $4{\mu}m$ was packed without pressure is silicon mold to form a bar shaped sample, and applied PVA solution as a binder. Samples were sinterd at $1350^{\circ}C$ for 1 hour. After cooling, $Y_{2}O_{3}$-containing glass($SiO_{2},\;Y_{2}O_{3},\;B_{2}O_{3},\;Al_{2}O_{3}$, ect) was infiltrated to the sinterd samples at $1300^{\circ}C$ for 2 hours and cooled. Six different proportions $Y_{2}O_{3}$ of were used to know the effect of the mismatch of the thermal expansion coefficient between alumina powder and glass. The samples were ground to $3{\times}3{\times}30$ mm size and polished with $1{\mu}m$ diamond paste. Flexural strength, fracture toughness, hardness and other physical properties were obtained, and the fractured surface was examined with SEM and EPMA. Ten samples of each group were tested and compared with In-Ceram(tm) core materials of same size made in dental laboratory. The results were as follows : 1. The flexural strengths of group 1 and 3 were significantly not different with that of In-Ceram, but other experimental groups were lower than In-Ceram. 2. The shrinkage rate of samples was 0.42% after first firing, and 0.45% after glass infiltration. Total shrinkage rate was 0.87%. 3. After first firing, porosity rate of experimental groups was 50%, compared with 22.25% of In-Ceram. After glass infiltration, porosity rate of experimental groups was 2%, and 1% in In-Ceram. 4. There was no statistical difference in hardness between two materials tested, but in fracture toughness, group 2 and 3 were higher than In-Ceram. 5. The thermal expansion coefficients of experimental groups were varied to $4.51-5.35{\times}10^{-6}/^{\circ}C$ according to glass composition, also the flexural strengths of samples were varied. 6. In a view of SEM, many microparticles about $0.5{\mu}m$ diameter and $4{\mu}m$ diameter were observed in In-Ceram. But in experimental group, the size of most particles was about $4{\mu}m$, and a little microparticles was observed. The results obtained in this study showed that the mismatch of the thermal expansion coefficients between alumina powder and infiltrated glass affect the flexural strength of alumin/glass composite. The $Y_{2}O_{3}$-containing glass infiltrated ceramic core made by powder packing method will takes less time and cost with sufficient flexural strength similar to all ceramic crown made with slip casting technique.

• Corrosion Science and Technology
• /
• 제13권1호
• /
• pp.28-35
• /
• 2014

Recently, the fuel oil of diesel engines of marine ships has been increasingly changed to heavy oil of low quality as the oil price is getting higher and higher. Therefore, the spiral gear attached at the motor of the oil purifier which plays an important role to purify the heavy oil is also easy to expose at severe environmental condition due to the purification of the heavy oil in higher temperature. Thus, the material of the spiral gear requires a better mechanical strength, wear and corrosion resistance. In this study, the heat treatment(tempering) with various holding time at temperature of $500^{\circ}C$ was carried out to the alloy of Cu-7Al-2.5Si as centrifugal casting, and the properties of both hardness and corrosion resistance with and without heat treatment were investigated with observation of the microstructure and with electrochemical methods, such as measurement of corrosion potential, cathodic and anodic polarization curves, cyclic voltammogram, and a.c. impedance. in natural seawater solution. The ${\alpha}$, ${\beta}^{\prime}$ and ${\gamma}_2$ phases were observed in the material in spite of no heat treatment due to quenching effect of a spin mold. However, their phases, that is, ${\beta}^{\prime}$ and ${\gamma}_2$ phases decreased gradually with increasing the holding time at a constant temperature of $500^{\circ}C$. The hardness more or less decreased with heat treatment, however its corrosion resistance was improved with the heat treatment. Furthermore, the longer holding time, the better corrosion resistance. In addition, when the holding time was 48hrs, its corrosion current density showed the lowest value. The pattern of corroded surface was nearly similar to that of the pitting corrosion, and this morphology was greatly observed in the case of no heat treatment. It is considered that ${\gamma}_2$ phase at the grain boundary was corroded preferentially as an anode. However, the pattern of general corrosion exhibited increasingly due to decreasing the ${\gamma}_2$ phase with heat treatment. Consequently, it is suggested that the corrosion resistance of Cu-7Al-2.5Si alloy can be improved with the heat treatment as a holding time for 48 hrs at $500^{\circ}C$.

• 한국식품조리과학회지
• /
• 제25권2호
• /
• pp.252-259
• /
• 2009

본 연구에서는 식품의 곰팡이 초기오염 검출에 사용할 수 있는 ergosterol 분석용 바이오센서를 개발하고자 $MWNT-NH_2$ 유리탄소전극을 제작하고, cholesterol oxidase의 고정화를 통해 효소반응기를 제작하여, 바이오센서의 전기 화학적 ergosterol 검출장치를 구성하였다. FT-IR을 통해 MWNT에 기능기가 잘 도입되었음을 확인하였고, cholesterol oxidase 효소 고정화 시 coupling efficiency는 99% 이었다. 제작한 $MWNT-NH_2$ 유리탄소전극의 $H_2O_2$ 용액에 대한 농도별 전류를 분석한 결과 $1{\times}10^{-5}{\sim}8{\times}10^{-5}$ M 농도에서 우수한 선형관계를 나타내었고 검출한계는 $10^{-7}$ M이었다. 본 연구에서 제작한 ergosterol 센서를 이용하여 ergosterol에 대한 반응을 측정한 결과 $1.0{\times}10^{-6}{\sim}1.0{\times}10^{-5}$ M의 농도에서 좋은 선형관계를 나타내어 고감도로 ergosterol을 정량할 수 있는 것으로 확인되어 식품의 곰팡이 오염을 확인하는데 유용하게 사용될 수 있을 것으로 보인다.

• 공업화학
• /
• 제20권3호
• /
• pp.317-321
• /
• 2009

고체 산화물 전해질로 사용되고 있는 초 이온 전도체인 $K^+-{\beta}/{\beta}"-Al_2O_3$의 고온 상관계와 소결성 분석을 위하여 $K_2O-LiO_2-Al_2O_3$ 삼성분계로부터 고상반응을 통하여 순수한 $K^+-{\beta}/{\beta}"-Al_2O_3$ 분말을 합성한 후 slip casting방법과 냉간정수압성형에 의하여 tube와 disk형을 각각 제작하였다. Slip casting은 40 wt%의 고체함량을 가지는 슬러리를 사용해 알루미나 몰드에서 이루어졌고 냉간정수압성형은 20 MPa의 압력하에서 수행되었다. 성형체들은 $1600^{\circ}C$, $1700^{\circ}C$, $1750^{\circ}C$에서 각각 소결하여 성형방법에 따른 상관계와 소결밀도를 조사하였다. 냉간정수압성형에 의한 시편이 $1700^{\circ}C$까지 ${\beta}"-Al_2O_3$의 상분율이 월등히 높은 반면, 소결밀도에 있어서는 slip casting방법의 경우가 다소 높았다. 소결 시 상대밀도는 $1750^{\circ}C$에서 1 h 경과 후, 두 경우 모두 약 83%를 나타내었다. 90 min 이상 소결하였을 때는 입자의 과대성장과 기공으로 인해 오히려 밀도가 낮아졌다.

• 대한치과보철학회지
• /
• 제57권2호
• /
• pp.95-101
• /
• 2019

목적: 레진 시멘트와 코발트 크롬 합금 간의 미세인장결합강도에 다양한 프라이머들이 미치는 영향을 평가하기 위한 것이다. 재료 및 방법: 본 실험에서는 4개의 프라이머(Universal primer, Metal primer II, Alloy primer, and Metal/Zirconia primer)와 2개의 레진 시멘트(Panavia F2.0, G-CEM LinkAce)를 사용하였고, 길이 6 mm, 폭 1 mm, 두께 1 mm의 150개의 코발트 크롬 빔들이 캐스팅 과정을 통해 제작되었다. 150개의 코발트 크롬 빔들을 프라이머와 레진 시멘트의 종류에 따라 프라이머 처리를 하지 않은 대조군을 포함하여 10개 그룹으로 나누었다. 금속과 레진시멘트를 산화알루미늄($125{\mu}m$ 크기)으로 샌드블라스팅 처리한 후 실리콘 틀을 이용하여 접착시켰다. 실험 전에, 입체현미경(stereomicroscope)을 이용하여 모든 금속-레진 빔들을 검사하였고, 미세인장결합강도 실험을 시행하였다. 통계적인 평가에는 one-way ANOVA와 Tukey's test를 사용하였다. 결과: 모든 그룹들의 평균 미세인장결합강도는 20 - 28 MPa이었으며, 그룹 간에 통계적으로 유의한 차이는 없었다. Panavia F2.0과 G-CEM LinkAce 그룹 모두에서 접착 파절과 응집 파절이 동시에 나타나는 혼합 파절이 가장 흔하게 일어난 파절 양태였다. 결론: 모든 실험군들의 미세인장결합강도는 상대적으로 높았지만, 본 실험에서는 프라이머의 사용이 Panavia F2.0 및 G-CEM LinkAce 레진시멘트와 코발트 크롬 합금 사이의 미세인장결합강도를 증가시키지 않았다.