• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.93-96
• /
• 2002

Instrumented impact tests and compression-after-impact(CAI) tests have been used to evaluate the effect of temperature on the low-velocity impact characteristics of phenolic matrix composites reinforced with various woven glass fabric. Impact characteristics and damage area in laminates are evaluated by C-scan. It is shown that the extent of damage and residual compressive strength of the laminates vary with energy level and impact test temperature. The damage area increases with increasing impact energy and temperature. All these observations indicate reduced impact damage resistance and damage tolerance of the laminates at elevated temperature.

• Proceedings of the KSR Conference
• /
• 2001.10a
• /
• pp.211-216
• /
• 2001

It is well known that composite laminates are easily damaged by low velocity impact. Low velocity impact damage characteristics and residual compressive strength of composite laminates used in light rail transit are investigated. The damage of composite laminates subjected to impact loading are occurred matrix cracking, delamination, and fiber breakage. The damage of matrix cracking and delamination are reduced suddenly the compressive strength after impact. The objectives of this study is to evaluate impact characteristics and the relationship between impact force and inside damage of composite laminates by low velocity impact loading. UT C-scan is used to determine impact damage areas by impact loading.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.228-233
• /
• 2001

It is well known that composite laminates are easily damaged by low velocity impact. The damage of composite laminates subjected to impact loading are occurred matrix cracking, delamination, and fiber breakage. The damage of matrix cracking and delamination are reduced suddenly the compressive strength after impact. This study is to evaluate impact characteristics and the relationship between impact force and inside damage of composite laminates by low velocity impact loading. UT C-scan is used to determine impact damage areas by impact loading.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.162-167
• /
• 2004

The low velocity impact characteristics of composite laminate curved beams are investigated to increase damage tolerance and reduce the deflection. Drop weight impact tests of the composite curved beam were performed with respect to pre-load, then the damage after impact was measured by macrography. Also, finite element analyses were performed using ABAQUS to investigate the stress state of composite curved beam with respect to pre-load and impact. From the investigation, it was found that pre-load of the composite curved beams had much influence on impact damage of the curved beam, which showed good agreement with the experiment results.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.225-230
• /
• 2000

This paper presents the fatigue behavior of composite materials with impact-induced damage. The impact damage parameter is proposed to evaluate the effect of impact damage on fatigue life. Subsequently, a new model is developed to predict the fatigue life of impacted composite materials. Also, a stochastic model is proposed to describe the variation of fatigue life due to the material nonhomogeneity. For these models, the fatigue tests were performed on the unimpacted and impacted composite materials. The effect of impact damage on fatigue life can be characterized by the impact damage parameter. Additionally, the results by the present fatigue life prediction model agree well with experimental results regardless of applied impact energy. Also, the variation of fatigue life can be described by the present stochastic model and is reduced with applied impact energy.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.235-239
• /
• 2005

In this research, we investigated the frequency characteristic of low-velocity impact induced damage signals on graphite/epoxy composite laminates using high-speed fiber Bragg grating(FBG) sensor system. Appling the FBG sensors to damage assessment, we need to study the response of FBG sensors as the damage signals of the different incident angles because FBG shows different directional sensitivity. In order to discriminate an impact induced damage signal from that of undamaged case, drop impacts with different energies were applied to the composite panel with different incident angle to the FBG sensor. Finally, detected impact signals were compared using frequency distributions of wavelet detail components in order to find distinctive signal characteristics of composites delamination.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.6
• /
• pp.135-141
• /
• 1997

Low velocity impact test and compressive residual strength test after impact were performed by using Hercules AS4/3501-6[45/0/-45/90]$_{2s}$ laminated plate to investigate the low velocity impact damage behavior and the post-impact strength degradation on orthotropic composite laminate plate. Due to the lateral impact losd, the load path showed "" shape according to the laminate central deflection. Damage in a laminate occurs by inclined matrix crack at the damage initiation load stage and vertical matrix crack, occurs on the outer surface. Evaluating the compressive residual strength after the low velocty impact test, it could be found that there is a transient range where the compressive residual strength drop suddenly in the initial damage which is in the matrix crack range and the initial delamination area. is in the matrix crack range and the initial delamination area.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.10a
• /
• pp.158-162
• /
• 2003

The PVDF(polyvinylidene fluoride) film sensor as one of smart sensors has good characteristics to detect the impact damages of composite structures. The capabilities of the PVDF film sensor for evaluating impact behaviors and damages of Gr/Ep laminates subjected to low-velocity impact were examined. From sensor signals, the specific wave-forms implying the damage were detected. The wavelet transform(WT) and Short Time Fourier Transform(STFT) were used to decompose the piezoelectric sensor signals in this study. The impact behaviors of Gr/Ep laminates were simulated and the impact forces were reconstructed using the sensor signals. Finally, the impact damages were predicted by finite element analysis with the reconstructed forces. For experimental verification, a series of low-velocity impact tests from low energy to damage-induced energy were carried-out. The extent of damage in each case was examined by means of ultrasonic C-scan and the measured damage areas were agreed well with the predicted areas by the F.E.A.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.264-267
• /
• 2005

Impact damages are very important in the perspective of residual strength of composite structures such as aircrafts, ships, and trains because those damages are sometimes not visible on the surface of the point of impact and the impact resistance of laminated composites is usually not so high. Thus, the impact characteristics of laminated composites should he investigated for the safety of composite structures. This paper investigates the low-velocity impact and damage detection conducted on woven carbon/epoxy laminates. Experimental results show that the type of damage is dependent on the impact energy level and the delamination area becomes larger as the impact energy increases.

• Proceedings of the KSR Conference
• /
• 2002.10a
• /
• pp.86-91
• /
• 2002

Glass/phenolic composite laminates have been used in the field of non-flammable light rail transit and their applications have expanded more widely. Low velocity impact tests have been used to evalute the effect of temperature and acceleration aging on low velocity impact response of phenolic matrix composites reinforced with woven E-glass fabric. The damage of matrix cracking and delamination are suddenly reduced the compressive strength after impact. The damage area increases with increasing temperature and impact energy. UT C-scan is used to determine damage areas by impact loading. Therefore, all this observations indicate reduced impact damage resistance and damage tolerance of the laminates at elevated temperature.