• Korean Journal of Metals and Materials
• /
• v.46 no.12
• /
• pp.788-799
• /
• 2008

This study is concerned with the effects of Mo, Cr, and V addition on tensile and Charpy impact properties of API X80 linepipe steels. Four kinds of steels were processed by varying Mo, Cr, and V additions, and their microstructures and tensile and Charpy impact properties were investigated. Since the addition of Mo and V promoted to form fine acicular ferrite and granular bainite, while prohibiting the coarsening of granular bainite, it increased the strength and upper shelf energy, and decreased the energy transition temperature. The Cr addition promoted the formation of coarse granular bainite and secondary phases such as martensite-austenite constituents, thereby leading to the increased effective grain size, energy transition temperature, and strength and to the decreased upper shelf energy. The steel containing 0.3wt.% Mo and 0.06wt.% V without Cr had the highest upper shelf energy and the lowest energy transition temperature because its microstructure was composed of fine acicular ferrite and granular bainite, together with a small amount of hard secondary phases, while its tensile properties maintained excellent.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.2
• /
• pp.10-21
• /
• 2006

Recycled polypropylene (RPP) - Wood Saw Dust (WSD) composites with and without acetylation of filler were produced at different filler loading (15%, 25%, 35% and 45% w/w) and filler size (300, 212 and $100{\mu}m$). The RPP-WSD was compounded using a Haake Rheodrive 500 twin screw compounder at $190^{\circ}C$ at 8 MPa for 30 minutes. The mechanical properties and water absorption properties of modified and unmodified WSD-PP composites were investigated. Acetylation of WSD improved the mechanical and water absorption characteristic of composites. The decrease of filler size (300 to $100{\mu}m$) of the unmodified and acetylated WSD showed increase of tensile strength and impact properties. The composites exhibited higher tensile modulus properties as the filler loading increased (15% to 45%). However tensile strength, elongation at break and impact strength showed the opposite phenomenon. Water absorption increased as the mesh number and filler loading increased. With acetylation, lower moisture absorption was observed as compared to unmodified WSD. The failure mechanism from impact fracture of the filler-matrix interface with and without acetylation was analyzed using Scanning Electron Microscope (SEM).

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.5
• /
• pp.813-821
• /
• 2002

Glass fiber reinforced PET matrix composite was manufactured by rapid press consolidation technique as functions of temperature, pressure and time in pre-heating, consolidation and solidification stages. The optimal manufacturing conditions for this composite were discussed based on the void content, tensile, interlaminar shear and impact properties. In addition, the levels of crystallinity with various manufacturing conditions were measured using differential scanning calorimetry to investigate the mechanical properties of this composite material as a function of crystallinity. Among many processing parameters, the mold temperature and the cooling rate after forming were found to be the most critical factors in determining the level of crystallinity and mechanical properties. The level of crystallinity affects the tensile properties to some degree. However, impact properties are affected much more. It also affects the degree of ductility, which determines the impact energy of this material.

• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.22-26
• /
• 2012

Butt-joints of A6061-T6 and AZ31 plates were successfully manufactured by using a friction stir welding method. Off-set free joints and off-set joints were fabricated to investigate the effect of the tool plunge position on the mechanical properties of the joints. Hardness test, tensile test and charpy impact test was performed to evaluate the mechanical properties of the joints. Off-set condition resulted in increase of mechanical properties of the joints. The variation of the hardness distribution in the SZ was also stabilized in the off-set condition. Tensile strength of the off-set joint was about 85% against to that of the AZ31 base metal. Impact absorption energy by Charpy-Impact-Test of the off-set joint also increased by almost 2 times against to that of the AZ31 base metal.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.7
• /
• pp.4081-4086
• /
• 2014

Cellulose acetate butyrate (CAB) is a biodegradable resin with excellent optical properties, but it is difficult to apply film process. In this study, an attempt was made to improve the processability of CAB using polyactic acid and the mechanical properties using an impact modifier. Polylacitc acid (PLA)/Cellulose acetate butyrate (CAB) blends with an impact modifier were prepared using a twin screw extruder. The temperature range was $140^{\circ}C$ to $200^{\circ}C$, and the screw speed was fixed to 200 rpm. To evaluate the miscibility of impact modified CAB/PLA, the glass transition behavior and morphology were observed by DSC and FE-SEM. The mechanical properties were investigated by dynamic mechanical analysis (DMA) and a Universal Testing Machine (UTM). In addition, the effect of an impact modifier in the polymer matrix was determined using a notched Izod impact strength tester. Finally, the PLA/CAB/impact modifier 75/25/10 ratio was found to be a compatible system. In the 10wt.% impact modifier, the sample had a 4 times higher izod impact strength than the non-toughening composition.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.100-108
• /
• 2015

The purpose of this study is to evaluate the effect of improvement on the impact resistance and strength properties of cement composites by surface modification of aramid fiber. For aramid fiber reinforced cement composites, therefore, dispersion capability and the bonding efficiency between the fibers and the cement composite material need to be improved. It is possible by modifying surface properties to hydrophobic, it is considered that oiling agent ratio of 1.2 % and improvement of performance is in need to be investigated. In this study, short aramid fibers were mixed by different fiber length and oiling agent ratio. And improvement of strength properties and impact resistance performance of hybrid cement composites were evaluated under the influence of steel fiber. As a result, strength properties of aramid fiber reinforced cement composites are different by mixing ratio of fiber, oiling agent ratio and length of fiber. In case of cement composites which have same volume fraction and fiber length, tensile strength and flexural strength were improved with increase of the emulsions throughput of the fiber surface. The results of evaluation on the static strength properties had effects on impact resistance performance by high-velocity impact. And it was observed that the scabbing of rear was suppressed with increase of the oiling agent ratio.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.3
• /
• pp.99-105
• /
• 2017

This study was carried out to investigate the effect of heat treatment on the microstructure and mechanical properties in 90% hot forged Incoloy 825 alloy. With increasing solution treatment temperature, the grain size increased and the volume fraction of total precipitates decreased, and the precipitates disappeared at $1,000^{\circ}C$. With increasing aging time at $700^{\circ}C$, the volume fraction of precipitate increased and the precipitates size increased. Most of the precipitates consist $Cr_{23}C_6$ carbide, and a small amount of TiC carbide was also observed. With decreasing solution treatment temperature and increasing aging time, tensile strength and hardness increased, and the elongation and impact value decreased. With increasing aging time, the impact value decreased sharply by the increased of the precipitate size.

• Korea-Australia Rheology Journal
• /
• v.20 no.4
• /
• pp.227-233
• /
• 2008

High impact polystyrene (HIPS)/organoclay nanocomposites via in situ polymerization were synthesized and their rheological properties were investigated. For the study, two types of organoclays were used: a commercially available organoclay, Cloisite 10A (C10A), and a laboratory-prepared organoclay having a reactant group, vinylclay (ODVC). The X-ray diffraction and transmission electron microscopy experiments revealed that the HIPS/ODVC nanocomposite achieved an exfoliated structure, whereas the HIPS/C10A nanocomposite achieved an intercalated structure. In the small-amplitude oscillatory shear experiments, both storage modulus and complex viscosity increased with increasing organoclay. A pronounced effect of the organoclay content was observed, resulting in larger storage modulus and stronger yield behavior in the low frequency region when compared to neat HIPS. The crossover frequencies associated with the inverse of a longest relaxation time decreased as the organoclay content increased. Over a certain value of ODVC content, a change of pattern in rheological properties could be found, indicating a solid-like response with storage modulus greater than loss modulus at all frequencies.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.51-51
• /
• 2009

In order to understand the properties of high heat input welds made by electro gas welding, two kinds of low temperature steel were welded. Welding heat inputs were controlled by width of root gap and ranged from 118 to 143kJ/cm. Chemical composition and micro-structural analysis were performed. To understand low temperature impact properties, Charpy impact test was conducted at several temperatures. The results were summarized as follows; 1) Grain size of weld metal and heat affected zone was increased with an increase in welding heat input. 2) Impact test values at fusion line were severely fluctuated regardless of base metals, showing enormous difference among the values at the same test temperature.

• Steel and Composite Structures
• /
• v.17 no.6
• /
• pp.825-834
• /
• 2014

This manuscript presents an experimental investigation on the effect of Multi-walled carbon nanotubes (MWCNTs) addition on the tensile, flexural and impact properties of woven Kevlar fabric reinforced epoxy composites. MWCNTs were dispersed in the epoxy resin by sonication technique and the samples were fabricated by hand layup laminating procedure. Scanning electron microscopy (SEM) was used to characterize the microstructure of produced samples. The effects of adding small amounts (${\leq}1%$) of MWCNT on the tensile, flexural and impact (Izod) behaviors of laminated composites were analyzed. Results revealed that MWCNTs enhanced the Young's modulus up to 20%, bending modulus up to 40%, and impact strength up to 45% in comparison with woven Kevlar fabric/epoxy composites. It was found that the maximum improvements in mechanical properties were happened for 0.5 wt.% MWCNT.