The effect of Ni addition, on the mechanical properties and fracture characteristics of Mo-Cu and Mo-Ni-Cu alloyed ductile iron austenitized at $900^{\circ}C$ and austempering temperatures of $250^{\circ}C$, $300^{\circ}C$ and $350^{\circ}C$. The tensile strength, yield strength and hardness are decreased and elongation and impact value are increased in both Mo-Cu and Mo-Ni-Cu alloyed austempered ductile iron, with increased austempering temperature. According to the austempering temperature are increased, the amount of retained austenite are increased. Maximum value of fracture toughness is obtained at $350^{\circ}C$ austempering temperature at this condition, the amount of retained austenite came to 40% in Mo-Ni-Cu alloyed ADI and 34% in Mo-Cu alloyed ADI. The fracture surface of ADI which had represented high toughness are showed a quasi-cleavage pattern and a dimple pattern with micro void. Comparing the fracture characteristics of Mo-Cu alloyed ADI with that of Mo-Ni-Cu alloyed ADI, the latter was superior to the former.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.22 no.4
• /
• pp.329-340
• /
• 2006

Statement of problem: Damping of the peak force transmitted to implants has been reported by in vitro studies using impact forces on resin-veneered superstructures. Theoretical assumptions suggest that use of acrylic resin for the occlusal surfaces of a prosthesis would protect the connection between implant and bone. Therefore, the relationship between prosthesis materials and the force transmitted through the implant system also needs to be investigated under conditions that resemble the intraoral mechanical environment. Purpose: The purpose of this study was to analyze the fracture strength and modes of temporary prosthesis when a flange or occlusally extended structure were connected on the top of the abutment. Material and method: Modified abutments of winged and bulk design were made by casting the desired wax pattern which is made on the UCLA type plastic cylinder. Temporary crowns were made using templates on the modified abutments, and its fracture toughness and strain were compared to the traditional temporary prosthesis. To evaluate the effect of aging, 5.000 times of thermocycling were performed, and their result was compared to the 24hours specimen result. Results: The following conclusions were drawn from this study: 1. In the fracture toughness test, temporary crown's fracture line located next to the screw hole while modified designs with metal support showed fracture line on the metal and its propagation along the metal-resin interface. 2. Wing and bulk structure didn't show significant difference in the fracture toughness (p>0.05), but wing structure showed stress concentration on the screw hole area compared to bulk structure which showed even stress distribution. 3. In the fracture toughness test after thermocycling, wing and bulk structure showed increased or similar results in metal supported area while off-metal area and temporary crown showed decreased results. 4. In the strain measurement after thermocycling, its value increased in the temporary and bulk structure. However, wing structure showed decreased value in the loading point while increased value in the screw hole area. Conclusion: Wing type design showed compatible result to the bulk type that its application with composite resin prosthesis to the implant dentistry is considered promising.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.12
• /
• pp.160-165
• /
• 1997

The instrumented Charpy impact test is generally used to evaluate the dynamic fracture toughnesses for varying engineering materials. However, the test is known to be difficult to evaluate the dynamic fracturetoughnesses for very brittle materials because of the small crack initiation load which may be engulfed by the inertia load of the instrumented tup. To evaluate the dynamic fracture toughnesses of very brittle materials, such as chalk or plaster,it is thus, necessary to develop a load sensitive instrumented tup. In this study, a polymer tup, which has very small Young's modulus comparing to one of the conventional steel tup, is used for the instrumented Charpy impact test, and a proper testing method to evaluate the dynamic fracture behavior of very brittle materials is developed. The results show that the developed method can measure rapidly changing loads from the moment of contact between the tup and the specimen to dynamic crack initiation of the very brittle materials.

• Journal of Welding and Joining
• /
• v.20 no.5
• /
• pp.63-71
• /
• 2002

One of the shortcoming of ferritic stainless steels is their limited toughness. The most important factor governing the toughness of ferritic stainless steels is hewn to be their interstitial contents. Due to the limited solubility of carbon and nitrogen in the ferrite matrix, it is difficult to avoid carbide and nitride precipitates. In the study, the role of nitrogen on the toughness of 260r-2Mo superferritic stainless steel welds has been investigated using alloys containing various nitrogen levels between 100 and 1640 ppm. Mechanical properties of weld metals have been evaluated by microhardness, Charpy impact test and notch tensile test. The alloys are mainly embrittled by the grain boundary and intragranular nitride precipitation. Grain boundary precipitates are considered to be more deleterious than intrauanular nitrides. Fracture mechanism have been elucidated through microscopic evaluation of notch tensile test

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.424-430
• /
• 2000

In order to develop an ultrasonic evaluation method for properties degradation of high temperature materials, a number of Cr-Mo-V steel samples were heat-treated and their damage mechanism was examined. Ultrasonic parameters such as velocity, attenuation, and more recently developed nonlinear acoustic parameter were measured. The nonlinear acoustic parameter was found to be most sensitive to material degradation mainly attributed to the precipitation of impurities in grain boundaries. When compared to the electrical resistivity results, the nonlinear parameters showed similar behavior. There existed a relatively good correlation between the nonlinear parameter and the fracture appearance transition temperature (FATT) obtained by Charpy V-notch impact test. Based on the relationship between the FATT and the fracture toughness ($K_{IC}$), correlation between the nonlinear parameter and $K_{IC}$ was established.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.3
• /
• pp.219-223
• /
• 2009

This paper prescribed the structural integrity of the API 5L X65 pipeline subjected to tensile pre-strain. The effects of pre-strain on the mechanical properties of API 5L X65 pipe were substantially investigated through a variety of the experimental procedures. Axial tensile pre-strain of 1.5, 5 and 10% was applied to plate-type tensile specimens cut from the pipe body prior to mechanical testing. Tensile test revealed that yield strength and tensile strength were increased with increasing tensile pre-strain. The increasing rate of the yield strength owing to the pre-strain is greater than that of the tensile strength. However, the pre-strain up to 5% had a little effect on the decreasing of the fracture toughness. The structural integrity of the API 5L X65 pipeline subjected to large plastic deformation was evaluated through the fitness-for service code.

• Proceedings of the KSR Conference
• /
• 2009.05a
• /
• pp.239-246
• /
• 2009

The Mode I interlaminar fracture toughness of woven fabric carbon/epoxy and glass/epoxy composites for a train carbody was measured and FEM analysis was conducted. The woven fabric epoxy composite manufactured by hand lay-up, has high stiffness and strength, good resistance for impact, fatigue, corrosion and in-plane failure. The DCB(Double Cantilever Beam) specimen made of woven fabric epoxy composite had the size of 180mm $\times$ 25mm $\times$ 5mm and the insert of 65mm. The Mode I interlaminar toughness of specimen was measured according to ASTM 5528-01. The crack propagation behavior of the DCB specimen was simulated using FEA with cohesive elements that model the adhesive layer between woven fabric plies.

• Macromolecular Research
• /
• v.17 no.8
• /
• pp.585-590
• /
• 2009

The cure behaviors, dielectric characteristics and fracture toughness of diglycidylether of bisphenol-A (DGEBA)/poly(ethylene terephthalate) (PET) blend system were investigated. The degree of conversion for the DGEBA/PET blend system was measured using Fourier transform infrared (FTIR) spectroscopy. The cure kinetics were investigated by measuring the cure activation energies ($E_a$) with dynamic differential scanning calorimetry (DSC). The dielectric characteristic was examined by dielectric analysis (DEA). The mechanical properties were investigated by measuring the critical stress intensity factor ($K_{IC}$), critical strain energy release rate ($G_{IC}$), and impact strength test. As a result, DGEBAIPET was successfully blended. The Ea of the blend system was increased with increasing PET content to a maximum at 10 phr PET. The dielectric constant was decreased with increasing PET content. The mechanical properties of the blend system were also superior to those of the neat DGEBA. These results were attributed to the increased cross-linking density of the blend system, resulting from the interaction between the epoxy group of DGEBA and the carboxyl group of PET.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.04b
• /
• pp.20-24
• /
• 1996

Three kinds of the sialon ceramics with and without TiN additions were hot pressed. Hardness and fracture toughness were measured with prepared specimens to study the effect of additives on the mechanical properties. A gas blast type erosion tester was employed to examine erosion behavior of the specimens up to 600 $^{\circ}$C. Erosion tests showed an increase of erosion rate up to 400 $^{\circ}$C and a gradual decrease of erosion rate 500 $^{\circ}$C for all kinds of sialon. The results also showed that erosion rates of the sialons were controlled better by microstructure factors than by mechanical properties such as fracture toughness.

• Tribology and Lubricants
• /
• v.13 no.3
• /
• pp.42-47
• /
• 1997

Three kinds of the sialon ceramics with and without TiN additions were prepared by hot pressing to investigate the effect of microstructure on erosion behaviors. Hardness and fracture toughness were measured with prepared specimens to study the effect of additives on the mechanical properties. A gas blast type erosion tester was employed to examine erosion behavior of the specimens up to $600^{\circ}C$. Erosion tests showed an increase of erosion rate up to 40$0^{\circ}C$ and a gradual decrease of erosion rate up to 50$0^{\circ}C$ for all kinds of sialon. The results also showed that erosion rates of the sialons were controlled better by microstructural factors than by mechanical properties including fracture toughness and hardness.