• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.164-167
• /
• 2003

The mechanical alloying effect has been studied on the three Cu-based alloy systems with a positive heat of mixing. The extended bcc solid solution has been formed in the Cu-V system and an amorphous phase in the Cu-Ta system. However, it is round that a mixture of nanocrystalline Cu and Mo Is formed in the Cu-Mo system. The neutron diffraction has been employed at a main tool to characterize the detailed amorphization process. The formation of an amorphous phase in Cu-Ta system can be understood by assuming that the smaller Cu atoms preferentially enter into the bcc Ta lattice during ball milling.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.170-170
• /
• 1999

We studied Nb growth mode on Cu(100) surface by scanning tunneling microscopy (STM) at room temperature. Nb/Cu is immiscible at room temperature and thus is an ideal system for studying surface alloy formation. Initially deposited Nb atoms are incorporated subsurface on Cu(100). After annealing, they are preferentially found at step edges and appear as bright dots surrounded by dark rings. Ordering emerges from step edges as annealed. Ordered ({{{{ SQRT { 5} }$\times${{{{ SQRT { 5} }}}})R 26.6$^{\circ}$phase Nb structure is formed at $\theta$<0.2ML after annealing to 50$0^{\circ}C$. At higher coverage, $\theta$>0.25, annealing leads to p(2$\times$2) phase. due to large mismatch in lattice parameters, the domain is limited to a few tens of nm2. Growth kinetics of the system will be discussed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.5
• /
• pp.210-215
• /
• 2006

Mechanical alloying (MA) by high energy ball mill of pure copper and niobium powders was carried out under the Ar gas atmosphere. The supersaturated solid solution can be produced in the range up to $Cu_xNb_{100-x}$(x=5-30) by MA for 120 hrs, as demonstrated by X-ray diffraction, DSC analysis and the electronic studies through a change in the superconducting transition in the low-temperature specific heat. The $Cu_{30}Nb_{70}$ samples ball-milled for 120 hrs exhibit only a broad exothermic heat release. The total energy, ${\Delta}H_t$ accumulated during MA far the mixture of $Cu_{30}Nb_{70}$ powders increased with milling time and approached the saturation value of 7.5 kJ/mol after 120 h of milling. It can be seen that the free energy difference between the supersaturated solid solution and the mixture of $Cu_{30}Nb_{70}$ powders is estimated to be 7 kJ/mol by Miedema et al. Hence it is thermodynamically possible to assume the formation of a supersaturated solid solution phase in this system.

• Korean Journal of Materials Research
• /
• v.4 no.6
• /
• pp.620-625
• /
• 1994

We recently showed from the neutron diffraction and extended X-ray absorption fine structure studies the structural evidence for the formation of an amorphous phase in immiscible Cu-Ta system subjected to mechanical alloying. In a system with a positive heat of mixing like Cu-Ta, we consider it necessary to confirm the formation of an amorphous phase not only from the structural studies but also from a change in the electronic properties. We show the electronic evidence for the formation of the chemical bonding between the unlike atoms Cu and Ta for the 120 h-milling sample through changes in superconducting transition temperature and X-ray photoemission spectroscopy valence band structure.