• Journal of Sensor Science and Technology
• /
• v.10 no.6
• /
• pp.328-337
• /
• 2001

The stochiometric mix of evaporating materials for the $CdGa_2Se_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CdGa_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CdGa_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.27{\times}10^{17}cm^{-3}$, $345\;cm^2/V{\cdot}s$ at 293 K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuInSe_2$ single crystal thin film, we have found that the values of spin orbit splitting ${\Delta}So$ and the crystal field splitting ${\Delta}Cr$ were 106.5 meV and 418.9 meV at 10 K, respectively. From the photoluminescence measurement on $CdGa_2Se_4$ single crystal thin film, we observed free excition ($E_x$) existing only high quality crystal and neutral bound exiciton ($D^{\circ}$, X) having very strong peak intensity. Then, the full-width-at -half-maximum(FWHM) and binding energy of neutral donor bound excition were 8 meV and 13.7 meV, respectivity. By Haynes rule, an activation energy of impurity was 137 meV.

• Journal of Sensor Science and Technology
• /
• v.2 no.1
• /
• pp.101-108
• /
• 1993

$TiO_{2}$/Se : Te heterojunction for color sensor has been fabricated by RF reactive sputtering and thermal evaporation methods onto glass substrate. The optimum deposition condition of $TiO_{2}$ films was such that RF power was 120 W, substrate temperature was $100^{\circ}C$, oxygen concentration was 50%, working pressure was 50 mTorr for the $TiO_{2}$ film thickness of $1000{\AA}$. In this case, the optical transmittance of $TiO_{2}$ film at 550 nm-wavelength was 85%, resistivity was $2{\times}10^9{\Omega}{\cdot}cm$, refractive index was 2.3, and optical bandgap was 3.58 eV. The composition ratio of 0 to Ti by AES analysis was 1.7. When $TiO_{2}$ films were annealed at $400^{\circ}C$ for 30 min. in $O_{2}$ ambient, the optical transmittance of $TiO_{2}$ films at the wavelength range of $300{\sim}580$ nm was improved from 0 to 25%. When Se : Te films were annealed at $190^{\circ}C$ for 1 min., photosensitivity under illumination of 1000 lux was 0.75. The optical bandgap of Se : Te films was 1.7 eV. The structures of Se : Te films were the hexagonal with (100) and (110) orientation. The spectral response of a-Se was improved by the addition of Te, especially in the long wavelength region. The $TiO_{2}$/Se : Te heterojunction showed wide spectral response, and more improved one than that of a-Si film in the blue light region.

• Journal of Sensor Science and Technology
• /
• v.10 no.1
• /
• pp.62-70
• /
• 2001

The ZnSe sample grown by chemical bath deposition (CBD) method were annealed in Ar gas at $45^{\circ}C$. Using extrapolation method of X-ray diffraction pattern, it was found to have zinc blend structure whose lattice parameter $a_o$ was $5.6687\;{\AA}$. From Hall effect, the mobility was likely to be decreased by impurity scattering at temperature range from 10 K to 150 K and by lattice scattering at temperature range from 150 K to 293 K. The band gap given by the transmission edge changed from $2.700{\underline{5}}\;eV$ at 293 K to $2.873{\underline{9}}\;eV$ at 10 K. Comparing photocurrent peak position with transmission edge, we could find that photocurrent peaks due to excition electrons from valence band, ${\Gamma}_8$ and ${\Gamma}_7$ and to conduction band ${\Gamma}_6$ were observed at photocurrent spectrum. From the photocurrent spectra by illumination of polarized light on the ZnSe thin film, we have found that values of spin orbit coupling splitting ${\Delta}so$ is $0.098{\underline{1}}\;eV$. From the PL spectra at 10K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be $0.061{\underline{2}}\;eV$ and the dissipation energy of the donor -bound exciton and acceptor-bound exciton to be $0.017{\underline{2}}\;eV$, $0.031{\underline{0}}\;eV$, respectively.