• 한국정보디스플레이학회:학술대회논문집
• /
• 2003.07a
• /
• pp.849-851
• /
• 2003

After multi-walled carbon nanotubes (MWNT) powder was crushed with ball milling process, it was mixed with organic vehicles. And then CNT paste was printed on ITO coated glass substrate. The field emission characteristics of CNT pastes fired in air atmosphere was better than that of CNT paste fired in Ar ambient due to less organic residues after firing.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.521-524
• /
• 2005

ZnO 2-D nanowall structure with around 100 nm thickness, which is composed of tens of nm scale ZnO single crystals, was fabricated through the low temperature chemical solution growth method. Electro Chemical Deposition (ECD) technique was applied to attach the ZnO seed crystals on ITO coated glass substrate. The ZnO nanowall structure was grown in the 0.015 mol$\%$ of aqueous solution of zinc nitrate and hexamethenamine at 60$^{\circ}C$ for 20 - 40 h. The nanowall structure depends on the ECD condition or the applied voltage and duration time. The nanowall shows a photoluminescence around 550 - 700 nm spectrum range.

• Journal of the Semiconductor & Display Technology
• /
• v.5 no.1 s.14
• /
• pp.51-55
• /
• 2006

MgO thin films were prepared through electron-beam deposition onto ITO-coated glass substrates in order to measure electrical, dielectric, and microstructural properties. Design of experiments was performed in this study with the aim to understanding of the effects of processing variables, e.g., substrate temperature and filament current of an e-beam evaporator statistically. Leakage currents, relative dielectric constants, and diffraction intensities of MgO thin films were analyzed statistically, following the analysis procedure provided in the design of experiments. The leakage current level of MgO thin films has been found to be statistically significant at the level of $\alpha=0.1$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.6
• /
• pp.481-485
• /
• 2012

ZnO nanowires were synthesized by hydrothermal technique. Prepared synthesis aqueous solutions were preserved by preheating in autoclave type synthesis equipment with various preheating time of 1 h difference. ITO-coated corning glass substrates deposited with AZO seed layers were then inserted in the preheated synthesis aqueous solutions and ZnO nanowires were grown for 180 min at $90^{\circ}C$. Density, length and aspect ratio of the grown ZnO nanowires were investigated. Composition, structural and optical properties of the grown ZnO nanowires were analyzed. Characteristics of the ZnO nanowires were comparatively studied in relation with $Zn^{2+}$ ion concentration measured directly after the preheating of synthesis aqueous solution.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.777-779
• /
• 2002

We report the performance of pentacene-based organic thin film transistors (OTFT) with PMMA (polymethyl methacrylate) as the gate insulator which was spin-coated on the ITO (indium tin oxide) glass substrate which was used as the gate contact. The pentacene thin film was deposited on the PMMA film and then Au source/drain contacts were deposited through shadow mask. The pentacene film shows better molecular ordering on PMMA compared with $SiO_2$ of Si wafer. The devices exhibited the field effect mobility of ${\sim}0.004cm^2$/Vs and on/off current ratio of ${\sim}10^3$.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.1
• /
• pp.46-54
• /
• 1995

An electrochromic(EC) cell was constructed using $WO_3$ as a electrochromic material and NiO as a counter electrode, deposited onto ITO-coated glass by the implementation of electron beam evaporation. The electrolytic media were both lithium and proton conducting polymers such as poly-acrylonitrile(PAN)-$LiClO_4$, poly-ethylene oxide(PEO)-$LiClO_4$, poly-vinyl butyral(PVB)-LiCl and PVB-H$_3$$PO_4$. Potentiodynamic cycling of the cells using PAN-$LiClO_4$, or PVB-$H_3$$PO_4$ electrolyte yielded a transmission variation of more than 40% at the wavelength of 632.8 nm within less than 10 sec response time at room temperature. These results indicate that these electrolytes, transparent in gel type, are premising for the application in large area electrochromic windows.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.7
• /
• pp.535-540
• /
• 1998

Thin films of PLZT were prepared on indium tin oxide(ITO) coated glass substrates by sol-gel process and annealed by rapid thermal annealing(RTA) at $750^{\circ}C$ for 5 minutes. The crystal structure of PLZT thin films were investigated for a different Zr mol% content. XRD results showed that the crystallographic structure was transitted from tetragonal to rhombohedral structure as Zr mol% increased. Raman spectroscopy results showed that the bands of spectra became broader as the amount of Zr mol% increased and two crystal phase coexisted at 2/55/45 PLZT film. Raman spectroscopy was useful for crystal structure analysis of PLZT thin films.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1477-1479
• /
• 2000

The annealing treatments on rf magnetron sputtered PZT($Pb_{1.05}(Zr_{0.52},Ti_{0.48})O_3$) thin films(4000${\AA}$) have been investigated for a structure of PZT/Pt/Ti/ITO coated glass. Crystallization properties of PZT films were strongly dependent on RTA(Rapid Thermal Annealing) annealing temperature and time. We were able to obtain a perovskite structure of PZT at 650$^{\circ}C$ and 10min. P-E curves of Pd/PZT/Pt capacitor demonstrate typical hysteresis loops. The measured values of $P_r$, $E_c$ were 15.8[${\mu}C/cm^2$], 95[kV/cm] respectively. Polarization value decrease about 10% after $10^9$ cycles.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.11C no.3
• /
• pp.75-80
• /
• 2001

Holographic polymer dispersed liquid crystals (HPDLCs) have fabricated by irradiating an Ar-ion laser ( ${\lambda}$=514nm) at various intensity on LC/acrylate monomer mixtures which were sandwitched between two ITO coated glass plates. Monomer systems were composed of dipentaerythritol-hydroxy penta acrylate (DPHPA, f=5)/monofunctional acrylate monofunctional monomers. The LC used in this system was E7 (BL001, Merck). Gratings were fabricated by periodic interference of twobeams. Reflection efficiency-irradiation intensity-monomer type relationships were obtained from the UV-visible spectra of the HPDLC films. Peaks were found at a bit smaller wavelength than 514nm, due to the shrinkage of mixture volume upon polymerization. Real time measurements of diffraction efficiency have been obtained according to monomer types and LC contents.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.52-55
• /
• 1997

In this study, PLZT stock solutions were prepared by sol-gel processing to fabricate PLZT thin films. The stock solutions were spin-coated on ITO-glass and the film were annealed by rapid thermal annealing(RTA). The variation of tile crystallographic structure of the thin films and the phase transition with respect to it were observed using Raman spectra. Raman result showed that the band of spectra are broad as the amount of Zr substitution increased and specially, abrupt change occurs in the raman spectra upon crossing the tetragonal-rhombohedral phase boundry at 2/55/45 PLZT thin film. So, the fact that the crystallographic structure was transitted from tetragonal to rhombohedral structure was certified.