• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.123-132
• /
• 2000

To overcome problems of conventional glass ionomers, resin components have been added to glass ionomers. On a continuum between glass ionomers and composites are a variety of blends, employing different proportions of acid-base and free radical reactions to bring about cure. Popular groups defined between the ends are resin-modified glass-ionomers(RMGIs), polyacid-modified composite resins(Compomers) and ionomer modified resins. These groups show different clinical properties, and in selecting these materials for a restoration, one should sufficiently understand these different setting properties. In this study, some difference in the setting characteristics of different groups of hybrid ionomers were examined. Two RMGIs (Fuji2 LC,GC / Vitremer, 3M), three Compomers (Dyract AP, Dentsply / F2000, 3M / Elan, Kerr) were involved in this study. The identification of the setting characteristics of different groups was achieved by a two-stage study. First, thermal analysis was performed by a differential scanning calorimeter, and then the hardness of each group at different depth and time were measured by a micro-hardness tester. Thermal analysis was performed to identify the inorganic filler content and to record the heat change during setting process. The setting process was progressed for each material by chemical set mode and light-cured mode. In the hardness test, samples of materials were prepared with a 6mm-diameter metal ring, and the hardness was measured at the top, and 1mm, 2.5mm, 4mm below at just after a 40 second-cure, and after 10 minutes, 24 hours, and 7 days. Statistical analysis was performed by Mann-Whitney rank sum test to assess significant differences between set modes and types of materials, and by ANOVA and T-test to evaluate the statistical meanings of data at different times and depths of each materials. Followings are findings and conclusions derived from this study. Thermal analysis; 1. Compomers show no evidence of chemical setting while RMGIs exhibit heat output during the process of chemical setting. 2. Heat of cure of RMGIs exceed Compomers. 3. The net heat output of RMGIs through light-cured mode is higher than through chemically set mode. Hardness test; 1. Initial hardness of RMGIs immediately after light cure is relatively low, but the hardness increases as time goes by. On the contrary, Comomers do not show evident increase of the hardness following time. 2. Compomers show a marked decrease of setting degree as the depth of the material increases. In RMGIs, the setting degree at different depths does not significantly differ.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2008년도 Spring Scientific Meeting(the 129th) of Korean Academy if Conservative Dentistry
• /
• pp.184-197
• /
• 2008

본 연구는 3차원 유한요소분석법적 연구를 통해 쐐기형 비우식성 치경부병소의 복합레진수복에서 다른 탄성계수를 가진 복합레진의 혼합수복이 5급 수복물의 응력분포에 미치는 영향에 대해 알아보고자 하였다. 발거된 상악 제2소구치를 Micro-CT로 스캔한 후 3D-DOCTOR로 3차원 유한요소 모형을 제작하였다. 제작된 소구치 모형에 쐐기형 와동과 변형시킨 와동을 형성하고 각 와동을 탄성 계수가 서로 다른 혼합형 복합레진 또는 흐름성 복합레진으로 수복하였다. 수복 전, 후 협측교두와 설측교두에 500N의 하중을 가한 후 응력분포를 ANSYS 프로그램을 이용하여 주 응력 분석법으로 평가한 결과 치아 및 수복물에 위해한 인장응력을 고려할 때 탄성계수가 높은 재료로 와동저선각을 수복하고 교합측변연과 치경부측 변연은 탄성계수가 낮은 재료로 수복하는 혼합수복법이 쐐기형 비치경부병소의 수복에 있어 가장 유리하였다.

• Restorative Dentistry and Endodontics
• /
• 제33권3호
• /
• pp.184-197
• /
• 2008

본 연구는 3차원 유한요소분석법적 연구를 통해 쐐기형 비우식성 치경부병소의 복합레진수복에서 다른 탄성계수를 가진 복합레진의 혼합수복이 5급 수복물의 응력분포에 미치는 영향에 대해 알아보고자 하였다. 발거된 상악 제2소구치를 Micro-CT로 스캔한 후 3D-DOCTOR로 3차원유한요소 모형을 제작하였다. 제작된 소구치 모형에 쐐기형 와동과 변형시킨 와동을 형성하고 각 와동을 탄성계수가 서로 다른 혼합형 복합레진 또는 흐름성 복합레진으로 수복하였다. 수복 전, 후 협측교두와 설측교두에 500N의 하중을 가한 후 응력분포를 ANSYS 프로그램을 이용하여 주 응력 분석법으로 평가한 결과 치아 및 수복물에 위해한 인장응력을 고려할 때 탄성계수가 높은 재료로 와동저선각을 수복하고 교합측변연과 치경부측 변연은 탄성계수가 낮은 재료로 수복하는 혼합수복법이 쐐기형 비치경부병소의 수복에 있어 가장 유리하였다.

• 대한소아치과학회지
• /
• 제30권1호
• /
• pp.54-60
• /
• 2003

본 연구는 영구치와 유치의 상아질 표면에 상품화된 화학기계적 우식치질 제거용액인 $Carisolv^{TM}$(MediTeam, Sweden)를 사용하고 복합레진을 접착한 후 전단결합강도를 측정함으로써 $Carisolv^{TM}$의 사용이 복합레진의 접착에 미치는 영향을 평가하고자 하였다. 교정치료를 위하여 발거된 상, 하악 소구치 80개와 정상적으로 탈락한 손상이 없이 건전한 상악 유전치 80개의 순, 협면의 상아질을 노출시키고 $Carisolv^{TM}$를 실험군은 60초 적용하고 대조군은 $Carisolv^{TM}$를 사용하지 않았다. 상아질 접착제는 Scotchbond Multi-Purpose(3M, USA), Single Bond(3M, USA), Clearfil SE Bond(Kuraray, Japan), AQ Bond(Sun Medical, Japan)를 각각 제조사의 지시대로 적용하였고 광중합형 복합레진은 Z100(3M, USA)을 사용하였다. $5^{\circ}C$와 $55^{\circ}C$에 각 30초씩 계류시켜 1,000회 열순환시키고 Universal Testing Machine(Zwick Z020, Zwick Co., Germany)을 사용하여 전단결합강도를 측정하고 분석하여 다음과 같은 결론을 얻었다. 1. 각 군간 전단결합강도를 비교한 결과, 유치에 비해 영구치의 전단결합강도가 높게 나타났다. 영구치에서는 Clearfil SE Bond만 사용한 군에서 가장 높았고 $Carisolv^{TM}$와 AQ Bond를 병용한 군에서 가장 낮았다. 2. $Carisolv^{TM}$ 사용하지 않은 군과 사용한 군간의 전단결합강도를 비교한 결과, 영구치와 유치 모두에서 상아질 접착제의 종류에 관계없이 $Carisolv^{TM}$를 사용한 군이 사용하지 않은 군에 비해 전단결합강도가 통계학적으로 유의하게 낮게 나타났다(P<0.001). 3. 상아질 접착제의 종류에 따른 전단결합강도를 비교한 결과, 영구치와 유치 모두에서 Clearfil SE Bond를 사용한 군의 전단결합강도가 가장 높았으며 AQ Bond를 사용한 군의 전단결합강도가 가장 낮았다.

• 한국전기전자재료학회논문지
• /
• 제23권12호
• /
• pp.988-995
• /
• 2010

In this study the (Alnico, Sm-Co) bonded magnets were fabricated by mixing the Sm-Co added alnico alloy powders with epoxy resin and binder, appropriately. Also, the hybrid ring magnets of (Alnico, Sm-Co)/Sr-ferrite were fabricated by coupling the Sr-ferrite composite layer with an (Alnico, Sm-Co) magnet. The magnetic properties of (Alnico, Sm-Co) ring magnets were varied with the amount of Sm-Co powders. The addition of Sm-Co powders increased a remanent induction($B_r$) and coercive force($_BH_C$), while decreasing a surface flux density and repulsive distance. The surface flux density and repulsive distance for the (Alnico, Sm-Co) ring magnet increased with a magnetizing voltage up to about 160 V and reached an apparent saturation point. Also, the measurements of temperature and moisture characteristics showed that the surface flux densities of N-S poles and repulsive distance decreased a little within 4% after 10 days passed.

• Restorative Dentistry and Endodontics
• /
• 제24권1호
• /
• pp.136-146
• /
• 1999

The purpose of this study was to estimate the changes of marginal adaptation to the cavity floor of light-cured glass ionomer cement base after application of a composite restoration. Eighty non-carious extracted human molars were used in the present study. Circular cavities were prepared on the center of the exposed dentin surface to 0.5mm, 1.0mm, 1.5mm, 2.0mm in depth and the prepared cavities were pretreated with Dentin conditioner and filled with Fuji II LC(GC Int. Co., Japan). They randomly assigned into 3 groups according to the difference in application of a composite restoration; Group 1(control group): only glass ionomer base, Group 2: The application of a composite restoration surrounded by dentin with class I cavity over glass ionomer base after conventional dentin bonding to the exposed dentin and glass ionomer base, Group 3: The application of composite restoration not-surrounded by dentin over glass ionomer base after conventional dentin bonding to the exposed dentin and glass ionomer base. To examine the interface between cavity floor and light-cured glass ionomer cement base, each groups were sectioned vertically through the center of restorations with diamond saw and the gap size(${\mu}m$) of interface measured by SEM. The results were analyzed by using One Way ANOVA. The results were as follows: 1. Good adaptation between glass ionomer cement base and cavity floor was showed in specimens with 0.5mm, 1.0mm depth base of control group. But in specimens with 1.5mm, 2.0mm depth base of control group, the gap was measured about $15{\mu}m$, $40{\mu}m$ respectively. 2. Gap size in group 2 was significantly higher than that in control group(P<0.05). 3. Gap size in group 3 was significantly higher than that in control group and group 2(P<0.05). 4. It was possible to observe the good adaptation between glass ionomer cement base and dentin which was intermediated with 4-10${\mu}m$ hybrid layer in specimens with 0.5mm, 1.0mm depth base of control group. Cohesive fracture within cement base was observed in all specimens which had the gap between glass ionomer cement base & dentin. 5. It was possible to observe the gap formation between cement base and bonding agent and between composite resin and dentin in all specimens of group 2.

• 한국응용과학기술학회지
• /
• 제29권1호
• /
• pp.141-148
• /
• 2012

본 연구에서는 초소수성 실리카 에어로겔을 이용하여 단열 성능을 갖는 투명 필름용 유/무기 복합 코팅물질을 제조하였다. 바인더 물질로 사용된 자외선 경화형 우레탄 아크릴레이트 수지와 에어로겔과의 상용성을 위해 계면활성제(Brij 56)를 이용하여 에어로겔의 표면을 개질하였다. 개질된 에어로겔을 고분자 수지와 복합화한 코팅 용액을 폴리카보네이트 기지재에 코팅한 후 자외선경화를 통해 코팅필름을 제조하였다. 에어로겔이 10 vol% 함량으로 첨가되었을 때, 코팅필름의 단열성능은 측정된 열전도도 기준으로 순수 기지재 대비 28% 정도로 향상되었다. 또한, 코팅필름의 광투과율은 에어로겔이 50 vol%로 과량 첨가된 경우에도 80% 이상 높은 수준을 유지하였으며, 우수한 접착성(5B) 및 연필 경도(4H)를 보여주었다.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2008년도 Spring Scientific Meeting(the 129th) of Korean Academy if Conservative Dentistry
• /
• pp.246-257
• /
• 2008

이 연구의 목적은 3차원 유한요소분석법을 사용하여 교합력의 위치와 방향이 상악 제2소구치의 치경부 복합레진 수복물의 응력분포에 미치는 영향에 대해 평가해 보고자 하였다. 발치된 상악 제2소구치를 이용하여 micro-CT (SkyScan1072; SkyScan, Aartselaar, Belgium)로 스캔한 후 HyperMesh Ver 6.0 (Altair Engineering, Inc., Troy, USA)와 3D-DOCTOR (Able Software Co., Lexington, MA, USA)로 3차원 유한요소 모형을 제작하였다. 제작된 소구치 모형에 쐐기형 와동을 형성하고 탄성계수가 서로 다른 혼합형 복합레진과 흐름성 복합레진으로 각각 수복하였다. 수복 후 설측교두의 협측사면 세 위치에 각각 수직, 20도, 40도의 각도로 하중을 가한 후 응력분포를 ANSYS Ver 9.0 (Swanson Analysis Systems. Inc., Houston, USA) 프로그램을 이용하여 인장 응력의 분포를 분석한 바 하중 위치와 관계없이 하중방향의 각도가 증가할수록, 또한 수복재료의 탄성 계수가 높을수록 인장응력도 증가하는 것으로 보아 교합력의 방향과 수복재료의 탄성계수가 치경부 수복물의 응력분포에 중요한 영향을 미치는 요소로 사료된다.

• Restorative Dentistry and Endodontics
• /
• 제33권3호
• /
• pp.246-257
• /
• 2008

이 연구의 목적은 3차원 유한요소분석법을 사용하여 교합력의 위치와 방향이 상악 제2소구치의 치경부 복합레진 수복물의 응력분포에 미치는 영향에 대해 평가해 보고자 하였다. 발치된 상악 제2소구치를 이용하여 micro-CT (SkyScan1072; SkyScan, Aartselaar, Belgium)로 스캔한 후 HyperMesh Ver 6.0 (Altair Engineering, Inc., Troy, USA)와 3D-DOCTOR (Able Software Co., Lexington, MA, USA)로 3차원 유한요소 모형을 제작하였다. 제작된 소구치 모형에 쐐기형 와동을 형성하고 탄성계수가 서로 다른 혼합형 복합레진과 흐름성 복합레진으로 각각 수복하였다. 수복 후 설측교두의 협측사면 세 위치에 각각 수직, 20도, 40도의 각도로 하중을 가한 후 응력분포를 ANSYS Ver. 9.0 (Swanson Analysis Systems. Inc., Houston, USA) 프로그램을 이용하여 인장 응력의 분포를 분석한 바 하중 위치와 관계없이 하중방향의 각도가 증가할수록, 또한 수복재료의 탄성계수가 높을수록 인장응력도 증가하는 것으로 보아 교합력의 방향과 수복재료의 탄성계수가 치경부 수복물의 응력분포에 중요한 영향을 미치는 요소로 사료된다.

• 대한소아치과학회지
• /
• 제31권3호
• /
• pp.527-533
• /
• 2004

저점도의 레진을 복합레진 수복물 위에 도포하는 것은 미세누출방지와 변연 완전성(integrity) 유지를 위한 한 방법이다. 하지만 장기간 관찰하면, 수복물은 저작압에 의한 영향을 받게 되는데, 저점도의 레진으로 수복물 변연부를 재접착(rebonding)하였을 때 저작압에 의한 응력에 견디면서 계속하여 수복물에 긍정적인 영향을 주는지에 대한 연구는 미흡한 실정이다. 본 연구는 부하순환(load cycling) 하에서 제V급 수복물의 미세변연누출에 대한 재접착제(rebonding agent)의 효과를 알아보고자 하였다. 40개의 건전한 소구치의 협면에 제V급 와동을 형성하고 제조사의 지시대로 광중합복합레진으로 수복하였다. 20개씩 무작위로 나누어 표면전색을 하지 않는 I군과 표면을 산부식 후 재접착한 II군으로 설정하였다. 열순환 후 각 군에서 10개씩의 하위군(A군=No load cycling군, B군=Load cycling군)으로 나누어 이중 B군의 시편에 1 Hz의 속도로 수직력이 4-100N까지 100,000회의 부하순환을 가하였다. methylene blue 용액에 침윤시켜 변연의 미세누출정도를 평가하여 다음과 같은 결과를 얻었다. 1. 교합변연에서는 재접착과 무관하게 유의한 차이가 없었다(IA-IIA군, IB-IIB군)(p>0.05). 2. 치은변연의 경우는 부하순환을 하지 않은 군의 경우 재접착을 한 군(IIA군)이 재접착을 하지 않은 군(IA군)에 비해 더 적은 미세누출결과를 보였다(p<0.05). 3. 치은 변연에서 부하순환을 시행한 군의 경우에는 재접착을 한 군(IIB군)과 재접착을 하지 않은 군(IB군)과 유의차가 없는 비슷한 미세누출의 결과를 보였다(p>0.05).