• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.613-621
• /
• 2012

Steel corrosion is one of the most critical deteriorations in concrete structures due to the problems associated with both durability and structural safety issues. For protection of steel against corrosion problems, researches to improve concrete durability and steel corrosion protection such as rebar coating by hot-dip galvanizing steel have been carried out. This study was performed to quantitatively evaluate anti-corrosion and structural performance of concrete structures reinforced with hot-dip galvanizing steel rebar. Preliminary tests for several metal coatings such as zinc, aluminum, and their alloy (Zn 45% + AL 55%) were performed. After evaluation of corrosive characteristics, Zn was selected for the coating material and the corrosion behaviors in Zn-coated steel were evaluated in various conditions. Furthermore, tensile and adhesive strengths were evaluated for the normal and the hot-dip galvanized steel. The crack patterns and structural behaviors of RC specimens with the normal and coated steel were investigated. Also, corrosion characteristics including corrosion in various coating metal and potential change in metal with notch were evaluated. Structural performances of tensile and adhesive strengths as well as RC beam behavior under flexural/shear loading were evaluated. The test and evaluation results showed that the applicability of hot-dip galvanized steel rebar can be used as corrosion resistant reinforcements for RC structures.

• KEPCO Journal on Electric Power and Energy
• /
• v.7 no.2
• /
• pp.237-240
• /
• 2021

Failure of a suspension clamp made of hot dip galvanized cast iron in 154kV transmission tower was investigated. Metallurgical analysis of a crack of the clamp was performed using a digital microscope, an optical microscope, and a scanning electron microscope. It was revealed that the crack surface was covered by continuous zinc layer. Distinctive casting skin was found underneath both the outer surface and crack surface. The result showed that pre-existing crack had been formed in the fabrication, and liquid metal embrittlement during hot dip galvanization may assist crack propagation.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.1
• /
• pp.27-32
• /
• 2015

Advanced high strength steels undergo recrystallization annealing in reducing gas atmosphere before galvanizing to improve mechanical properties. The selective oxidations of elements such as Mn, Si, Cr and Al during annealing decrease wettability of liquid zinc, resulting in bare spots and other defects. In this work, Fe-3wt%Mn steel sheet was annealed at $780^{\circ}C$ for 1200 sec. in 5% $H_2-N_2$ atmosphere and then dipped into zinc bath held at $460^{\circ}C$, which contained 0.2wt% dissolved Al. MnO crystallines in the average size of 200 nm were formed on the surface after annealing. It is estimated that MnO has been detached into bath with the formation and growth of inhibition layer with longer immersion time during galvanizing. No evidence of aluminothermic reduction of MnO has been found in this study.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.04a
• /
• pp.63-63
• /
• 2006

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2011.06a
• /
• pp.249-249
• /
• 2011

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2012.06a
• /
• pp.194-195
• /
• 2012

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.11a
• /
• pp.35-35
• /
• 2002

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.27 no.8
• /
• pp.1105-1113
• /
• 2003

In the gas wiping process of continuous hot-dip galvanizing, edge overcoating develops near the edge of the steel strip. The overcoating is supposed to occur due to the reduced impact pressure of wiping gas on the strip surface. The purpose of this study is to investigate the effect of edge vortex on the reduced impact pressure. Three-dimensional unsteady flows are simulated using a commercial code, STAR-CD. Standard k-$\varepsilon$ model is used as a turbulence model. It is found that an alternating vortex structure in the vicinity of strip edge is developed by buckling of opposed jet streams and that the reduced amount of impact pressure at strip edge becomes smaller as the air knife gets closer to the strip. The effect of edge baffle on the reduced impact pressure is also investigated.

• Korean Journal of Metals and Materials
• /
• v.49 no.4
• /
• pp.281-290
• /
• 2011

In order to gain better understanding of the selective surface oxidation and its influence on the galvanizability of a transformation-induced plasticity (TRIP) assisted steel containing 1.5 wt.% Si and 1.6 wt.% Mn, a model experiment has been carried out by depositing Si and Mn (each with a nominal thickness of 10 nm) in either monolayers or bilayers on a low-alloy interstitial-free (IF) steel sheet. After intercritical annealing at $800^{\circ}C$ in a $N_2$ ambient with a dew point of $-40^{\circ}C$, the surface scale formed on 590 MPa TRIP steel exhibited a microstructure similar to that of the scale formed on the Mn/Si bilayer-coated IF steel, consisting of $Mn_{2}SiO_{4}$ particles embedded in an amorphous $SiO_{2}$ film. The present study results indicated that, during the intercritical annealing process of 590 MPa TRIP steel, surface segregation of Si occurs first to form an amorphous $SiO_{2}$ film, which in turn accelerates the out-diffusion of Mn to form more stable Mn-Si oxide particles on the steel surface. During hot-dip galvanizing, particulate $Fe_{3}O_{4}$, MnO, and Si-Mn oxides were reduced more readily by Al in a Zn bath than the amorphous $SiO_{2}$ film. Therefore, in order to improve the galvanizability of 590 TRIP steel, it is most desirable to minimize the surface segregation of Si during the intercritical annealing process.

• 제어로봇시스템학회:학술대회논문집
• /
• 1995.10a
• /
• pp.323-327
• /
• 1995

A new air knife system for coating thickness control in hot dip galvanizing process had been developed and installed on the CGL in Pohang Steel Works, POSCO. This new system consists of air knives with remotely adjustable nozzle slot and an automatic control system which can control both longitudinal and traverse coating deviations. Based on the optimal control algorithm, a traverse coating deviation control was designed. The controller controls the lip profile of the air knives with flexible structure according to the deviation of coating weight. From the measured values which are dependent on the strip width, the lip gaps are calculated with optimal algorithm and the model of the coating deviation. Time delay between knives and a coating thickness gauge is solved by the Smith Predictor.