• Korean Chemical Engineering Research
• /
• v.47 no.1
• /
• pp.96-104
• /
• 2009

In order to lower a reaction temperature with high conversions for simultaneous catalytic reduction of NO and $N_2O$ over Pd-Rh supported mixed metal oxide honeycomb catalysts, $H_2$ or CO was utilized as a reductant. When using the reductants, the effects of reaction conditions were examined in NO and $N_2O$ conversions, where reaction temperatures, concentrations of the reductants and oxygen and the concentration ratio of $N_2O$ to NO were varied. In using $H_2$ reductant, larger than 50% of NO and $N_2O$ conversions was observed at the temperatures below $200^{\circ}C$ in absence of $O_2$. In using CO reductant, NO and $N_2O$ conversions increased from the temperatures higher than $200^{\circ}C$ and $300^{\circ}C$, respectively. However, in use of both reductants, NO and $N_2O$ conversions decreased with increasing oxygen concentration. As a result, $H_2$ reductant could reduce simultaneously NO and $N_2O$ at relatively lower reaction temperature than CO. Also, NO and $N_2O$ conversions were less influenced by using $H_2$ reductant than CO one. Concentration ratio between NO and $N_2O$ did not affect their conversions regardless the type of reductants. Pretreatment of the catalyst in $H_2$ was more effective in simultaneous reduction of NO and $N_2O$ at low reaction temperature than that in $O_2$.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.3
• /
• pp.321-328
• /
• 2011

The autothermal reforming reaction of methane was investigated to produce hyd rogen with Ni/$CeO_2-ZrO_2$, Ni/$Al_2O_3$-MgO and Ni-Ru/$Al_2O_3$-MgO catalysts. Honeycomb metalli c monolith was applied in order to obtain high catalytic activity and stability in autothermal r eforming. The catalysts were characterized by XRD, BET and SEM. The influence of various catalysts on hydrogen production was studied for the feed ratio($O_2/CH_4$, $H_2O/CH_4$). The $O_2/CH_4$ and $H_2O/CH_4$ ratio governed the methane conversion and temperature profile of reactor. Th e reactor temperature increased as the reaction shifted from endothermic to exothermic reactio n with increasing $O_2/CH_4$ ratio. Among the catalysts used in the experiment, the Ni-Ru/$Al_2O_3$-MgO catalyst showed the highest activity. The 60% of $CH_4$ conversion was obtained, and th e reactor temperature was maintained $600^{\circ}C$ at the condition of GHSV=$10000h^{-1}$ and feed ratio S/C/O=0.5/1/0.5.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.11
• /
• pp.5384-5391
• /
• 2011

The computational fluid dynamics was analyzed for the pressure distribution, stream velocity distribution, stream line field, retention time and temperature distribution which are applied to the catalyst layer in the RCO reactor to derive the optimum operating condition of the heat condensing type catalytic oxidation (RCO) reactor. The results from the computational analysis revealed that the pressure loss due to the ceramic honeycomb in the catalytic bed of the reactor which is operating currently is not significant and the stream velocity (1.8~2.7 m/s) after the ceramic filter is working in stability without big channeling. To improve the stream velocity distribution of the air stream, it is necessary to extension of the connecting range between the plenum and catalytic bed inside the facility. However, the method of attaching the air stream guide vane or the perforated plate inside the reactor was not so effective.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.252-256
• /
• 2015

Nitrogen oxides ($NO_X$) was emitted from flue gas of stationary sources and exhaust gas of mobile sources, can leads to various environments problems. Selective Catalysts Reduction (SCR) is the most effective $NO_X$ removal system. Commercial $V_2O_5-WO_3/TiO_2$ catalysts, usually containing $V_2O_5$ 0.5~3 wt%, $WO_3$ 5~10 wt%, and $V_2O_5$ is active in the reduction of $NO_X$ but also in the desired oxidation of $SO_2$ to $SO_3$. To reduce the amount of vanadium, using graphene matrix supported vanadium to synthesize nanocomposite. Then, we fabricated to 1 inch honeycomb type of SCR catalysts adding graphene-vanadium nanocomposite. The chemical-physical characteristics and the catalytic activity were performed by XRD, XRF, BET and Micro-Reactor (MR). As a result, the De-NOX performance was showed, similar to the commercial catalyst activity as 77.8 % and using nanocomposite catalyst as 77.1 % at $350^{\circ}C$.

• Proceedings of the SAREK Conference
• /
• 2008.11a
• /
• pp.363-368
• /
• 2008

Nitrogen oxides (NO, $NO_2$ and $N_2O$) have been controlled effectively by the SCR catalysts coated on monolith or honeycomb in commercial sites with ammonia as reductant at high temperature range $300{\sim}400^{\circ}C$. However, the catalytic filter has much merit on the point of controlling the particles and nitrogen oxides simultaneously. It will be more advanced-system if the catalytic working temperature is reduced to the normal filtration temperature of under $200^{\circ}C$. This study has focus on the development of the catalytic filter working at the low temperature. So the additive effect of the components such as Pt and Mn (which are known the catalytic component of $V_2O_5/TiO_2$ was investigated. The $V_2O_5-WO_3$ catalytic filter exhibited high activity and selectivity at $250{\sim}320^{\circ}C$ showing more than 95% NO conversion for the treatment of 600 ppm NO at face velocity 2 cm/s. The Pt-$V_2O_5-WO_3$ catalytic filter shifted the optimum working temperature towards the lower temperature ($170{\sim}200^{\circ}C$). And NO conversion was 100% and higher than that of $V_2O_5-WO_3$ catalyst at $250{\sim}320^{\circ}C$. The $MnO_X-V_2O_5-WO_3$ catalytic filter showed the wide temperature range of $220{\sim}330^{\circ}C$ for more than 95% NO conversion. This is a remarkable advantage when considered the $MnO_X$ catalytic filter presents the maximum activity at $150{\sim}250^{\circ}C$ and $V_2O_5-WO_3$ catalytic filter shows the maximum activity at $250{\sim}320^{\circ}C$.

• Korean Chemical Engineering Research
• /
• v.51 no.3
• /
• pp.319-324
• /
• 2013

The partial oxidation reaction of methane was investigated to produce syngas with $Ni/CeO_2-ZrO_2$, $Ni-Ru/CeO_2-ZrO_2$ and $Ni-Pd/CeO_2-ZrO_2$ catalysts. Honeycomb metallic monolith was applied in order to obtain high catalytic activity and stability in partial oxidation reforming. The catalysts were characterized by XRD and FE-SEM. The influence of various catalysts on syngas production was studied for the feed ratio (O/C), GHSV and temperature. Among the catalysts used in the experiment, the $Ni-Pd/CeO_2-ZrO_2$ catalyst showed the highest activity. The 99% of $CH_4$ conversion was obtained at the condition of T=$900^{\circ}C$, GHSV=10,000 $h^{-1}$ and feed ratio O/C=0.55. It was confirmed that $H_2$ yield increased slightly as O/C ratio increased, while CO yield remained almost constant. Also, $CH_4$ conversion decreased as GHSV increased. It was found that the safe range of GHSV for high $CH_4$ conversion was estimated to be less than 10,000 $h^{-1}$.

• Korean Chemical Engineering Research
• /
• v.62 no.1
• /
• pp.125-131
• /
• 2024

In this study, synthesized Ni/Ce_xZr_1-xO₂ catalysts were coated on the surface of honeycomb metalic monoliths to investigate catalytic activity in steam reforming of methane reactions. Supports with varying Ce/Zr ratios were synthesized to observe their behavior in the reforming reaction, and catalysts with Ni contents ranging from 5 wt% to 20 wt% were prepared to analyze the effect of Ni loading contents on catalytic activity. The catalysts were characterized by XRD, BET, TPR, and SEM. The TPR analysis indicated the formation of Ni-Ce-Zr oxide with a strong interaction between the active metal Ni and CeO₂-ZrO₂ support. The 15 wt% Ni/Ce_0.80Zr_0.20O₂ catalyst exhibited the highest activity and stability in the steam reforming of methane reaction. Catalysts with enhanced activity and stability were synthesized by manufacturing composite materials using excellent oxygen storage and donor properties of CeO₂ and the thermal properties of ZrO₂.