• Elastomers and Composites
• /
• v.47 no.3
• /
• pp.231-237
• /
• 2012

This study measured the mechanical and damping properties of EPDM compounds including fillers. Semi-reinforcing furnace black (SRF), high abrasion furnace black (HAF) and acetylene black were used as fillers. Dicumyl peroxide (DCP) were used as curing agents. The measurements were conducted using a moving die rheometer (MDR), durometer, universal testing machine (UTM), compression set and dynamic mechanical analysis (DMA). The tensile strength and elongation at break increased with increasing SRF contents in EPDM compounds. However, they decreased with increasing the amount of acetylene black. In the inspecting temperature range, EPDM compound filled acetylene black had stable storage modulus. Furthermore, the tan ${\delta}$ of the EPDM compounds obtained was enhanced by compounding with acetylene black.

• Journal of the Society of Naval Architects of Korea
• /
• v.38 no.1
• /
• pp.99-107
• /
• 2001

Manufacture of fishing vessel is needed the effective material for light, strength, fire and corrosion of water in order to improve durability by high-speed and fishing. These fishing vessel can be divided into FRP and AI alloys fishing vessel. FRP fishing vessel is light and effective for strength but highly ignited and susceptible to heat during the manufacturing ship by-produce noxious component for human. In the case of a scrapped ship, it cause environmental pollution. On the other hand, aluminum is a material in return for FRP and has merit of high-strength and lightness. It's more heat proof and durable than FRP and superior to prevent from corrosion. Al alloys fishing vessel development is rising as an urgent matter. But, al alloy has some defect of bad weldability, welding transformation, cracks and overcost of construction. Therefore this study is to develop the new welding joint shape solving aluminum defects and mechanical behavior. First of all, strength was compared and reviewed by analysis of plate, stiffen plate, new model simplified by using plate theory. On the base of this result, plate and new model of temperature distribution, weld residual stress and strength of tensile, compressive force were compared and reviewed by finite element computer program has been developed to deal with heat conduction and thermal elasto plastic problem. Also, new model is proved application possibility and excellent mechanic by strength comparison is established to tensile testing result.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.9
• /
• pp.27-33
• /
• 2016

Phenolic resin has excellent heat resistance and good mechanical properties as a thermosetting resin. However, its thermosetting characteristics cause it to produce a non-recyclable waste in the form of sprue and runner which is discarded and represents up to 15~20% of the overall products. Forty thousand tons of phenolic resin sprue and runner are disposed of (annually). The (annual) cost of such domestic waste disposal is calculated to be 20 billion won. In this study, discarded phenol resin scraps were pulverized and treated by silanes to improve their interfacial adhesion with HDPE. The sizes of the pulverized pulverulent bodies and fine particles were (100um~1000um) and (1~100um), respectively. The pulverized phenol resin was treated with 3-(methacryloyloxy) propyltrimethoxysilane and vinyltrimethoxy silane and the changes in its characteristics were evaluated. The thermal properties were evaluated by DSC and HDT. The mechanical properties were assessed by a notched Izod impact strength tester. When the silane treated phenol resin was added, the heat distortion temperature of HDPE increased from $77^{\circ}C$ to $96^{\circ}C$ and its crystallinity and crystallization temperature also increased. Finally, its impact strength and tensile strength increased by 20% and 50%, respectively, in comparison with the non-treated phenol resin.

• Korean Journal of Materials Research
• /
• v.28 no.12
• /
• pp.763-768
• /
• 2018

In this study, glass fibers are fabricated via a continuous spinning process using manganese slag, steel slag, and silica stone. To fabricate the glass fibers, raw materials are put into an alumina crucible, melted at $1550^{\circ}C$ for 2 hrs, and then annealed at $600^{\circ}C$ for 2 hrs. We obtain a black colored glass. We identify the non-crystalline nature of the glass using an XRD(x-ray diffractometer) graph. An adaptable temperature for spinning of the bulk marble glass is characterized using a high temperature viscometer. Spinning is carried out using direct melting spinning equipment as a function of the fiberizing temperature in the range of $1109^{\circ}C$ to $1166^{\circ}C$, while the winder speed is in the range of 100rpm to 250rpm. We investigate the various properties of glass fibers. The average diameters of the glass fibers are measured by optical microscope and FE-SEM. The average diameter of the glass fibers is $73{\mu}m$ at 100rpm, $65{\mu}m$ at 150rpm, $55{\mu}m$ at 200rpm, and $45{\mu}m$ at 250rpm. The mechanical properties of the fibers are confirmed using a UTM(Universal materials testing machine). The average tensile strength of the glass fibers is 21MPa at 100rpm, 31MPa at 150rpm, 34MPa at 200rpm, and 45MPa at 250rpm.