• Advances in concrete construction
• /
• v.10 no.5
• /
• pp.443-454
• /
• 2020

In recent years, many studies have been done on the performance of concrete containing glass powder (GP). For the purpose of widespread use of GP in concrete mixes, a knowledge of the performance of such a mixture after a fire is essential for the perspective of structural use. This research work was carried out to evaluate the performance of High Performance Concrete (HPC) made with GP after being exposed to elevated temperature. The studied mixtures include partial replacement of cement by GP with up to 30%. The mechanical performance and structural alterations were assessed after high temperature treatment from 200℃ to 800℃. The mechanical performance was evaluated by testing the specimens to the compressive and tensile strength. In addition, the mass loss and the porosity were measured to notice the structural alterations. Changes in microstructure due to temperature was also investigated by the X-ray diffraction (XRD) and thermal gravimetric analyses (TGA) as well as porosity adsorption tests. The results of the concrete strength tests showed a slight difference in compressive strength and the same tensile strength performance when replacing a part of the cement by GP. However, after high temperature exposition, concrete with GP showed better performance than the reference concrete for temperature below 600℃. But, after heating at 800℃, the strength of the concrete with GP drop slightly more than reference concrete. This is accompanied by an important increase in mass loss and water porosity. After the microstructure analysis, no important changes happened differently for concrete with GP at high temperature except a new calcium silica form appears after the 800℃ heating.

• Carbon letters
• /
• v.16 no.3
• /
• pp.203-210
• /
• 2015

This study fabricated low thermal conductive polyacrylonitrile (PAN)-based carbon fibers containing cellulose particles while maintaining their mechanical properties. The high thermal conductivity of carbon fibers limits their application as a high temperature insulator in various systems such as an insulator for propulsion parts in aerospace or missile systems. By controlling process parameters such as the heat treatment temperature of the cellulose particles and the amount of cellulose added, the thermal and mechanical properties of the PAN-based carbon fibers were investigated. The results show that it is possible to manufacture composite carbon fibers with low thermal conductivity. That is, thermal conductivities were reduced by the cellulose particles in the PAN based carbon fibers while at the same time, the tensile strength loss was minimized, and the tensile modulus increased.

• Journal of Korea Foundry Society
• /
• v.19 no.6
• /
• pp.456-465
• /
• 1999

The overall objective of this study is to investigate the effect of Ag addition on the mechanical properties and microstructure of rapid solidified 7000 Al series alloys. Al-Zn-Mg-Cu alloys with small amounts of Ag was fabricated into the powder by gas atomization. The powder was extruded after the cold compaction and degassing and then followed by T6 heat treatment. Microstructure observation, phase analysis, room and high temperature tensile test and hardness test were pursued. The tensile strength and hardness of Ag-added alloy after heat treatment was increased with increasing Ag contents. However, the elongation of extruded alloys was not increased as much as to be expected. The reason of this result seems to be related to $the{\Omega}$ phase, which contribute to the high temperature strength stability of Al-Cu-Zn alloys through the formation of eutectoid with Ag addition.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.181-186
• /
• 2001

JLF-1 steel (Fe-9Cr-2W-V-Ta), low activation ferritic steel, is one of the promising candidate materials fer fusion reactor applications. High temperature fatigue life and tensile strength of JLF-1 steel and its TIG welded joints were investigated at the room temperature and $400^{\circ}C$. The strength of base metal (JLF-1) is in between those of weld metal and the HAZ. When the test temperature was increased from room temperature to $400^{\circ}C$, both strength and ductility decreased for base metal, weld metal and the HAZ. The longitudinal specimens of base metal showed similar strength and ductility compared with those of the transverse specimens at room temperature and $400^{\circ}C$. Little anisotropy was observed in the JLF-1 steel base metal in terms of rolling direction. Fatigue limit of weld metal which was obtained from cross-weld specimen is 495MPa. Thus, the weld metal showed the higher fatigue limit than those of base metal at both room temperature and $400^{\circ}C$. Little anisotropy of fatigue properties was observed for JLF-1 base metal in terms of rolling direction. When the test temperature was increased from room temperature to $400^{\circ}C$, the fatigue limit of both base metal and weld metal decreased substantially.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.2
• /
• pp.199-204
• /
• 2013

Owing to the global energy crisis, studies have strongly focused on realizing energy savings through vehicle weight reduction using light metal alloys or polymer composites. Polymer composites afford many advantages including enabling the fabrication of complex shapes by injection molding, and glass and carbon fibers offer improved mechanical properties. However, the high temperature in an engine room and the high humidity during the rainy season can degrade the mechanical properties of the polymer. In this study, the mechanical properties of injection-molded glass-fiber-reinforced polymer were assessed at a temperature of $85^{\circ}C$ and the maximum moisture absorption conditions. The result showed a 23% reduction in the maximum tensile strength under high temperature, 30% reduction under maximum moisture absorption, and 70% reduction under both heat and moisture conditions. For material selection during the design process, the effects of high temperature and high humidity should be considered.

• Fashion & Textile Research Journal
• /
• v.14 no.6
• /
• pp.1024-1031
• /
• 2012

The thermal bonding PET fabrics were produced through high temperature steaming (HTS) of low melting PET yarn as warp and composite fancy yarn containing low melting PET yarn as weft. The low melting PET yarn of sheath-core structure consisted of a regular PET in core portion and low melting PET in sheath portion. The composite fancy yarn consisted of regular PET yarn as inner part and effect part and low melting PET yarn as binding part. This study was carried out to investigate the melting behavior of thermal bonded PET fabric, the effect of HTS on the thermal bonding, mechanical properties, and dyeing properties. The melting peak of low melting PET yarn showed two melting peaks caused by sheath-core structure. Almost the entire thermal bonding of the fancy PET fabrics containing low melting PET yarn has formed at $200^{\circ}C{\times}3min$ of HTS. The tensile strength in warp and weft direction of the fancy PET fabrics slightly decreased as temperature of HTS increased. The total K/S value of the fancy PET fabrics decreased slightly to $180^{\circ}C{\times}3min$ of HTS, while increased slightly above $200^{\circ}C{\times}3min$ of HTS. The changes in the hue angle ($H^{\circ}$) of the thermal bonded fancy PET fabrics dyed with disperse dyes hardly ever happened.

• Journal of Korea Foundry Society
• /
• v.13 no.2
• /
• pp.187-193
• /
• 1993

In this study, it was examined the relationship between the microstructure, fatigue properties, mechanical properties and retained austenite volume of Mo-Ni ADI corresponding to various austempering temperatures. When the austempering temperature is increased to $370^{\circ}C$, acicular bainite structure was found to be transformed to feathery bainite structure. But at the austempering temperature of $420^{\circ}C$, the dissolved bainite lath was showned. Up to the austempering temperature of $370^{\circ}C$, the volume of retained austenite was increased. However at the austempering temperature of $420^{\circ}C$ a large amount of retained austenite was decreased. In this study, the retained austenite volume was determined by XRD(X-ray diffraction). It was observed that the optimum fatigue properties can be obtained at the condition of austempering temperature $370^{\circ}C$. Under the such conditions, fatigue limit determined as the value of 290 MPa, tensile strength 877MPa elongation 6%, hardness 285(BHN), impact values(CVN) 9.2J and retained austenite volume 30.3%, respectively.

• Journal of the Korean Society for Precision Engineering
• /
• v.24 no.1 s.190
• /
• pp.57-63
• /
• 2007

Wire drawing process of the high carbon steel with a high speed is usually conducted at room temperature using a number of passes or reductions through consequently located dies. In the multi-pass drawing process, temperature rise in each pass affects the mechanical properties of the final product such as bending, torsion, and tensile property, etc. This temperature rise during the deformation promotes the occurrence of delamination, and deteriorates the torsion property and durability of wire. This study investigates the occurrence of delamination in the wire through the torsion test and the evaluation of wire temperature. The excessive wire temperature leads to the occurrence of the delamination. Based on the calculation of the wire temperature, a new pass schedule, which can prevent the delamination due to the excessive wire temperature rise, is designed through the isothermal pass schedule.

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.4
• /
• pp.399-406
• /
• 2005

Alloy 625 is used widely in industrial applications such as aeronautical aerospace, chemical, petrochemical and marine applications. Because of a good combination of yield strength. tensile strength, creep strength, excellent fabricability, weldability and good resistance to high temperature corrosion on prolonged exposure to aggressive environments. High qualify weldments for this material are readily produced by commonly used processes. But all of processes are not applicable to this material by reason of unavailability of matching, position or suitable welding filler metals and fluxes may limit the choice of welding processes. Recently, the flux cored wire is developed and applied for the better productivity in several welding position including the vortical position. In this study. the weldability and weldment characteristics of Alloy 625 are evaluated in FCAW weld associated with the several shielding gases($80\%Ar+20\%\;CO_2,\;50\%Ar+50\%\;CO_2.\;100\%\;CO_2$) in viewpoint of welding productivity. The results of the experimental study on corrosive characteristics of Alloy 625 are as follows; There is no remarkable difference among shielding gases. however they has a striking difference among corrosive solutions by results of distinguished density and time of corrosive solution. Generally, the shielding gases($80\%Ar+20\%\;CO_2$) was superior to the other gases on high temperature tensile and a low temperature impact. but all of the shield gases were making satisfactory results on corrosion test.

• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.4_2
• /
• pp.585-589
• /
• 2023

Unlike general carbon steel, stainless steel's mechanical properties change depending on the content of chromium and nickel. In this study, since stainless steel for high-temperature pressure container parts is used as shafts, the fatigue strength and fatigue limit of the materials were evaluated using a rotational bending fatigue test. Meanwhile, fatigue analysis was conducted under the same conditions as the specimen for structural analysis and fatigue analysis of stainless steel for high-temperature pressure container parts. Using the fatigue analysis results, we tried to derive the life of the material and the safety factor for each part. As a result of performing a fatigue test by processing a specimen for the fatigue test of A182 F6A stainless steel, the fatigue limit was 548 MPa. The ratio between the tensile strength and fatigue limit of the material was 0.545, representing 54.5% of the tensile strength.