• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.3
• /
• pp.121-126
• /
• 2014

High-nitrogen Fe-18Mn-18Cr-N austenitic steels with higher yield strength have been recently developed and used for generator retaining rings because they have non-magnetic, high strength, high ductility, and good corrosion resistance. In the present study, a high-nitrogen Fe-18Mn-18Cr-0.61N austenitic steel was fabricated and then tensile and Charpy impact tests were conducted on them in order to investigate the effect of cold working on the mechanical properties. Although the yield and tensile strengths usually increased with cold working, the ductility and impact toughness significantly decreased after cold working. On the other hand, the high-nitrogen austenitic steel exhibited a ductile-brittle transition due to unusual brittle fracture at low temperatures despite having a face-centered cubic structure. The ductile-brittle transition temperature obtained from Charpy impact tests could be remarkably increased by $60^{\circ}C$ after 20% cold working because of the enhanced cleavage-like brittle fracture.

• Transactions of Materials Processing
• /
• v.15 no.2 s.83
• /
• pp.112-117
• /
• 2006

Sliding wear mechanism of a high nitrogen austenitic 18Cr-18Mn-2Mo-0.9N steel has been investigated. Dry sliding wear tests of the steel were carried out at various loads of IN-10N under a constant sliding speed condition of 0.15m/s against AISI 52100 bearing steel balls. Solution ($1050^{\circ}C$) and isothermal aging ($900^{\circ}C$) heat treatments were performed on the steel and the effect of the heat treatments on the wear was investigated. Wear rates of the solution-treated steel specimen remained low until 5N load, and then increased abruptly at loads above 5N. The rates of isothermally aged specimens were low and increased gradually with the applied load. Worn surfaces, their cross sections, and wear debris of the steel specimens were examined with a scanning electron microscopy. Phases of the heat-treated specimen and the wear debris were identified using XRD. The transformed phase underneath a sliding track was investigated and analyzed using a TEM. Effects of the phase transformation during the wear and $Cr_{2}N$ precipitates formed during the isothermal aging on the wear of the austenitic steel were discussed.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.105-108
• /
• 2005

Sliding wear mechanism of a high nitrogen austenitic 18Cr-18Mn-2Mo-0.9N steel has been investigated. Dry sliding wear tests of the steel were carried out at various loads of 1N-10N under a constant sliding speed condition of 0.15m/s against AISI 52100 bearing steel balls. Solution $(1050^{\circ}C)$ and isothermal aging $(900^{\circ}C)$ heat treatments were performed on the steel and the effect of the heat treatments on the wear were investigated. Wear rates of the solution-treated steel specimen remained low until 5N, and then increased abruptly at loads above 5N. The rates of isothermally aged specimens were low and increased gradually with the applied load. Worn surfaces, their cross sections, and wear debris of the steel specimens were examined with a scanning electron microscopy. Phases of the heat-treated specimen and the wear debris were identified using XRD. Phases transformed underneath the sliding track during the wear were investigated and analyzed using TEM. Effects of the phase transformation during the wear and $Cr_2N$ precipitates formed during the isothermal aging on the wear of the austenitic steel were discussed.

• Journal of Power System Engineering
• /
• v.16 no.3
• /
• pp.51-56
• /
• 2012

The effect of deformation induced martensite transformation on the mechanical properties in austenitic stainless steel with high Mn was studied. ${\alpha}$'-martensite was formed by deformation in austenitic stainless steel with high Mn. Deformation induced ${\alpha}$'-martensite was formed with surface relief by cold rolling. With the increase of deformation degree, volume fraction of deformation induced martensite was increased rapidly in early stage of deformation and then, increased slowly. With the increase of deformation degree, hardness and tensile strength were rapidly increased with linear relations, while elongation was rapidly decreased and then slowly decreased. Hardness, tensile strengths and elongation were influenced strongly by deformation induced martensite.

• Korean Journal of Materials Research
• /
• v.29 no.3
• /
• pp.189-195
• /
• 2019

The effect of C, Mn, and Al additions on the tensile and Charpy impact properties of austenitic high-manganese steels for cryogenic applications is investigated in terms of the deformation mechanism dependent on stacking fault energy and austenite stability. The addition of the alloying elements usually increases the stacking fault energy, which is calculated using a modified thermodynamic model. Although the yield strength of austenitic high-manganese steels is increased by the addition of the alloying elements, the tensile strength is significantly affected by the deformation mechanism associated with stacking fault energy because of grain size refinement caused by deformation twinning and mobile dislocations generated during deformation-induced martensite transformation. None of the austenitic high-manganese steels exhibit clear ductile-brittle transition behavior, but their absorbed energy gradually decreases with lowering test temperature, regardless of the alloying elements. However, the combined addition of Mn and Al to the austenitic high-manganese steels suppresses the decrease in absorbed energy with a decreasing temperature by enhancing austenite stability.

• Korean Journal of Materials Research
• /
• v.23 no.9
• /
• pp.483-488
• /
• 2013

Over the past few decades, high-nitrogen austenitic steels have steadily received greater attention since they provide a unique combination of high strength and ductility, good corrosion resistance, and non-magnetic properties. Recently, highnitrogen 18Mn-18Cr austenitic steels with enhanced strength have been developed and widely used for generator retaining rings in order to prevent the copper wiring from being displaced by the centrifugal forces occurring during high-speed rotation. The high-nitrogen austenitic steels for generator retaining ring should be expanded at room temperature and then stress relief annealed at around $400^{\circ}C$ to achieve the required mechanical properties. In this study, four kinds of high-nitrogen 18Mn-18Cr austenitic steels with different nitrogen content were fabricated by using a pressurized vacuum induction melting furnace, and then the effects of nitrogen content, cold working, and stress relieving on tensile properties were investigated. The yield and tensile strengths increased proportionally with increasing nitrogen content and cold working, and they further increased after stress relieving treatment. Based on these results, a semi-empirical equation was proposed to predict the tensile strength of highnitrogen 18Mn-18Cr austenitic steels for generator retaining rings. It will be a useful for the effective fabrication of high-nitrogen 18Mn-18Cr austenitic steels for generator retaining rings with the required tensile properties.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2001.05a
• /
• pp.332-337
• /
• 2001

The objective of research is to clarify the interaction between dislocations and precipitates during high temperature creep deformation behaviors of high Mn austenitic steels. After measuring the internal stress in minimum creep rate at 873K, a transmission electron microscope (TEM) observation was performed to investigate the interaction between dislocations and precipitates during high temperature creep deformation. The band width of effective stress and internal stress increased when the nitride precipitates distribute more densely. Fine nitrides disturbed the dislocation movement with pinning the dislocations and perfect dislocations were separated into Shockley partial dislocations by fine nitrides. Coarse nitrides disturbed the dislocation movement with climb mechanism.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.4
• /
• pp.277-287
• /
• 1994

The effect of grain size on the tensile properties and fatigue behavior of austenitic high Mn steel has been investigated. The recrystallized austenite grain size of the cold rolled high Mn steel was increased as the annealing temperature increased from $600^{\circ}C$ to $1000^{\circ}C$. Larger austenite grain size decreased the yield strength and the tensile strength, and increased the uniform elongation due to transformation of some austenite into twins or E-martensite phase during deformation. Austenite grain refinement increased the tendency to form dislocation cells, instead. The specimen annealed at $1000^{\circ}C$ with large grain size showed lower fatigue crack propagation rate in low ${\Delta}K$ region due to rougher fracture surface caused by formation of deformation twins during fatigue at the crack tip region.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.3
• /
• pp.58-62
• /
• 2001

The objective of research is to clarify the interaction between dislocations and precipitates during high temperature creep deformation behaviors of high n austenitic steels. After measuring the internal stress in minimum creep rate state under applied stress of 236MPa at 873K, a transmission electron microscope (TEM) observation was performed to investigate the interaction between dislocations and precipitates during high temperature creep deformation. The band widths and values of internal stress increased when the nitride precipitates distribute more densely. Fine nitrides disturbed the dislocation movement with pinning the dislocations and perfect dislocations were separated into Shockley partial dislocations by fine nitrides. Coarse nitrides disturbed the dislocation movement with climb mechanism.

• Journal of Ocean Engineering and Technology
• /
• v.27 no.4
• /
• pp.9-13
• /
• 2013

The tensile properties of high manganese austenitic stainless steel with the two phase structures of deformation-induced martensite and reversed austenite were studied. Reversed austenite with an ultra-fine grain size of less than $0.3{\mu}m$ was obtained by reversion treatment. The two phases structures of deformation-induced martensite and reversed austenite were obtained by an annealing treatment in the range of $500^{\circ}C-700^{\circ}C$ for various times in 70% cold- rolled high-manganese austenitic stainless steel. The volume fraction of the reversed austenite increased rapidly with increases in the annealing temperature and time. In the stainless steel with the two phases of austenite and martensite, the strength decreased rapidly, while the elongation increased slowly and then rapidly increased with an increase in the volume fraction of the reversed austenite. Therefore, the strength and elongation were strongly controlled by the volume fraction of reversed austenite. A good combination of high strength and elongation could be obtained by the mixed structure of reversed austenite and deformation-induced martensite.