• 한국초전도ㆍ저온공학회논문지
• /
• 제24권4호
• /
• pp.55-58
• /
• 2022

Carbon-based doping to MgB₂ superconductor is the simplest approach to enhance the critical current densities under magnetic fields. Carbon quantum dots is synthesized in this work as a carbon provider to MgB₂ superconductors. Polyvinyl Pyrrolidone is pyrolyzed and dispersed in dimethylfomamide solvent as a dopant to the mixture of Mg and B powders. Doped MgB₂ bulk samples clearly show the decrease of a-axis lattice constant, grain refinements, and broadening of FWHM of diffraction peaks compared to un-doped MgB₂ possibly due to the carbon substitution and/or boron vacancy at the boron site in MgB₂ lattice. Also, high-field J_c for the doped MgB₂ is enhanced significantly with the crossover about 3 T at 5 & 20 K when increasing the doping of carbon quantum dots.

• 한국재료학회지
• /
• 제2권3호
• /
• pp.197-201
• /
• 1992

고은 초전도체 $Y_{1-X}Sm_{x}Ba_{2}Cu_{3}O_{7-y}$(x=0, 0.2, 0.4, 0.6, 0.8, 1.0)의 시료들을 제조하여 온도에 따른 자기 모우먼트를 측정하였다. 또한 자화율과 자기 임계전류밀도 같은 30K의 온도에서 자기이력 곡선으로부터 구하였다. 자화율 측정 결과로부터 고온 초전도상의 양이 14.7~49.175 범위에 있었으며, 입계전류밀도의 값은 $10^{3}~10^{4}A/cm^2$범위에 있었다. 그리고 침투깊이는 간섭성 길이보다 대략90배 정도 큼을 알 수 있었다

• 한국자기학회지
• /
• 제2권3호
• /
• pp.228-232
• /
• 1992

고온초전도체 $Y_1Ba_2Cu_3O_{7-y}$의 grain을 높은 자기장에서 정렬시켜 여러가지 자기적 특성을 조사하였다. Grain이 정렬된 초전도체는 단결정과 같이 Cu-O layer에 수직, 수평 방향에 대해 자기이방성을 가진다. 2~77 K의 온도영역에서 측정한 lower critical field$(H_{c1})$은 온도가 증가하면서 선형적으로 감소하였는데, Cu-O layer에 대하여 외부 자기장이 수직인 경우가 더욱 급격히 감소하였다. 온도변화에 따른 자율화$(4{\pi}\;X)$의 측정으로부터 극저온의 자화율이 -1에 가까운 값을 가진다는 것을 알 수 있었다. 또한 이 자화 곡선을 London의 공식과 two-fluid model을 이용해 최소자승법으로 fitting하여 절대 영도에서 침투깊이$({\lambda}_0)$를 구하였다. 또한 2 K에서 외부 자기장에 따른 자화곡선을 측정하였으며, Bean의 critical state model을 이용한 임계전류밀도$(J_c)$의 계산으로부터 grain내부는 단결정 수준의 높은 $(J_c)$를 가지고 있음을 알 수 있었다.

• 한국재료학회지
• /
• 제32권2호
• /
• pp.66-71
• /
• 2022

In this article, Pb₂Ba_1.7Sr_0.3Ca₂Cu₃O_10+δ superconductor material was synthesized using conventional solid-state reaction method. X-ray diffraction (XRD) analysis demonstrated one dominant phase 2223 and some impurities in the product powder. The strongest peaks in the XRD pattern were successfully indexed assuming a pseudo-tetragonal cell with lattice constants of a = 3.732, b = 3.733 and c = 14.75 Å for a Pb-Based compound. The crystallite size and lattice strain between the layers of the studied compound were estimated using several methods, namely the Scherrer, Williamson-Hall (W.H), size-strain plot (SSP) and Halder Wagner (H.W) approach. The values of crystallite size, calculated by Scherrer, W.H, SSP and H.W methods, were 89.4540774, 86.658638, 87.7555823 and 85.470086 Å, respectively. Moreover, the lattice strain values obtained by W.H, SSP and H.W methods were 0.0063240, 0.006325 and 0.006, respectively. It was noted that all crystallite size results are consistent; however, the best method is the size-strain plot because it gave a value of R² approaching one. Furthermore, degree of crystallites was calculated and found to be 59.003321%. Resistivity analysis suggests zero-resistance, which is typical of superconducting materials at critical temperature. Four-probe technique was utilized to measure the critical temperature at onset T_c(onset), zero resistivity T_{c(off set)}, and transition (width ΔT), corresponding to temperatures of 128 K, 116 K, and 12 K, respectively.

• Journal of information and communication convergence engineering
• /
• 제1권2호
• /
• pp.63-66
• /
• 2003

High $T_c$ superconducting lines will be applied as key materials in the areas of power transmission line; magnetic levitation of vehicle; magnetic separation; magnetic energy storage and marine propulsion. A combination method of electrophoresis deposition and zone-melting for preparation of YBaCuO tape is proposed. The submicron particle powder of YBaCuO made by sol-gel method is used in the electrophoresis process. A 40∼50 ${\mu}\textrm{m}$ thickness of YBaCuO film on Ag plate could be deposited in about three minutes. After deposition the film is rolled and heat treated in order to increase the density and the adhesion of the film to the Ag plate. Silver(Ag) and lead oxide(PbO) were added in the YBaCuO powder in order to reduce its melting point. The YBaCuO coating with controlled Ag and PbO contents was preliminarily zone-melted at about $945^{\circ}C$.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 추계학술발표대회 개요집
• /
• pp.262-264
• /
• 2005

$Bi_{2}Sr_{2}CaCu_{2}O_{x}$(Bi-2212) and $Bi_{2}Sr_{2}Ca_{2}Cu_{3}O_{y}$(Bi-2223) high-$T_{c}$ superconductor(HTS) coating have been prepared by plasma spraying and heaat treatment. The Bi-2212 HTS coating later is synthesized through the peritectic reaction between Sr-Ca-Cu oxide coating layer and Bi-Cu oxide coating later, and $Bi_{2}Sr_{2}CaCu_{2}O_{y}$(Bi-2212) superconducting phase grow by partial melting process. The superconducting characteristic depends strongly on the conditions of the partial melting process. the Bi-2212 HTS layer consists of the whiskers grown in the diffusion direction. Above the 2212 layer, Bi-2223 phase and secondary phase was observed. The secondary phase is distributed uniformly over the whole surface. This is caused to the microcrack on the coatings surface. Despite everything, the film shows superconducting with an onset $T_{c}$ of about 115K. There are two changes steps. One changes (1step) at 115K is due to the diamagnetism of the Bi-2223 phase and the other changes (2step) at 78K is due to the diamagnetism of the Bi-2212 phase.

• 한국초전도ㆍ저온공학회논문지
• /
• 제21권2호
• /
• pp.40-44
• /
• 2019

In this study, the effects of the compaction method for (Mg+2B) powders on the apparent density and superconducting properties of $MgB_2$ bulk superconductor were investigated. The raw powders used in this study were nano-sized boron (B) and spherical magnesium (Mg). A batch of a powder mixture of (Mg+2B) was put in a steel mold and uniaxially pressed at 1 ton or 3 tons into pellets. Another batch of the powder mixture was uniaxially pressed at 1 ton and then pressed isostatically at $1800kg/cm^2$ in the water chamber. All pellets were heat-treated at $650^{\circ}C$ for 1 h in flowing argon gas for the formation of $MgB_2$. The apparent density of powder compacts pressed at 3 ton was higher than that at 1 ton. The cold isostatic pressing (CIP) in a water chamber allowed further increase of the apparent density of powder compacts, which influenced the pellet density of the final products ($MgB_2$). The compaction methods (uniaxial pressing and CIP) did not affect the formation of $MgB_2$ and superconducting critical temperature ($T_c$) of $MgB_2$, but affected the critical current density ($J_c$) of $MgB_2$ significantly. The sample with the high apparent density showed high $J_c$ at 5 K and 20 K at applied magnetic fields (0-5 T).

• 한국초전도ㆍ저온공학회논문지
• /
• 제11권2호
• /
• pp.1-6
• /
• 2009

We report a successful fabrication of $high-J_c\;NdBa_2Cu_3O_{7-{\delta}}$ (NdBCO) films on $SrTiO_3$(STO) (100) substrates by pulsed laser deposition (PLD) in a relatively wide processing window. Under various oxygen pressures controlled by either 1%$O_2$/Ar mixture gas or pure $O_2$ gas, strongly c-axis oriented NdBCO films were grown at the substrate temperature $(T_s)\;of\;800^{\circ}C$ in 800 mTorr with 1%$O_2$/Ar gas and also in 400 and 800 mTorr with pure $O_2$ gas. These samples exhibited $T_c$ values over 90K and $J_c$ values of $2.8-3.5MA/cm^2$ at 77K in self-field (77K, sf). On the other hand, $J_c$ values over $1A/cm^2$ were obtained at the temperature regions of $700-830^{\circ}C$ in 800 mTorr with 1%$O_2$/Ar gas at those of $750-830^{\circ}C$ in 800 mTorr with pure $O_2$ gas. Unlike previous reports, resent results support that the PLD processing window for high-Jc NdBCO films is not narrow.

• Progress in Superconductivity
• /
• 제6권1호
• /
• pp.89-94
• /
• 2004

The policrystalline$SmBa_2$$Cu_2$$O_{y}$ was synthesized by the solid state reaction method. The dependence of AC susceptibility on temperature and applied ac field was studied. The critical temperature $T_{c}$ is about 92 K. As the ac field is increased, the slope and the value of real part of susceptibility become smaller and the peak position of imaginary part $T_{P}$ was shifted to a lower temperature with peak broadening. Using Bean's model, we determined intergrain critical current density $J_{c}$ and obtained $44 A/{cm}^2$ at 75 K. From the relation of the $J_{c}$ (T)=($1-T/T_{c}$ )$^{\beta}$ we obtained $\beta$=0.8 and found that the Josephson junction type of the $SmBa_2$$Cu_2$$O_{y}$ is SIS junction. The peak of the imaginary part shifts to higher temperature with increasing frequency, f. from Arrhenius plot, we obtained the activation energy of about 0.96 eV.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.222-225
• /
• 2000

BSCCO thin films have been fabricated by co-deposition at an ultralow growth rate using ion beam sputtering(IBS) method. Bi 2212 phase appeared in the temperature range of 750 and $795^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785^{\circ}C$. Whereas, $Po_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with $T_c$ (onset) of about 90 K and $T_c$(zero) of about 45 K is obtained. Only a smd amount of CuO in some films was observed as impurity, and no impurity phase such as $CaCuO_2$ was observed in d of the obtained films.