• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.51-52
• /
• 2011

This study is to propose a curing method for a concrete wall structure under severe cold climate. The curing methods of using heated cable, heated panel and insulated form were applied. Results showed that the concrete cured by the heated cable resulted in the highest temperature history and the highest strength development at 28 days. Further, it is believed that the curing methods of the heated panel and insulated form are also recommendable for the resistance of the early frost damage on the concrete in practice.

• Computers and Concrete
• /
• v.19 no.1
• /
• pp.33-39
• /
• 2017

In this study, two types of aggregate were used for making self-compacting concrete. Standard cubic specimens were exposed to different temperatures. Seventy-two standard cylindrical specimens ($150{\times}300mm$) and Seventy-two cubic specimens (150 mm) were tested. Compressive strengths of the manufactured specimens at $23^{\circ}C$ were about 33 MPa to 40 MPa. The variable parameters among the self-compacting concrete specimens were of sand stone type. The specimens were exposed to 23, 100, 200, 400, 600, and $800^{\circ}C$ and their mechanical specifications were controlled. The heated specimens were subjected to the unconfined compression test with a quasi-static loading rate. The corresponding stress-strain curves and modulus of elasticity were compared. The results showed that, at higher temperatures, Scoria aggregate showed less sensitivity than ordinary aggregate. The concrete made with Scoria aggregate exhibited less strain. The heated self-compacting concrete had similar slopes before and after the peak. In fact, increasing heat produced gradual symmetrical stress-strain diagram span.

• Computers and Concrete
• /
• v.8 no.4
• /
• pp.425-443
• /
• 2011

Most previous studies have generally overlooked the contribution of thermal stresses generated within the concrete mass when subjected to microwave heating and reported on pore-pressure as being the dominant cause of surface spalling. Also, the variation in electromagnetic properties of concrete and its effects on the microwave heating process have not been studied in detail. In this paper, finite element modeling is used to examine the simultaneous development of compressive thermal stresses and pore-pressure arising from the microwave heating of concrete. A modified Lambert's Law formulation is proposed to estimate the microwave power dissipation in the concrete mass. Moreover, the effects of frequency and concrete water content on the concrete heating rate and pattern are investigated. Results show high compressive stresses being generated especially in concrete with a high water content when heated by microwaves of higher frequencies. The results also reveal that the water content of concrete plays a crucial role in the microwave heating process.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.157-160
• /
• 2004

If concrete structure is exposed to high temperature such as long-term fire, damages affecting partial or whole structure system may occur. Therefore accurate diagnosis of deterioration is needed based on mechanism of fire deterioration in general concrete structures. Fundamental information and data on the properties of concrete exposed to high temperature are necessary. Especially, the amount of fire damage done to concrete depends on the materials, the standard design compressive strength of concrete, and heated temperature. So, the object of this study is to present data for supposed heated Temperature of deteriorated concrete by fire.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.10a
• /
• pp.89-90
• /
• 2016

In the cold-weathering(Mongolian region) concrete construction, this purpose of this research is the evaluation on the performance of concrete using various binders such as Mongolian cement, Chinese cement and high blane-self heated cement.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.05a
• /
• pp.53-54
• /
• 2015

This study is conducted to investigate the characteristics of cracks depending on the different mixture rates of calcium hydroxide and distilled water in high-strength concrete, which is substituted with a high percentage of blast-furnace slag, by using specimens produced under different heating temperatures: 600℃, 800℃, and 1000℃, respectively. According to the results of the study, the specimen heated under the temperature of 600℃ did not produce cracks; the specimen heated under 800℃ produced little cracks and showed no difference between calcium hydroxide and distilled water; whereas the specimen heated under 1000℃ produced cracks larger than 5mm on average in the case of calcium hydroxide, compared to distilled water.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.219-222
• /
• 1999

Concrete is to be important quality in placement point and exact test method needed about early judgement method concrete on placement point. But early judgement method of concrete proposed various kind of method because the problems of accuracy and the time required of test exists, it is used within the limits. This study is to propose of early strength judgement by using microwave for accurate estimating early strength of concrete and to develop test machine. Through out this study we find that belows. 1) Strength development of concrete specimen according to the time heated by microwave showed the height strength development in 9 minutes regardless of slump and w/c. 2) As cooling time is long, strength of concrete specimen according to the time heated by microwave showed high strength development and this tendency is like regardless of heating time, w/c and slump. 3) As w/c is high, accelerating strength development according to w/c showed lower strength development and this tendency is like regardless of slump, heating time and cooling time. 4) As slump is big, compressive strength of specimen in standard curing showed lower value and as w/c is big, strength development showed lower

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.449-452
• /
• 2006

This study inhence the strength of concrete by using domestic low grade kaolin. In conclusion, we confirmed to inhence the strength of concrete when added the low grade kaolin(heated in $800^{\circ}C$) about 10%.

• Fire Science and Engineering
• /
• v.12 no.4
• /
• pp.31-40
• /
• 1998

Very often, whether accidentally or intentionally set fire, according as building are elevated, varied or complicated day by day. It is of primary importance that we have a treatment of fire damaged structure. In general, strength and elasticity modulus of heated concrete are reduced. Product background of cement, sand and coarse aggregate differ from country to country, so that thermal behaviour of concrete make a difference in high temperature. To cope with demand, this paper is a study on relation to microstructure and strength reduction. In consequence of experiments, concrete exposed to high temperature are estimating the reduction of mechanical properties in comparison with microstructure characteristics which are abtained from the SEM/EDX, XRD and DSC-TG analysis of heated specimens under various temperature.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.239-240
• /
• 2021

In this study, we conducted a study to evaluate the more accurate mechanical properties of concrete damaged by fire. In relation to this, in this study, the results of compressive strength and biaxial flexural strength were compared for concrete that received high temperature heat. As a result, both the compressive strength and the biaxial bending strength decreased as the heating temperature increased. As a result of examining the correlation between the compressive strength and the biaxial flexural strength, the biaxial flexural strength was smaller than the compressive strength.