In this study, effect of various material hardening models based on Holloman's isotropic, Ziegler's linear kinematic, non-linear kinematic and mixture of the isotropic and nonlinear kinematic hardening laws on springback prediction of titanium alloy (Ti-3Al-2.5V) in a tube rotary draw bending (RDB) process was investigated with presenting the keynotes for a comprehensive step by step ABAQUS simulation. Influence of mandrel on quality of the final product including springback, wall-thinning and cross-section deformation of the tube was investigated, too. Material parameters of the hardening models were obtained based on information of a uniaxial test. In particular, in the case of combined iso-nonlinear kinematic hardening the material constants were calibrated by a simple approach based on half-cycle data instead of several stabilized cycles ones. Moreover, effect of some material and geometrical parameters on springback was carried out. The results showed that using the various hardening laws separately cannot describe the material hardening behavior correctly. Therefore, it is concluded that combining the hardening laws is a good idea to have accurate springback prediction. Totally the results are useful for predicting and controlling springback and cross-section deformation in metal forming processes.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.229-232
• /
• 2003

In the roll forming process, a sheet or strip of metal is continuously and progressively formed into a desired cross-sectional profile by feeding it through a series of forming roll. Accordingly, it is important to maintain the material properties of the initial sheet and deform uniformly during the roll forming. The roll forming process was estimated in consideration of some factors such as material properties, strip thickness, roll diameter, roll velocity, and the deformation of the material that influence the forming length. The hydroforming technology has been recognized as a new technique in manufacturing industry, especially in automotive industry. The formed pipe in used in hydroforming process is manufactured by the roll forming. The formability during hydroforming is very sensitive to the state of pipes which are made by roll forming. Particularly the amount of hardening during roll forming affects the formability. Therefore, it is necessary to design the optimum roll flower to reduce the local hardening. In this paper, optimum roll flower which has uniform strain distribution through sheet width was obtained by comparing strain distribution in various roll flower. Finite element analysis(FEA) is performed to estimate the strain distribution related to hardening by roll forming. A numerical analysis is carried out by SHAPE-RF.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.12 no.2
• /
• pp.49-54
• /
• 2013

Recently welding of aluminum material is actively carried out to make lightweight in the fields of LNG vessels, aircraft, chemical plants, etc. To obtain high strength, hardness and elongation, elements such as manganese, zinc, silicon, etc should be added in aluminum alloy, which has been improved on the mechanical properties like precipitation hardening, age hardening, loosening, corrosion resistance acid resistance. Ar gas is used as a shielding gas of MIG welding for aluminum, also $N_2$, $O_2$, $CO_2$, $H_2$ etc can be added depending on the composition of the alloy. In this study, Ar + $O_2$, Ar, and He were used for welding, hardness, penetration status and changes in composition of penetrated parts were compared and analyzed. This made it possible to know the status and changes of the process in the penetrated parts depending on used gas throughout this study.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.98-101
• /
• 1999

The plastic instable flow phenomenon happens in practical forming process I. e. upsetting backward extrusion piercing indentation. And also it is difficult to control precisely the shape and dimensions of forming process. It is found that instabilities of the process are mainly connected with imperfection in the lubrication billet eccentricity inclined punch alignment. In view of the direct relationship between instable material flow and quality defects of the products and it is for better control of forming operation we should necessarily find out their phenomena. In this study we used the friction disturbance due to inclined punch angle and introduced the method considering kinematic hardening effect Analysis of upset forging is carried out using the rigid plastic FEM and slab method with eccentricity.

• Journal of Korea Foundry Society
• /
• v.4 no.2
• /
• pp.102-107
• /
• 1984

The variations of the mold compression strength were studied by varing the contents of the silicon powder and water glass, silion purities, and molecule rates of the water glass, when domestic JA EUN DO sand is mixed with water glass (sodium silicate) and metallic silicon or ferro - silicon powder by the self - hardening N - PROCESS method. The results obtained from this experiment are as follows; 1) The compression strength of the mold used with metalic powder was higher and more stable than to be used ferro - silicon powder. 2) 6% water glass of 2.8 molecule rate and 1.5% of ferro - silicon of 75% purity for the N - PROCESS used with JA EUN DO sand was suitable mixing rate. 3) The compression strength increased with self - hardening time, and the PH values of the mixture of silicon powder and water glass did not change after 2 hours, but the compression strength increased steadily due to the reaction of remained silicon. 4) It is recommended to take 24 hours for self - hardening time at least.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.8 no.5
• /
• pp.961-969
• /
• 2004

A panic state is often caused by careless computer control. It could be also caused by a kernel programmer's mistake. It can make a big problem in computer system when it happens a lot. When a panic occurs, the process of the panic state has to be checked, then if it can be restored, operating system restores it, but if not, operating system runs the panic function to stop the system in the kernel hardening O.S. To decide recovery of the process, the type of the panic for the present process should be checked. 1'he value type and the address type have to restore the process. If the system process is in a panic state, the system should be designed to shutdown hardening function In the Linux operating system. So it has to decide whether the process should be restored or not before going to the panic state.

• Journal of Advanced Marine Engineering and Technology
• /
• v.18 no.5
• /
• pp.29-35
• /
• 1994

The microstructual refinement process of Al-5Cr-2Zr alloys mechanical alloying 30h can be divided in five stages ; initial stage, welding predomminance stage, spherical partical formation stage, convolution welding predominance stage, and steady state. The rate of structural of aluminium splats was roughly logarithmic with processing time ; ${\in}$=k/0.78 ln(1+0.0028t). The age hardening in rapidly solidified Al-5Cr-2Zr alloys is ascribed to the coherency and dispersion hardening. Coherency hardening is occurred by matastable cubic Al3Zr precipitates in Al-Cr-Zr alloys. Dispersion hardening after mechanical alloying is attributed to the finely-dispersed $Al_2O_3$ and $Al_4C_3$ in Al-5Cr-2Zr alloys.

• Journal of Welding and Joining
• /
• v.25 no.3
• /
• pp.85-91
• /
• 2007

The conventional study on the laser surface transformation hardening has been carried out with a beam of the specified shape and uniform power-intensity distribution in order to ensure the uniformity of the hardening depth. Two types of beams - the circular gaussian beam and rectangular beam of the uniform power-intensity distribution were used in this study. we were supposed to optimize the process parameters and to compare the hardening results with two optics respectively. As a result, the hardness distribution of the hardened zone was similar in both cases and the hardened phase by the rectangular beam was denser than that by the circular gaussian beam.

• Korean Journal of Metals and Materials
• /
• v.49 no.6
• /
• pp.448-453
• /
• 2011

Pre-aging heat treatment after solution heat treatment (SHT) of Al-0.4 wt%Mg-1.2 wt%Si-0.1 wt%Mn alloy sheets for auto-bodies was carried out to investigate the effect of pre-aging and its conditions on the bake-hardening response. Mechanical properties were evaluated by a tensile and Vickers hardness test. Microstructural observation was also performed using a transmission electron microscope (TEM). It was revealed that pre-aging treatments play a great role in the bake-hardening response. In addition, it was found that the sphere-shaped nanosized clusters that can directly transit to the needle-shaped ${\beta}$" phase during the paint-bake process, not being dissolved into the matrix, are formed at 343 K. The result, reveals that the dominant factor of the bake-hardening response is the pre-aging temperature rather than the pre-aging time.

• Laser Solutions
• /
• v.11 no.4
• /
• pp.7-12
• /
• 2008

Laser Transformation Hardening(LTH) is one branch of the laser surface modification processes. A lot of energy is needed for the LTH process to elevate workpiece surface to temperature of the austenite transformation($A_3$), which results from utilizing a beam with a larger size and lower power density comparatively. This study is related to the surface hardening for the rod-shaped carbon steel by the high power diode laser whose beam absorptivity is better than conventional types of lasers such as $CO_2$ or Nd:YAG laser. Because a beam proceeds on the rotating specimen, the pretreated hardened-phase can be tempered and softened by the overlapping between hardened tracks. Accordingly, the longitudinal hardness measurement and observation of the micro structure was carried out for an assessment of the hardening characteristics. In addition, a hardening characteristics as a hardenability of materials was compared in the point of view of the hardness distribution and hardening depth and width.