• International Journal of Concrete Structures and Materials
• /
• v.8 no.1
• /
• pp.69-81
• /
• 2014

In this study, portland cement (PC) has been partially replaced with a Class F fly ash (FA) at level of 70 % to produce high-volume FA (HVFA) concrete (F70). F70 was modified by replacing FA at levels of 10 and 20 % with silica fume (SF) and ground granulated blast-furnace slag (GGBS) and their equally combinations. All HVFA concrete types were compared to PC concrete. After curing for 7, 28, 90 and 180 days the specimens were tested in compression and abrasion. The various decomposition phases formed were identified using X-ray diffraction. The morphology of the formed hydrates was studied using scanning electron microscopy. The results indicated higher abrasion resistance of HVFA concrete blended with either SF or equally combinations of SF and GGBS, whilst lower abrasion resistance was noted in HVFA blended with GGBS.

• Advances in concrete construction
• /
• v.13 no.1
• /
• pp.35-43
• /
• 2022

The experimental investigations into hooked-end round steel fibers (HSF) effect on the age-dependent strengths of high volume fly ash (HVFA) concrete is studied. The concrete was prepared with class F fly ash used as partial cement replacement varied from 0% to 70% on an equal weight basis. Two percentages of HSF (i.e., 0.5% and 1.5% by volume fraction) of 50 mm length were added in plain, and 50% fly ash concrete mixes. The compressive and flexural tensile strength was determined at 7, 28, 56, and 90 days. The strength results of fly ash concrete mixes with and without steel fibers were compared with the plain concrete strength. The test results indicated that the strength of fly ash concrete is comparable with the plain concrete strength and further increases with an increase in the percentage of steel fibers. The maximum flexure strength of HVFA concrete is found with 0.5% steel fibers. It is concluded that the HVFA concrete with steel fibers of 50 mm length can effectively be used in concrete construction. The analytical models are proposed to predict the age-dependent compressive and flexural tensile strength of HVFA concrete with and without HSF. The compressive and tensile strength of HVFA concrete with HSF can be predicted using these models when the 28-day compressive strength of plain concrete is known. The present study will be helpful in the design and construction of reinforced and pre-stressed concrete structures made with HVFA and HSF.

• Advances in concrete construction
• /
• v.3 no.4
• /
• pp.317-331
• /
• 2015

This paper presents the effect of different micro-silica (MS) contents of 5, 10 and 15 wt.% as partial replacement of cement on mechanical and durability properties of high volume fly ash - recycled aggregate concretes (HVFA-RAC) containing 50% class F fly ash (FA) and 35% recycled coarse aggregate (RCA) as partial replacement of cement and natural coarse aggregate (NCA), respectively. The measured mechanical and durability properties are compressive strength, indirect tensile strength, elastic modulus, drying shrinkage, water sorptivity and chloride permeability. The effects of different curing ages of 7, 28, 56 and 91 days on above properties are also considered in this study. The results show that the addition of MS up to 10% improved the early age (7 days) strength properties of HVFA-RAC, however, at later ages (e.g. 28-91 days) the above mechanical properties are improved for all MS contents. The 5% MS exhibited the best performance among all MS contents for all mechanical properties of HVFA-RAC. In the case of measured durability properties, mix results are obtained, where 10% and 5% MS exhibited the lowest sorptivity and drying shrinkage, respectively at all ages. However, in the case of chloride ion permeability a decreasing trend is observed with increase in MS contents and curing ages. Strong correlations of indirect tensile strength and modulus of elasticity with square root of compressive strength are also observed in HVFA-RAC. Nevertheless, it is established in this study that MS contributes to the sustainability of HVFA-RAC significantly by improving the mechanical and durability properties of concrete containing 50%less cement and 35% less natural coarse aggregates.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.2
• /
• pp.109-114
• /
• 2015

Recently, numerous studies were dedicated on the HVFA concrete using high volume CCPs. In initial studies, main topics are dependent on material properties of HVFA concrete, but several studies were dedicated on the structural behavior of HVFA concrete such as elasticity modulus, stress-strain relationship and structural behavior nowadays. Therefore, in this paper, on the basis of recent studies on the structural behavior, 2 large-scale test members were manufactured with 7.5m span length and fly ash replacement ratio 50%, concrete compressive strength 50MPa in order to apply to the practical structure and evaluate possibility of application. From the test results, although there were small differences between test results and existing research results on the stress-strain relationship, the application to practical structure is not hard. In flexural test, as the produced pattern of displacement and strain were similar to those of general concrete without fly ash, the difference between 50% fly ash concrete and general concrete is very small. And the concrete shear strength obtained by test was similar to that of design code, so existing design code will be also able to apply.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.3
• /
• pp.202-208
• /
• 2014

For evaluating basic structural behavior of HVFA (High Volume Fly Ash) concrete, several tests are performed considering different ratios of fly ash replacement and structural evaluation regarding compressive strength, elasticity modulus, stress-strain relationship, and bond strength is also performed. Test results show that elasticity modulus of HVFA concrete has close relationships with compressive strength and fly ash replacement ratio. The ultimate strain shows slight difference from domestic design code. On the other hand, there are no differences between general concrete and HVFA concrete for elasticity modulus and bond strength.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.1
• /
• pp.34-39
• /
• 2014

The purpose of this experimental research is to evaluate the resistance of reinforcement corrosion and chloride ion penetration of high volume fly ash (HVFA) concrete. For this purpose, concrete test specimens were made for various strength level and replacement ratio of fly ash, and then compressive strength and diffusion coefficient for chloride ion of them were measured for 28, 91 and 182 days, respectively. Also, corrosion monitoring by half cell potential method was carried out for the made lollypop concrete test specimens to detect the time of corrosion initiation for reinforcement in concrete. As a result, it was observed from the test results that compressive strength of HVFA concrete was decreased with increasing replacement ratio of fly ash but long-term resistance against reinforcement corrosion and chloride ion penetration of that was increased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.5
• /
• pp.95-102
• /
• 2022

Recently, there has been a growing interest in reducing greenhouse gases in all industrial fields. In the construction industry, studies have been conducted for the use of high-volume fly ash concrete to replace cement with fly ash. Quantitative measurements of cement hydration and fly ash reactivity enable a clear understanding of the strength development mechanism of high-volume fly ash concrete. It is very difficult to describe the reactivity in a simple way because the hydration and pozzolanic reactions of cement paste containing fly ash are very complex and the composition of the hydration product cannot be accurately determined. This study investigated the hydration and mechanical properties of high volume fly ash (HVFA) cement according to the substitution rate of fly ash (FA). The hydration degree of cement and the reactivity of FA were evaluated through the selective dissolution method and the non-evaporable water content of the paste according to age. In addition, compressive strength was measured using HVFA mortar specimens according to age. As a result of the experiment, as the substitution rate of fly ash increased, the hydration degree of cement increased, but the reactivity of FA decreased.

• Corrosion Science and Technology
• /
• v.13 no.6
• /
• pp.209-213
• /
• 2014

Due to the increasing of interest about the eco-friendly concrete, it is increased to use concretes containing by-products of industry such as fly ash(FA), ground granulated blast furnace slag(GGBFS), silica fume(SF), and etc. Especially, these are well known for improving the resistances to reinforcement corrosion in concrete and decreasing chloride ion penetration. The purpose of this experimental research is to evaluate the resistance against corrosion of reinforcement of high volume fly ash(HVFA) concrete which is replaced with high volume fly ash for cement volume. For this purpose, the concrete test specimens were made for various strength level and replacement ratio of FA, and then the compressive strength and diffusion coefficient for chloride ion of them were measured for 28, 91, and 182 days, respectively. Also, corrosion monitoring by half cell potential method was carried out for the made lollypop concrete test specimens to detect the time of corrosion initiation for reinforcement in concrete. As a result, it was observed from the test results that the compressive strength of HVFA concrete was decreased with increasing replacement ratio of FA but long-term resistances against reinforcement corrosion and chloride ion penetration of that were increased.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.309-310
• /
• 2010

In this study we investigated the properties of the fundamental and adiabatic temperature rise of the concrete using high volume fly-ash. For this, the fly ash was used to replace cement at replacement ratio of 40% and 50% by mass, and then the slump, air content, bleeding, compressive strength and adiabatic temperature rise test of concrete were performed.

• KCI Concrete Journal
• /
• v.14 no.2
• /
• pp.76-80
• /
• 2002

The role of high volume Class F fly ash in reducing expansion due to Alkali-Silica Reaction (ASR) was investigated. A series of modified ASTM C 1260 tests were performed under three different levels of NaOH normality, extending the test period to 28 days, using high- or low alkali cement, and Class F fly ash up to 58 ％ by mass of cement. A reactive siliceous fine aggregate was used. The test results confirm that HVFA replacement in a cementitious system significantly helps in controlling expansion caused by ASR.